A kind of metal organogel and preparation method thereof and utilize this metal organogel to al 3+ Visual detection method

A metal-organic, detection method technology, applied in the field of chemical analysis and detection, can solve the problems of insufficient detection speed, expensive instruments, and complicated pretreatment.

Active Publication Date: 2021-05-11
HAINAN UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These techniques have high sensitivity and selectivity and are often used in ion quantitative detection, but these methods are expensive, the sample pretreatment is more complicated during the measurement, the detection is not fast enough, and the interference is large, so the application is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of metal organogel and preparation method thereof and utilize this metal organogel to al <sup>3+</sup> Visual detection method
  • A kind of metal organogel and preparation method thereof and utilize this metal organogel to al <sup>3+</sup> Visual detection method
  • A kind of metal organogel and preparation method thereof and utilize this metal organogel to al <sup>3+</sup> Visual detection method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A kind of preparation method of metal organogel, comprises the steps: at first getting 1mL concentration is the DMF solution of 1,3,6,8-tetrakis(4-carboxyphenyl)pyrene of 0.01mmol / mL, 1mL concentration is 0.1mmol / mL The DMF solution of 4-4 bipyridine in mL and the DMF solution of 0.2mL nickel nitrate hexahydrate with a concentration of 0.01mmol / mL are fully mixed to obtain a DMF mixed solution; the above DMF mixed solution is poured into a glass bottle and sealed and placed in an oven Heating the reaction, the reaction time is 10 h, and the reaction temperature is 90° C. to obtain a gel; the gel is vacuum-dried at 60° C. for 20 h to obtain a metal organic gel.

[0039] a trivalent Al 3+ A visual detection method, including the following steps:

[0040] (1) Preparation of metal-organic gel composite film: Take 20 mg of metal-organic gel prepared above, 130 mg of polyethylene glycol, 2 g of polyvinyl alcohol, and 18 mL of water and stir evenly at 85 ° C to obtain viscous...

Embodiment 2

[0043] A kind of preparation method of metal organogel, comprises the steps: at first getting 2mL concentration is the DMF solution of 1,3,6,8-tetrakis(4-carboxyphenyl)pyrene of 0.02mmol / mL, 2mL concentration is 0.2mmol / mL The DMF solution of 4-4 bipyridine in mL and 0.3mL NiDMF solution of hexahydrate nitric acid with a concentration of 0.02mmol / mL are fully mixed to obtain a DMF mixed solution; the above DMF mixed solution is poured into a glass bottle, sealed and placed in an oven for heating reaction , the reaction time was 14 hours, and the reaction temperature was 95° C. to obtain a gel; the gel was vacuum-dried at 60° C. for 25 hours to obtain a metal-organic gel.

[0044] a trivalent Al 3+ A visual detection method, including the following steps:

[0045] (1) Preparation of metal-organic gel composite film: take 40 mg of metal-organic gel prepared above, 180 mg of polyethylene glycol, 5 g of polyvinyl alcohol, and 28 mL of water and stir evenly at 85 ° C to obtain vis...

Embodiment 3

[0048] A kind of preparation method of metal organogel, comprises the steps: at first getting 3mL concentration is the DMF solution of 1,3,6,8-tetrakis(4-carboxyphenyl)pyrene of 0.03mmol / mL, 3mL concentration is 0.3mmol / mL The DMF solution of 4-4 bipyridine in mL and the NiDMF solution of nitric acid hexahydrate with a concentration of 0.03mmol / mL are fully mixed to obtain a DMF mixed solution; the above-mentioned DMF mixed solution is poured into a glass bottle, sealed and placed in an oven for heating reaction , the reaction time was 16 hours, and the reaction temperature was 100° C. to obtain a gel; the gel was vacuum-dried at 60° C. for 30 hours to obtain a metal-organic gel.

[0049] a trivalent Al 3+ A visual detection method, including the following steps:

[0050] (1) Preparation of metal-organic gel composite film: take 30 mg of metal-organic gel prepared above, 150 mg of polyethylene glycol, 3 g of polyvinyl alcohol, and 22 mL of water and stir evenly at 85 ° C to o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a kind of metal organic gel and preparation method thereof and utilize this metal organic gel to Al 3+ The visual detection method is specifically to synthesize a metal-organic gel by the sol-gel method, and then use the metal-organic gel synthesized above to combine with a polymer to make a polymer composite film. This polymer composite film can al 3+ It has a good fluorescent response, and this fluorescent color change can be identified with the naked eye, and it can detect Al with a concentration higher than 3+ , this composite film has good anti-interference ability and can be reused. The advantage of the present invention is that the detection of Al 3+ The operation steps of the method are simple and can be observed with the naked eye.

Description

technical field [0001] The invention belongs to the field of chemical analysis and detection, and in particular relates to a metal organic gel and a preparation method thereof and the use of the metal organic gel for Al 3+ Visual detection method. Background technique [0002] Aluminum is the most abundant metal element in the earth's crust, accounting for about 7.73% of the total amount of the earth's crust, second only to oxygen and silicon. Most of the aluminum in the soil exists in the form of fixed aluminum, which has no toxic effect on plants and the environment, and only ionic aluminum can affect it. In recent years, with the deteriorating environment and the frequent precipitation of acid rain, the acidification of soil has intensified, leading to the activation of aluminum in soil. The harm of aluminum has become the main factor limiting the growth of crops in acidic soil. It seriously restricts the growth of plants, causing large-scale degradation of forests and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J13/00G01N21/64C07F15/04
CPCB01J13/0065B01J13/0069C07F15/045G01N21/643
Inventor 杨玮婷谷东旭潘勤鹤任国建王芙香
Owner HAINAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap