A preparation method of multifunctional electrospun fiber dressing

An electrospinning, multi-functional technology, applied in fiber processing, filament/thread forming, textiles and papermaking, etc., can solve the problems of less research and achieve uniform diameter, soft texture, good filling and adhesion Effect

Active Publication Date: 2021-07-27
CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is a feasible method to realize the multifunctionality of the material itself through material screening and grafting functional groups, but there are still relatively few related studies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of multifunctional electrospun fiber dressing
  • A preparation method of multifunctional electrospun fiber dressing
  • A preparation method of multifunctional electrospun fiber dressing

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The present invention also provides a kind of preparation method of multifunctional electrostatic spinning fiber dressing, and this method comprises:

[0031] Step 1: grafting functional groups to the polymer material; the functional groups are antioxidant groups or / and antibacterial groups; the polymer material has the function of stimulating macrophage transformation;

[0032] Step 2: Dissolving the polymer material grafted with functional groups obtained in Step 1 in a solvent for electrospinning to obtain an electrospun fiber mat;

[0033] Step 3: Place the electrospun fiber mat obtained in Step 2 in a crosslinking agent solution, soak it, take out the fiber mat, wash it, blow dry or dry it, and obtain a multifunctional electrospun fiber dressing.

[0034] According to the present invention, first prepare the macromolecular material grafted with functional groups, the preparation method of the macromolecular material grafted with functional groups is to blend the sm...

Embodiment 1

[0047] Dissolve 200mg of hyaluronic acid (HA) in 100ml of deionized water, stir magnetically until completely dissolved, add 64mg of 2-(methylthio)ethylamine, 53mg of 1-hydroxybenzotriazole and 75mg of EDC, and stir in an ice bath for 30min. Add 1M NaOH or 1M HCl to adjust the pH value to 6.5-7.0, continue ice bathing for 30 min, and then react at room temperature for 3 days. The resulting reaction solution was settled with ice ethanol and filtered to keep the precipitate. The precipitate was re-dissolved with deionized water, filtered, and the filtrate was retained for dialysis with deionized water for 3 days. Finally, the dialysate was freeze-dried to obtain hyaluronic acid (HA-S) grafted with thioether groups.

[0048] Dissolve 120mg of HA-S in 7.2ml of ammonia water and 2.8ml of N-methylpyrrolidone, stir at room temperature until completely dissolved, and use the resulting solution for spinning.

[0049] The resulting spinning solution is spun, and the electrospinning op...

Embodiment 2

[0058] Dissolve 200mg of sodium alginate (SA) in 80ml of deionized water, magnetically stir until completely dissolved, add 96mg of aminoethyl sulfide, 153mg of 1-hydroxybenzotriazole and 120mg of EDC, stir in an ice bath for 30min, add 1M NaOH or Adjust the pH value to 6.5-7.0 with 1M HCl, and continue the ice bath for 30 minutes. Then react at room temperature for 4h. The resulting reaction solution was settled with ice ethanol and filtered to keep the precipitate. The precipitate was re-dissolved with deionized water, filtered, and the filtrate was retained for dialysis with deionized water for 3 days. Finally, the dialysate was freeze-dried to obtain alginic acid grafted with antioxidant thioether groups (SA-S).

[0059] Dissolve 100mg of SA-S in 40ml of water, add 5ml of 1M NaOH and 50mg of glycidyltrimethylamine chloride (GTAC), and stir in a water bath at 60°C for 5h. 1% glacial acetic acid neutralized the pH, the reaction solution was dialyzed with deionized water f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a multifunctional electrostatic spinning fiber dressing and a preparation method thereof, belonging to the technical field of polymer medical materials. The fiber dressing has a micro-nano structure, and is obtained by spinning high-molecular materials grafted with functional groups into fibers by electrospinning, and then cross-linking. The high-molecular materials have the function of stimulating transformation of macrophages. The invention also provides a preparation method of the multifunctional electrostatic spinning fiber dressing. The electrospun fiber dressing of the present invention is obtained by grafting functional groups on macromolecular materials that can promote the transformation of macrophages, and then performing electrospinning and crosslinking. It can not only close superficial wounds, but also fill deep wounds, and can realize the multifunctionality of hemostasis, anti-oxidation, anti-inflammation, antibacterial, promoting healing and reducing scars.

Description

technical field [0001] The invention belongs to the technical field of polymer medical materials, and in particular relates to a multifunctional electrostatic spinning fiber dressing and a preparation method thereof. Background technique [0002] Skin trauma is a frequently faced clinical problem. As the world's population ages, chronic wounds such as decubitus ulcers and diabetic ulcers, which are closely related to the elderly, are increasing. The wound repair process generally includes the hemostatic and inflammatory response phase, the proliferation phase, and the tissue modeling phase. The repair process of chronic wounds is more complicated. From the perspective of wound repair process, chronic inflammation prevents wounds from achieving the transition from inflammation to proliferation, which is the main reason why chronic wounds cannot heal for a long time. However, excessive use of antibacterial agents and anti-inflammatory drugs will cause serious drug resistanc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/4382D04H1/728D01D5/00A61L15/28A61L15/32A61L15/42A61L15/44A61L15/46
Inventor 黄宇彬刘沙周东方李晓媛
Owner CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com