Liquid development white photoimageable ink and preparation method thereof

A photosensitive solder resist ink, white technology

Inactive Publication Date: 2018-09-14
江苏海田电子材料有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a liquid-developed white photosensitive solder resist ink suitable for flexible electric board printing and its preparation method to overcome the disadvantages of long curing time, high brittleness of the cured film and printing problems. The disadvantage of low precision

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid development white photoimageable ink and preparation method thereof
  • Liquid development white photoimageable ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Mix o-cresol novolac epoxy acrylate, butyl cellosolve, di-tert-butyl p-cresol polymerization inhibitor and triethylamine catalyst and heat up to 75° C. and stir for 45 minutes, then add the toluene solution of phthalic anhydride, (o The reaction molar ratio of cresol novolac epoxy acrylate, butyl cellosolve, di-tert-butyl p-cresol, triethylamine and phthalic anhydride is 3:1:0.2:0.3:2) to react until the acid value is the initial acid After half of the value, the solvent is distilled off under reduced pressure to obtain polybasic anhydride modified novolak epoxy acrylate.

Embodiment 2

[0038] Mix o-cresol novolak epoxy acrylate, butyl cellosolve, di-tert-butyl p-cresol polymerization inhibitor and triethylamine catalyst and heat up to 80° C. and stir for 30 minutes, then add the toluene solution of phthalic anhydride, (o The reaction molar ratio of cresol novolac epoxy acrylate, butyl cellosolve, di-tert-butyl p-cresol, triethylamine and phthalic anhydride is 3:1:0.2:0.3:5) to react until the acid value is the initial acid After half of the value, the solvent is distilled off under reduced pressure to obtain polybasic anhydride modified novolak epoxy acrylate.

Embodiment 3

[0040] Step 1: Take 42 parts of polybasic anhydride-modified novolak epoxy acrylate prepared in Example 1, 16 parts of acrylic active monomers (dipropylene glycol diacrylate and tetrahydrofuran acrylate monomers, the weight ratio is 1:1) and light 8 parts of the initiator 2-hydroxy-2-methyl-1-phenyl-1-acetone are put into the feeding channel;

[0041] Step 2: Use a high-speed disperser at a speed of 900r / min to disperse at 75°C for 0.6h, stop stirring and keep warm;

[0042] Step 3: Add 6 parts of titanium dioxide, 3 parts of barium sulfate, 4 parts of fluorine-containing surfactant, 2 parts of defoamer, 2 parts of water reducer and 2 parts of leveling agent into the feed liquid obtained in step 2, and continue with Stir at 600r / min for 0.4h;

[0043] Step 4: After stirring and mixing, use a hydraulic three-roller to grind until the particle size is below 300 nanometers;

[0044] Step 5: It is obtained after filtering with a 1 μm filter element filter.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses liquid development white photoimageable ink and a preparation method thereof. The liquid development white photoimageable ink comprises, by weight, 30-45 parts of multi-elementanhydride modified linear phenolic epoxy acrylate, 10-20 parts of acrylic acid active monomer, 5-10 parts of photoinitiator, 3-8 parts of titanium dioxide, 2-5 parts of barium sulfate, 2-6 parts of fluorine-containing surfactant, 1-3 parts of defoaming agent, 1-3 parts of water reducing agent and 1-3 parts of leveling agent. The liquid development white photoimageable ink and the preparation method thereof have the advantages that multi-element phthalic anhydride is used to modify o-cresol formaldehyde epoxy acrylate to obtain the multi-element anhydride modified linear phenolic epoxy acrylate, the multi-element anhydride modified linear phenolic epoxy acrylate is small in thermal expansion coefficient, stable in dimension, high in softening temperature and capable of guaranteeing the cold dryness of a substratum before exposure, and accordingly the precision of circuit board printing is increased.

Description

technical field [0001] The invention relates to a liquid developing white photosensitive solder resist ink and a preparation method thereof, belonging to the field of solder resist inks. Background technique [0002] Liquid photosensitive ink is a special UV ink, which can be used for full-page printing without a printing plate. After the ink coating is photosensitive cured and developed, it can be processed by etching, electroplating, electrophoretic coloring, etc., which is suitable for the production of small batch, multi-variety, personalized and high-precision graphic products. The solder mask is a permanent protective layer coated on the surface of the printed board. It selectively protects the surface of the printed board and prevents short circuits and bridging between wires and pads when soldering components. In addition, it also has the functions of moisture proof, mildew proof and salt spray proof. Therefore, the quality of the solder mask not only affects the a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/107C09D11/03G03F7/004C08G59/14
CPCC08G59/1438C09D11/03C09D11/107G03F7/004
Inventor 王琦常红言
Owner 江苏海田电子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap