CuSbS2 nanoparticle and preparing method and application thereof

A nanoparticle and particle technology, applied in chemical instruments and methods, chemical/physical processes, physical/chemical process catalysts, etc., can solve the problems of poor photocatalytic performance and uncontrollable shape of nanoparticles, and achieve improved photocatalytic performance , short preparation cycle, and the effect of improving mobility

Active Publication Date: 2019-09-06
JINLING INST OF TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN108467063A patent document discloses a kind of microwave synthesis CuSbS 2 CuSbS prepared by nanoparticle method, but commonly used preparation method 2 Sb exists in both nanoparticles 2 S 3 and other impurity phases, and the morphology cannot be adjusted, resulting in CuSbS 2 Nanoparticles have poor photocatalytic performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • CuSbS2 nanoparticle and preparing method and application thereof
  • CuSbS2 nanoparticle and preparing method and application thereof
  • CuSbS2 nanoparticle and preparing method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A preparation of CuSbS by microwave liquid phase method 2 A method for nanoparticles comprising the steps of:

[0044] Weigh 0.001mol copper nitrate trihydrate, 0.002mol antimony trichloride, 0.003mol thiourea, and 30mg / mL polyvinylpyrrolidone and dissolve them in 50mL of ethylene glycol in turn, and prepare a precursor solution after it is completely dissolved to adjust the pH= 5. Using the microwave method, the precursor solution was irradiated with microwaves, the microwave power was 400W, the microwave time was 4min, and then the microwave power was adjusted to 240W, and the microwave time was 6min to prepare CuSbS 2 black solution. The black solution was washed three times with ultrapure water and ethanol, and the CuSbS 2 The black solution was centrifuged to obtain CuSbS 2 nanoparticles. Then the CuSbS 2 Nanoparticles placed in 0.2mol / L NaS 2 CuSbS in solution with ultrasonic vibration for 20 min and magnetic stirring at 25 °C for 60 min 2 nanoparticles. ...

Embodiment 2

[0048] Weigh 0.001mol cupric chloride, 0.0011mol antimony acetate, 0.0042mol thioacetamide, 24mg / mL hexadecyltrimethylammonium bromide and dissolve them in polyethylene glycol-200 and ethylene glycol at a ratio of 5:5 50mL solution mixed in the proportion of the mixture, after it was completely dissolved, it was prepared as a precursor solution and hydrochloric acid was added to adjust the pH=2. The precursor solution was heated by microwave with a microwave power of 600W and a microwave time of 6min, then a microwave power of 160W and a microwave time of 4min to prepare CuSbS 2 black solution. The black solution was washed three times with ultrapure water and ethanol, and the CuSbS 2 CuSbS was separated from the black solution by centrifugation 2 nanoparticles. Then the CuSbS 2 Nanoparticles placed in 0.36mol / L NaS 2 CuSbS in solution with ultrasonic vibration for 20 min and magnetic stirring at 60 °C for 30 min 2 nanoparticles. The cleaned CuSbS 2 Nanoparticles dry. ...

Embodiment 3

[0050] Weigh 0.001mol copper chloride, 0.0025mol antimony nitrate, 0.0175mol L-cysteine, 12mg / mL sodium dodecylbenzenesulfonate and dissolve them in 50mL glycerol in turn, and prepare Precursor solution and adding hydrochloric acid to adjust pH=1. Microwave the precursor solution by microwave heating, the microwave power is 200W, the microwave time is 2min, and then the microwave power is adjusted to 480W, and the microwave time is 12min to prepare CuSbS 2 black solution. The black solution was washed three times with ultrapure water and ethanol, and the CuSbS 2 The black solution was centrifuged to obtain CuSbS 2 nanoparticles. Then the CuSbS 2 Nanoparticles placed in 0.68mol / L NaS 2 CuSbS in solution with ultrasonic vibration for 30 min and magnetic stirring at 40 °C for 20 min 2 nanoparticles. The cleaned CuSbS 2 Nanoparticles dry. CuSbS 2 The morphology and photocatalytic properties of the nanoparticles are consistent with the results of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparing method and application of a CuSbS2 nanoparticle. The particle is an agglomerate with a regular square rod-shaped structure. The preparing method comprises the stepsthat copper salt, antimonic salt and a sulfocompound are dissolved in a solvent, and then a precursor solution is prepared after the materials are fully dissolved; a microwave method is adopted for preparing the CuSbS2 nanoparticle; a Na2S solution is added into the obtained CuSbS2 nanoparticle for removing impurity phases. According to the CuSbS2 nanoparticle and the preparing method and application thereof, by regulating preparing technologies and parameters, the purpose of regulating the crystal appearance is achieved, then the ideal crystal surface appearance is prepared, the photocatalytic performance of the CuSbS2 nanoparticle is improved, and the CuSbS2 nanoparticle can increase the degradation rate of rhodamine B under 7 hours of illumination by an xenon lamp of 500 W to 96% from19%.

Description

technical field [0001] The present invention relates to a kind of solar energy, photocatalytic material and preparation method, application, specifically relate to a kind of CuSbS 2 Nanoparticles and their preparation methods and applications. Background technique [0002] With the advancement of modern science and technology, the serious pollution of the environment caused by traditional fossil energy and its increasing scarcity have brought great challenges to human survival and development. Therefore, countries all over the world are seeking an alternative renewable energy, forcing people to look for a renewable and pollution-free energy. As a widely distributed, energy-storage, and environmentally friendly energy source, solar energy is considered an ideal alternative energy source. Therefore, solar cells are widely concerned and used. At present, silicon solar cells are basically used in the market, but the manufacturing process of crystalline silicon cells is highly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01G30/00B01J27/04B01J35/02
CPCC01G30/002B01J27/04C01P2002/72C01P2004/03C01P2004/04C01P2002/82C01P2006/80C01P2004/16B01J35/40B01J35/39
Inventor 王威支国伟郝凌云杨璐周梦娇丁玲
Owner JINLING INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com