Preparation method of LED lamp with high heat dissipation and used in humid and decomposition environment

A technology of LED lamps and high heat dissipation, applied in lighting and heating equipment, anti-corrosion coatings, semiconductor devices of light-emitting elements, etc., can solve the problems of low working reliability and short service life of lamps, and achieve good acid and alkali corrosion resistance, The effect of long service life and high acid and alkali resistance

Inactive Publication Date: 2019-03-19
ANHUI LANRUI ELECTRONICS TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are still some deficiencies, especially in humid and corrupt environments, where the requirements for moisture resistance and acid-base corrosion are high. At present, it is generally solved by coating heat-conducting coatings on the aluminum alloy surface, but the working reliability of the lamps is still very low. The problem of short life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of LED lamp with high heat dissipation and used in humid and decomposition environment
  • Preparation method of LED lamp with high heat dissipation and used in humid and decomposition environment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for preparing a high heat dissipation LED lamp for a humid and corrupt environment, comprising the following steps:

[0019] S1. Stir 60kg of water-based hydroxyl fluorine-containing polyurethane resin, 5kg of bamboo charcoal fiber, and 200kg of ethylene glycol butyl ether acetate for 14min at a stirring temperature of 90°C, and add 10kg of methyl methacrylate-butadiene-styrene terpolymer Continue to stir for 2 minutes to obtain prefabricated material a;

[0020] S2. Stir 250kg of prefabricated material, 24kg of water-based acrylic resin, 4kg of propylene glycol methyl ether acetate, and 1kg of ethylene glycol ether acetate for 20min at a stirring temperature of 60°C and a stirring speed of 260r / min, then add 2kg of talcum powder, 16kg of Remove soil, 4kg light calcium carbonate, 5kg vermiculite powder, 2kg porous powder quartz and stir for 20min, add 1kg terminal vinyl silicone oil, 1.6kg pine tar, 1kg compatibilizer, 2kg defoamer, 1kg thickener and mix evenly...

Embodiment 2

[0023] A method for preparing a high heat dissipation LED lamp for a humid and corrupt environment, comprising the following steps:

[0024] S1. Stir 100kg of water-based hydroxyl fluorine-containing polyurethane resin, 1kg of bamboo charcoal fiber, and 400kg of ethylene glycol butyl ether acetate for 10 minutes at a stirring temperature of 98°C, and add 4kg of methyl methacrylate-butadiene-styrene terpolymer Continue to stir for 10 minutes to obtain prefabricated material a;

[0025] S2. Stir 150kg of prefabricated material, 56kg of water-based acrylic resin, 1kg of propylene glycol methyl ether acetate, and 3kg of ethylene glycol ether acetate for 10 minutes at a stirring temperature of 80°C and at a stirring speed of 200r / min, then add 8kg of talcum powder and 10kg of Mongolian Remove soil, 12kg light calcium carbonate, 1kg vermiculite powder, 10kg porous powder quartz and stir for 10min, add 1.8kg terminal vinyl silicone oil, 1kg pine tar, 2kg compatibilizer, 1kg defoamer,...

Embodiment 3

[0028] A method for preparing a high heat dissipation LED lamp for a humid and corrupt environment, comprising the following steps:

[0029] S1. Stir 70kg of water-based hydroxyl fluorine-containing polyurethane resin, 4kg of bamboo charcoal fiber, and 250kg of ethylene glycol butyl ether acetate for 13min at a stirring temperature of 92°C, and add 8kg of methyl methacrylate-butadiene-styrene terpolymer Continue to stir for 4 minutes to obtain prefabricated material a;

[0030] S2. Stir 220kg of prefabricated material, 30kg of water-based acrylic resin, 3kg of propylene glycol methyl ether acetate, and 1.5kg of ethylene glycol ethyl ether acetate for 18 minutes at a stirring temperature of 65°C and a stirring speed of 240r / min, then add 4kg of talcum powder, 14kg of Montmorillonite, 6kg light calcium carbonate, 4kg vermiculite powder, 4kg porous powder quartz and stir for 17min, add 1.2kg terminal vinyl silicone oil, 1.4kg pine tar, 1.3kg compatibilizer, 1.7kg defoamer, 1.4kg ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an LED lamp with high heat dissipation and used in the humid and decomposition environment. The preparation method comprises the following steps that waterborne hydroxyl fluorinated polyurethane resin, bamboo carbon fibers, and 2-butoxyethyl acetate are stirred; methyl methacrylate-butadiene-styrene terpolymer is added and continuously stirred to obtain a prefabricated material a; the prefabricated material, waterborne acrylic resin, 2-acetoxy-1-methoxypropane and 2-ethoxyethyl acetate are stirred; talcum powder, montmorillonite, light calcium carbonate, vermiculite powder, and porous powdered quartz are stirred, end vinyl silicone oil, pine tar, a compatilizer, an anti-foaming agent, and a thickening agent are added and uniformly mixed to obtain a pre-processing coating; and the pre-processing coating is applied to the clean surface of an aluminum alloy section bar, an LED rear panel is obtained after solidification, and an LED chip is sealed and packed onto the LED rear panel to obtain the LED lamp with high heat dissipation and used in the humid and decomposition environment.

Description

technical field [0001] The invention relates to the technical field of LED lamps, in particular to a method for preparing high heat dissipation LED lamps used in humid and corrupt environments. Background technique [0002] Light-emitting diodes (LEDs) are widely used in the fields of display, TV lighting decoration and lighting because of their advantages that traditional light sources are inferior to, such as environmental protection and energy saving, high efficiency, long life, unbreakable, high switching speed, and high reliability. LED heat sinks are mostly made of aluminum alloy, but the current aluminum alloy is in the market. . . There are still some deficiencies, especially in humid and corrupt environments, where the requirements for moisture resistance and acid-base corrosion are high. At present, it is generally solved by coating heat-conducting coatings on the aluminum alloy surface, but the working reliability of the lamps is still very low. The problem of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F21K9/90C09D175/04C09D133/00C09D7/61C09D5/08
CPCC08K2003/265C09D5/08C09D7/61C09D7/70C09D175/04F21K9/90C08L33/00C08K3/34C08K3/346C08K3/26C08K7/26C08K7/06
Inventor 胡广储昭学
Owner ANHUI LANRUI ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com