A high-strength steel for thin-gauge construction machinery and its shape control method

Abstract

The invention relates to a high-strength steel for thin-gauge engineering machinery. The composition mass percentage is: C: 0.07%-0.10%, Si: 0.15%-0.30%, Mn: 1.2%-1.6%, P≤0.012%, S≤0.003 %, Nb: 0%~0.08%, V: 0%~0.07%, Ti: 0.06%~0.13%, Cr: 0.1%~0.2%, Mo: 0.1%~0.2%, Nb+V+Ti: 0.08% ~0.15%, Mo+Cr: 0.25%~0.35%, the rest is Fe and impurities. Adopt blast furnace hot metal, hot metal desulfurization, converter smelting, LF+RH refining, continuous casting, hot charging and hot delivery, heating, rolling, cooling, coiling, leveling, tempering heat treatment, and straightening process routes. The yield strength is greater than 690MPa, the tensile strength is greater than 785MPa, and the impact energy at -20°C is greater than 100J.

Description

technical field [0001] The invention relates to the field of high-strength steel manufacturing, in particular to a high-strength steel for thin-gauge construction machinery and a shape control method. Background technique [0002] Thin-gauge high-strength steel for construction machinery is widely used in the manufacture of cranes, aerial work vehicle booms and other equipment. It requires high safety performance. In addition to reaching a certain strength level, it also requires excellent shape quality. The quality will make it difficult to weld after cold bending or the welding stress is too large. Once defects such as welding cracks occur during use, there is a high probability of causing safety accidents and the impact is bad. [0003] In order to obtain excellent shape quality, some steel mills use slow cooling of hot-rolled coils or annealing in bell annealing furnaces for flattening, or use multiple times of heat straightening, all of which have certain effects, but t...

AI Technical Summary

Problems solved by technology

Its strength and elongation have large margins, good impact toughness, and low loss of strength after welding, but the means to improve the final shape of the plate mainly rely on tempering heat treatment to eliminate stress, without considering that the release of stress after tempering may further deteriorate the shape of the plate Possibility, the quality of the plate shape may not be stable enough. In addition, its precious metal Mo content is high, which pushes up the production cost, and for steel plates above 8.5mm, it cannot be produced

[0006] Publication No. CN101670372B invention patent discloses a method for eliminating shape defects of hot-rolled high-strength steel plates. The combination of temper rolling, bell annealing and roller straightening processes is introduced into the specification range of thickness 3-18.4mm×width 900-1800mm, yield The production and processing process of hot-rolled high-strength steel coils with strength ≥ 600MPa eliminates the internal stress of hot-rolled high-strength steel, significantly improves the shape quality, and enables users to obtain good shape stability, which can meet users' requirements for flatness less than or equal to The strict requirement of 2mm / m, but there is a certain contradiction between the internal stress relief uniformity and strength of the bell-type annealed steel coil, and the requirements for temperature control are relatively high. The impact is critical, the patent does not mention the original plate (coil) control means

Images