High-strength and tough heat-resistant mg-y alloy suitable for gravity casting and preparation method thereof

A gravity casting and alloying technology, which is applied in the field of high-strength, toughness and heat-resistant Mg-Y alloys and their preparation, can solve the problems of inability to achieve the performance of cast aluminum alloys, insufficient heat resistance, etc., and achieve the effect of high efficiency and simple process

Active Publication Date: 2021-08-06
SHANGHAI JIAO TONG UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the industrial problem that the existing cast magnesium alloys cannot reach the performance of cast aluminum alloys such as A380 due to insufficient toughness and heat resistance, resulting in greatly restricted applications, the present invention provides a high-strength magnesium alloy suitable for gravity casting. Tough and heat-resistant Mg-Y alloy and its preparation method; after gravity casting and heat treatment of the alloy, the room temperature tensile strength of the alloy is above 260MPa, and the elongation rate is above 18%; the high temperature tensile strength at 200°C is above 185MPa, and Rate 25% or more

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength and tough heat-resistant mg-y alloy suitable for gravity casting and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The percentage by weight of a high-strength, tough, heat-resistant Mg-Y alloy suitable for gravity casting related to this embodiment is: according to the theoretical ratio, 4.0% Y, 3.0% Zn, 0.5% Al, 0.3% Mn, 0.01% Ti, 0.01% B, the balance is Mg and other unavoidable impurities.

[0040] Its preparation method is: (1) according to the above-mentioned Mg-Y alloy composition and stoichiometric ratio, calculate the consumption of required raw materials; mix industrial pure magnesium ingot, industrial pure zinc, industrial pure aluminum ingot and Mg-Y and Mg-Mn intermediate Remove the oxide layer from the alloy, dry and preheat to 200°C; calculate the amount of raw materials required according to the composition and stoichiometric ratio of the alloy; (2) melt the industrial pure magnesium ingot accounting for 25% of the crucible height at 680°C into After the molten pool, the protective gas argon is introduced, and the remaining magnesium ingots are added; (3) after the mag...

Embodiment 2

[0043] The percentage by weight of a high-strength, tough, heat-resistant Mg-Y alloy suitable for gravity casting related to this embodiment is: according to the theoretical ratio, 8.0% Y, 3.2% Zn, 0.8% Al, 0.1% Mn, 0.08% Ti, The balance is Mg and other unavoidable impurities.

[0044] Its preparation method is: (1) according to above-mentioned Mg-Y alloy composition and stoichiometric ratio, calculate the consumption of required raw material; Deoxidize industrial pure magnesium ingot, industrial pure zinc, industrial pure aluminum ingot and MgY30 and MgMn10 master alloy layer and dry and preheat to 180°C; calculate the amount of raw materials required according to the composition and stoichiometric ratio of the alloy; (2) After melting the industrial pure magnesium ingot accounting for 20% of the crucible height into a molten pool at 685°C, Introduce a protective gas containing 0.2% volume fraction of SF 6 and CO 2 (3) After the magnesium ingots are completely melted, heat ...

Embodiment 3

[0047] The percentage by weight of a high-strength and tough heat-resistant Mg-Y alloy suitable for gravity casting related to this embodiment is: according to the theoretical ratio, 4.0% Y, 4.0% Zn, 0.9% Al, 0.2% Mn, 0.05% Ti, 0.03% B, the balance is Mg and other unavoidable impurities.

[0048] Its preparation method is (1): according to the above-mentioned Mg-Y alloy composition and stoichiometric ratio, calculate the consumption of required raw material; Deoxidize industrial pure magnesium ingot, industrial pure zinc, industrial pure aluminum ingot and MgY30 and MgMn10 master alloy layer and dry and preheat to 180°C; calculate the amount of raw materials required according to the composition and stoichiometric ratio of the alloy; (2) after melting the industrial pure magnesium ingot accounting for 22% of the crucible height into a molten pool at 675°C, Pass through the protective gas argon, and add the remaining magnesium ingots; (3) After the magnesium ingots are complete...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength, toughness, heat-resistant Mg-Y alloy suitable for gravity casting and a preparation method thereof. The alloy chemical composition mass percent content is: 4.0-8.0% Y, 3.0-6.0% Zn, 0.5-1.2% Al, 0.1-0.3% Mn, 0.01-0.08% M, the balance being Mg and other unavoidable impurities, wherein M is at least one element among Ti and B. After gravity casting, secondary solution treatment and artificial aging heat treatment, the high-strength, toughness and heat-resistant cast Mg-Y alloy of the present invention has a room temperature tensile strength of more than 260 MPa and an elongation of more than 18%; high temperature tensile strength at 200°C It is more than 185MPa, and the elongation rate is more than 25%, which meets the high-end demand for lightweight development in aerospace, military industry, automobile and other industries.

Description

technical field [0001] The invention belongs to the field of industrial magnesium alloy and its manufacture, and in particular relates to a high-strength and tough heat-resistant Mg-Y alloy suitable for gravity casting and a preparation method thereof. Background technique [0002] As the lightest engineering metal material (the density of magnesium is 2 / 3 of aluminum and 1 / 4 of steel), its specific strength is obviously higher than that of aluminum alloy and steel. Higher than engineering plastics, it also has a series of advantages such as good castability, good machinability, good thermal conductivity, damping, strong electromagnetic shielding ability and easy recycling. Wide application prospects. Magnesium alloy has become an ideal material to replace aluminum alloy, steel and engineering plastics to achieve lightweight, among which aluminum alloy has the greatest substitution potential. Cast aluminum alloy has the necessary strength, toughness and thermal stability, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C23/06C22C23/04C22C1/03C22C1/06C22F1/06
Inventor 叶兵刘子利蒋海燕丁文江
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com