Material for environment-friendly doors and windows and preparation method of material

A kind of door and window, environmental protection technology, applied in the material and preparation field of environmental protection door and window, can solve the problems such as the anti-ultraviolet performance and acid resistance of environmental protection doors and windows, and achieve the effect of improving the anti-ultraviolet performance and acid resistance

Inactive Publication Date: 2018-04-27
长沙善道新材料科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a material for environmentally friendly doors and windows and a preparation method thereof, in order to solve the anti-ultraviolet performance of materials for environmentally friendly doors and windows disclosed in the Chinese patent document "An energy-saving and environmentally friendly composite door and window profile and its preparation method (application publication number: CN107141725A)" and the problem of insufficient acid resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Material for environment-friendly doors and windows and preparation method of material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0018] The preparation method of the material of described environmental protection door and window, comprises the following steps:

[0019] S1. Heat up vinyl resin, polyvinyl chloride and halogenated unsaturated polyester to 140-160°C, keep warm for 20-40min, then add glass fiber felt, steel fiber, polyphenylene sulfide fiber, ceramic fiber, bamboo charcoal powder, Mix nano-titanium dioxide, ammonium persulfate, polyamide fiber, trichloroethyl phosphate, barium metaborate and magnesium hydroxide evenly, continue to heat up to 180-220°C, keep warm for 5-15min, and stir at 3500-5500r / min for 1 -2h, cooled to room temperature to obtain the base material;

[0020] S2. Mix the hydroxyl-terminated polybutadiene and azobisisobutylcyanide evenly, heat up to 120-140° C., keep warm for 20-40 minutes, then add single-walled carbon nanotubes, chitosan and hydroxyapatite and mix evenly. Stir at 650-850r / min for 1-2h, then cool down to 60-80°C, keep warm for 5-15min, then add UV absorber ...

Embodiment 1

[0024] A kind of material of environment-friendly door and window, with weight part as unit, comprises following raw material: vinyl resin 46.8 parts, polyvinyl chloride 31.6 parts, hydroxyl-terminated polybutadiene 12.4 parts, halogenated unsaturated polyester 7.3 parts, glass fiber mat 5.6 parts, 4.7 parts of steel fiber, 2.4 parts of polyphenylene sulfide fiber, 4.5 parts of ceramic fiber, 6.9 parts of bamboo charcoal powder, 5.2 parts of nano-titanium dioxide, 3.6 parts of ammonium persulfate, 2.2 parts of azobisisobutylcyanide, 5.1 parts of polyamide fiber Parts, 6.6 parts of trichloroethyl phosphate, 4.7 parts of barium metaborate, 3.5 parts of magnesium hydroxide, 5.6 parts of silane coupling agent KH-570, 5.7 parts of polyhydroxyzinc terephthalate, modified ethylene difatty acid acyl 6.9 parts of amine, 54.9 parts of ultraviolet absorber triazine, 2.3 parts of phenyl salicylate, 4.5 parts of single-walled carbon nanotubes, 7.4 parts of chitosan, and 1.7 parts of hydroxy...

Embodiment 2

[0030] A kind of material of environment-friendly door and window, with weight part as unit, comprises following raw material: vinyl resin 40 parts, polyvinyl chloride 35 parts, hydroxyl-terminated polybutadiene 5 parts, halogenated unsaturated polyester 9 parts, glass fiber mat 3 parts, 5 parts of steel fiber, 1 part of polyphenylene sulfide fiber, 6 parts of ceramic fiber, 4 parts of bamboo charcoal powder, 6 parts of nano-titanium dioxide, 2 parts of ammonium persulfate, 4 parts of azobisisobutylcyanide, 3 parts of polyamide fiber 8 parts, 8 parts of trichloroethyl phosphate, 3 parts of barium metaborate, 5 parts of magnesium hydroxide, 4 parts of silane coupling agent KH-5704, 8 parts of polyhydroxyzinc terephthalate, modified ethylene bis fatty acid acyl 3 parts of amine, 56 parts of ultraviolet absorber triazine, 2 parts of phenyl salicylate, 6 parts of single-walled carbon nanotubes, 6 parts of chitosan, and 2 parts of hydroxyapatite.

[0031] The preparation method of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a material for environment-friendly doors and windows and a preparation method of the material. The material comprises chlorinated polyvinyl chloride resin, neoprene, nitrile-butadiene rubber, vinisol, polyphenylene sulfide, polyethylene wax, dimethyl phthalate, nano boron nitride, sepiolite powder, antimony trioxide, zinc stearate, aluminum tripolyphosphate, tungsten disulfide, copper oxide, titanium dioxide, carbon fibers, 2,2'-azoisobutyronitrile, mineral wool, magnesium powder, borax, chitosan and 1, 3-butanediol. The preparation method includes: preparing a main material, preparing a modification material, mixing the main material, the modification material, polyhydroxy zinc terephthalate and modified ethylene bis-fatty acid imide, and performing heating, plasticizing, extrusion, rolling and the like to obtain the material. The material is high in strength, high in fire resistance and excellent in ultraviolet resistance and acid resistance.

Description

【Technical field】 [0001] The invention belongs to the technical field of door and window material preparation, and in particular relates to an environment-friendly door and window material and a preparation method thereof. 【Background technique】 [0002] Plastic steel profiles are referred to as plastic steel, and the main chemical composition is PVC, so it is also called PVC profiles. It is a new type of building material that is widely used. , excellent anti-aging performance, usually used as a substitute for non-ferrous metals such as steel, zinc, aluminum, etc. [0003] Chinese patent application document "An energy-saving and environment-friendly composite door and window profile and its preparation method (application publication number: CN107141725A)" discloses an energy-saving and environment-friendly composite door and window profile, including the following raw materials in parts by weight: vinyl resin 50-60 parts, 35-45 parts of halogenated unsaturated polyester,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L101/00C08L27/06C08L47/00C08L67/06C08L81/02C08L5/08C08K13/06C08K9/06C08K7/14C08K7/06C08K5/3492C08K5/134C08K7/24C08K3/32C08K5/5425
Inventor 不公告发明人
Owner 长沙善道新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com