Conductive silver paste used for solar cells

A technology of solar cells and conductive silver paste, applied in circuits, conductive materials dispersed in non-conductive inorganic materials, photovoltaic power generation, etc., can solve problems such as adverse effects, improve wettability, overcome agglomeration and settlement, and have high viscosity at high temperature Effect

Inactive Publication Date: 2018-10-16
SUZHOU ISILVER MATERIALS
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, in previous studies, it was proposed to avoid glass crystallization, and it was believed that crystallization would cause adverse effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conductive silver paste used for solar cells
  • Conductive silver paste used for solar cells

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1~4

[0033] Embodiment 1~4: a kind of conductive silver paste for solar cell, described conductive paste is made up of the component of following parts by weight:

[0034] Table 1

[0035] ;

[0036] The above-mentioned organic carrier is formed by mixing butyl carbitol acetate, ethyl cellulose, acrylate, oleic acid, polypropylene glycol, and polyamide wax in a weight ratio of 75:7:6:4:3:5.

[0037] The above-mentioned organic carrier is formed by heating, stirring and mixing at a temperature of 90 degrees.

[0038] Note: embodiment 1 organic solvent is at least one in terpineol, butyl carbitol, propylene glycol phenyl ether, propylene glycol methyl ether, dimethyl glutarate, dimethyl succinate; embodiment 2 organic solvent It is a mixed solvent formed by butyl carbitol and propylene glycol phenyl ether; the organic solvent of embodiment 3 is propylene glycol phenyl ether; the organic solvent of embodiment 4 is a mixed solvent formed by terpineol and dimethyl glutarate.

[003...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses conductive silver paste used for solar cells. The conductive paste consists of the following components, by weight: 75-92 parts of silver powder, 5-12 parts of an organic solvent, 2-3 parts of an organic carrier, 0.5-1 part of alkyl phenol polyoxyethylene ether, and 0.8-5.3 parts of metal microcrystalline glass powder. The particle size D50 of the metal microcrystalline glass powder is 0.3-2 mu m. The metal microcrystalline glass powder consists of the following components: 10-50 parts of tellurium dioxide, 15-70 parts of titanium diboride, 2-10 parts of zinc oxide, 1-15 parts of silicon dioxide, 5-20 parts of lithium oxide, 0.4-2 parts of molybdenum oxide, 1-6 parts of boron oxide, 1-4 parts of germanium chloride, and 1-2 parts of strontium chloride. The conductivepaste effectively improves the conversion efficiency of cells, and has the characteristics of high temperature viscosity and large surface tension. Molten glass cannot not flow easily during a pastesintering process, thereby maintaining a fine line shape.

Description

technical field [0001] The invention relates to a conductive silver paste for solar cells, belonging to the technical field of solar cell functional materials. Background technique [0002] Photovoltaic cells, as an important branch of new clean energy, have achieved rapid development in recent years. Photovoltaic cell technology is also changing with each passing day. The entire industry chain is actively improving the conversion efficiency of photovoltaic cells and reducing costs through technological innovation, striving to achieve grid parity and replace traditional high pollution. energy. [0003] Crystalline silicon photovoltaic cells are currently the most important type of photovoltaic cells, accounting for more than 90%. The principle of photoelectric conversion is: boron-doped P-type silicon and phosphorus-doped N-type silicon form a PN junction. The junction then absorbs photon energy to excite electron transitions, forming electron-hole pairs, thereby generating...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B1/22H01L31/0224
CPCH01B1/22H01L31/022425Y02E10/50
Inventor 周欣山汪山包娜
Owner SUZHOU ISILVER MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com