A kind of fe-cr-ni-ti powder coated honeycomb zta ceramic preform and its preparation and application

A fe-cr-ni-ti, honeycomb technology, applied in ceramic products, applications, other household appliances, etc., can solve the problems of composite interface tearing, ceramic preform size limit, complex process, etc. Metallurgical bond strength, improved interfacial bond characteristics, and the effect of reducing complex processes

Active Publication Date: 2021-07-23
JINAN UNIVERSITY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor wettability between the composite metal or metal compound and the ceramic reinforcement, or no wetting at all, the interface bonding quality between the metal and the ceramic in the prepared composite material is poor, and tearing often occurs at the composite interface In addition, the bonding strength between ceramic particles is the decisive factor for the resistance to thermal shock and thermal shock of the metal solution. At present, the ceramic particles are mainly sintered by pressureless sintering technology near the melting point of the metal powder, and finally the bonding between the particles Molding, the process of this method is relatively complicated, it is difficult to guarantee the quality of the molding, and there are certain restrictions on the size and specifications of the ceramic preform

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of fe-cr-ni-ti powder coated honeycomb zta ceramic preform and its preparation and application
  • A kind of fe-cr-ni-ti powder coated honeycomb zta ceramic preform and its preparation and application
  • A kind of fe-cr-ni-ti powder coated honeycomb zta ceramic preform and its preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] 1) Take Fe, Cr, Ni, Ti powder with a purity of about 99.99%, particle size less than 200 mesh, Fe: 75%, Cr: 10.8%, Ni: 13.3%, Ti: 0.90% by weight, and alloy Chemical treatment, main mechanical alloying parameters: ball diameter: 5mm, ball to material ratio 10:1, speed 400r / min, ball milling time 48h. Usually the whole process of ball milling and powder filling is carried out under the environment of inert gas;

[0050] 2) In a 30mm×20mm×10mm cavity and a through Φ10mm cylindrical mold, add the Fe, Cr, Ni, Ti micropowder and ZTA ceramic particles obtained in step (1), then add water glass, and then add 10~ 12 purpose paraffin, wherein choose Fe, Cr, Ni, Ti mixed micropowder 2.4g, ZTA ceramic particles (ZrO 2 20wt.%, Al 2 o 3 Accounting for 80wt.%) 30g, the amount of water glass is 0.12g, 10-12 mesh paraffin wax particles are added as 0.65g as a pore-forming agent, the four are evenly mixed and processed, and the whole process is carried out in a protective atmosphere....

Embodiment 2

[0056] 1) Take Fe, Cr, Ni, Ti powder with a purity of about 99.99%, particle size less than 200 mesh, Fe: 78%, Cr: 10.0%, Ni: 11.0%, Ti: 1.0% by weight, and alloy Chemical treatment, main mechanical alloying parameters: ball diameter: 5mm, ball to material ratio 10:1, speed 400r / min, ball milling time 48h. Usually the whole process of ball milling and powder filling is carried out under the environment of inert gas;

[0057] 2) In a 30mm×20mm×10mm cavity and a through Φ10mm cylindrical mold, first add the Fe, Cr, Ni, Ti micropowder and ZTA ceramic particles obtained in step (1), then add water glass, and then add 10 ~12 purpose paraffin wax, wherein choose Fe, Cr, Ni, Ti mixed micropowder 2.4g, ZTA ceramic particles (ZrO 2 20wt.%, Al 2 o 3 Accounting for 80wt.%) 30g, the amount of water glass is 0.12g, 0.65g of 10-12 mesh paraffin particles are added as a pore-forming agent, and the four are uniformly mixed and processed, and the whole process is carried out in a protective...

Embodiment 3

[0062] 1) Take Fe, Cr, Ni, Ti powder with a purity of about 99.99%, particle size less than 200 mesh, Fe: 78.3%, Cr: 10%, Ni: 10.5%, Ti: 1.2% by weight, and mix the powder for alloying Chemical treatment, main mechanical alloying parameters: ball diameter: 5mm, ball to material ratio 10:1, speed 400r / min, ball milling time 48h. Usually the whole process of ball milling and powder filling is carried out under the environment of inert gas;

[0063] 2) In a 30mm×20mm×10mm cavity and a through Φ10mm cylindrical mold, add the Fe, Cr, Ni, Ti micropowder and ZTA ceramic particles obtained in step (1), then add water glass, and then add 10~ 12 purpose paraffin, wherein choose Fe, Cr, Ni, Ti mixed micropowder 2.4g, ZTA ceramic particles (ZrO 2 20wt.%, Al 2 o 3 Accounting for 80wt.%) 30g, the amount of water glass is 0.12g, 0.65g of 10-12 mesh paraffin particles are added as a pore-forming agent, the four are uniformly mixed, and the whole process is carried out in a protective atmos...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
crushing strengthaaaaaaaaaa
crushing strengthaaaaaaaaaa
crushing strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of material processing, and discloses a honeycomb ZTA ceramic prefabricated body coated with Fe-Cr-Ni-Ti micropowder, a preparation method and application thereof. Fe, Cr, and Ni elements are the main elements in chromium-based cast iron and high manganese steel. After alloying with Ti powder, it is beneficial to reduce the melting temperature of pure Ti powder. It is conducive to the formation of molten Ti, and through the diffusion reaction between Ti and oxygen in ZTA ceramics, a metal-ceramic bonding interface with high bonding strength is realized. In addition, water glass and CO 2 The reaction produces silicic acid with a certain connection strength, which promotes the bonding between ZTA ceramic particles and the shaping of the preform, and is beneficial to the preform's resistance to the erosion of poured liquid metal. In addition, paraffin wax is used as a pore-forming agent, which is beneficial to the uniform distribution and communication of cavities in the preform. Therefore, it can be well applied to the preparation of metal matrix composites.

Description

technical field [0001] The invention belongs to the field of material processing, and in particular relates to a honeycomb ZTA ceramic prefabricated body coated with Fe-Cr-Ni-Ti micropowder and its preparation method and application. Background technique [0002] Ceramic reinforced metal matrix composites, with high strength, heat resistance, and excellent composite properties of metal and ceramics, have attracted more and more attention, especially in the field of wear reduction and wear resistance. The application prospect is huge. Usually, the process of preparing ZTA ceramic / high chromium cast iron composite mainly includes two processes: first, the preparation of ZTA ceramic preform; secondly, the pressureless infiltration process of high chromium cast iron ZTA ceramic preform in molten state. The prefabricated body is the basis for the preparation of composite materials and is also the decisive factor for the performance of composite materials. Due to the poor wettab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/06C04B35/10C04B35/622C04B35/626B22F1/02C22C38/50
CPCC22C38/50C04B35/10C04B35/622C04B35/62605C04B38/068C04B2235/3427C04B2235/3244B22F1/16C04B38/0074
Inventor 涂小慧李卫郑宝超徐方伟林怀俊张鹏
Owner JINAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com