Flame-retardant type textile fabric

A textile fabric, flame-retardant technology, applied in the field of flame-retardant textile fabrics, can solve the problems of wrinkle resistance, poor resilience, easy shrinkage and deformation, etc., and achieve the effect of simple preparation process and superior flame-retardant performance

Inactive Publication Date: 2018-08-28
FOSHAN YIXIANG DISI CLOTHING DESIGN CO LTD
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, cellulose fiber fabrics are easy to shrink and deform when taking and washing, and have poor wrinkle resistance and resilience.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1) Preparation of nano-zinc oxide-nano-titanium dioxide:

[0023] Dissolve zinc acetate in absolute ethanol, stir evenly to obtain a mixed solution, evaporate the mixed solution to dryness in a water bath, then put it in an oven for drying, and then put it in a muffle furnace for high-temperature roasting to obtain nano-zinc oxide Powder: Mix the prepared nano-zinc oxide powder, absolute ethanol and glacial acetic acid, continue to add butyl titanate for hydrolysis, evaporate to dryness in a water bath, and perform drying treatment to obtain a composite powder of nano-zinc oxide and nano-titanium dioxide .

[0024] 2) Weigh the following components by mass for later use: 22 parts of pentachlorophenol, 24 parts of ammonium polyphosphate, 20 parts of nano-zinc oxide-nano-titanium dioxide, 18 parts of nano-carbon powder, 24 parts of polyvinylpyrrolidone, 20 parts of sodium polyacrylate 18 parts, 18 parts of volcanic ash, 24 parts of vinyl acetate.

[0025] 3) Flame retar...

Embodiment 2

[0032] 1) Preparation of nano-zinc oxide-nano-titanium dioxide:

[0033] Dissolve zinc acetate in absolute ethanol, stir evenly to obtain a mixed solution, evaporate the mixed solution to dryness in a water bath, then put it in an oven for drying, and then put it in a muffle furnace for high-temperature roasting to obtain nano-zinc oxide Powder: Mix the prepared nano-zinc oxide powder, absolute ethanol and glacial acetic acid, continue to add butyl titanate for hydrolysis, evaporate to dryness in a water bath, and perform drying treatment to obtain a composite powder of nano-zinc oxide and nano-titanium dioxide .

[0034] 2) Weigh the following components by mass for later use: 22 parts of pentachlorophenol, 24 parts of ammonium polyphosphate, 20 parts of nano-zinc oxide-nano-titanium dioxide, 18 parts of nano-carbon powder, 24 parts of polyvinylpyrrolidone, 20 parts of sodium polyacrylate 18 parts, 18 parts of volcanic ash, 24 parts of vinyl acetate.

[0035] 3) Flame retar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a flame-retardant type textile fabric. A used flame retardant coating layer is prepared from the following components: pentachlorophenol, ammonium polyphosphate, basalt fiber,nano carbon powder, polyvinylpyrrolidone, sodium polyacrylate, pozzolan and vinyl acetate. A preparation technique of a flame retardant for the textile fabric is simple, and the prepared product is relatively high in flame retarding performance.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a flame-retardant textile fabric. Background technique [0002] China is a big country in the production and export of textiles. After years of development, China's textile industry has obvious competitive advantages. It has the most complete industrial chain in the world, the highest level of processing facilities, and many developed industrial clusters to respond to market risks. Self-regulation The continuous enhancement of capabilities provides a solid guarantee for the industry to maintain a steady pace of development. From the perspective of the international environment, there is still a lot of room and opportunity for expansion in the international market. With the expiry of the China-Europe textile quotas at the end of 2007 and the end of the Sino-US textile quotas at the end of 2008, the era of China's textile quota-free is approaching, and the regions accounting for ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06N3/00D06N3/04C09D4/06C09D5/18C01G23/053
CPCD06N3/0006C01G23/053C09D4/06C09D5/18D06N3/0015D06N3/0061D06N3/0063D06N3/04D06N3/045D06N2201/042D06N2201/045D06N2201/085D06N2209/067
Inventor 刘广飞
Owner FOSHAN YIXIANG DISI CLOTHING DESIGN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com