A kind of automobile exhaust pipe and muffler powder coating and preparation method thereof

A technology for powder coatings and automobile exhaust, applied in powder coatings, coatings and other directions, can solve the problems of poor decorative performance of surface texture coatings, large particle size gaps, uneven coatings, etc., to achieve excellent decorative effects and color. Brilliant, high-quality finish

Active Publication Date: 2019-11-15
ZHANGJIAGANG JIANGNAN POWDER COATING
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Powder coating is a new type of solvent-free, easy-to-operate, 100% solid powder-like environmentally friendly coating. The powder coating has high utilization efficiency and is widely used in household appliances, automobiles, construction, petroleum and petrochemical industries; traditional high-temperature-resistant powder coatings Most of them are black sand grain paints, with poor surface texture and paint decoration performance; traditional high-temperature resistant powder paints have a large gap in particle size, and the coating is uneven during coating, and the overall coating thickness is often thick

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of automobile exhaust pipe and muffler powder coating and preparation method thereof
  • A kind of automobile exhaust pipe and muffler powder coating and preparation method thereof
  • A kind of automobile exhaust pipe and muffler powder coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Produce a kind of automobile exhaust pipe and muffler powder coating, its specific steps are as follows:

[0048] a. Weigh the raw materials and prepare the following raw materials in parts by mass:

[0049] Methylphenyl silicone resin 50kg;

[0050] Lead-free low temperature molten glass powder (300 mesh) 20kg;

[0051] Polyimide powder (300 mesh) 15kg;

[0052] Leveling agent 3kg;

[0053] Silane coupling agent KH550 2kg;

[0054] Titanate coupling agent 1kg;

[0055] Inorganic ceramic pigment 15kg;

[0056] Benzoin 1kg;

[0057] White carbon black 0.8kg;

[0058] b. Add the methyl phenyl silicone resin prepared in step a, lead-free low temperature molten glass powder, leveling agent, silane coupling agent KH550, titanate coupling agent, inorganic ceramic pigment and benzoin into the mixer Misai Carat cylinder, pre-mixing, mixing time: low speed 2 minutes, high speed 6 minutes; low speed speed is 100r / min, high speed speed is 280r / min;

[0059] c. Put the homog...

Embodiment 2

[0065] Produce a kind of automobile exhaust pipe and muffler powder coating, its specific steps are as follows:

[0066] a. Weigh the raw materials and prepare the following raw materials in parts by mass:

[0067] Methylphenyl silicone resin 55.3kg;

[0068] Lead-free low temperature molten glass powder (300) 22.6kg;

[0069] Polyimide powder (300) 17.8kg;

[0070] Leveling agent 4kg;

[0071] Silane coupling agent KH550 2.6kg;

[0072] Titanate coupling agent 1.5kg;

[0073] Inorganic ceramic pigment 18.4kg;

[0074] Benzoin 1kg;

[0075] White carbon black 0.8kg;

[0076] b. Add the methyl phenyl silicone resin prepared in step a, lead-free low temperature molten glass powder, leveling agent, silane coupling agent KH550, titanate coupling agent, inorganic ceramic pigment and benzoin into the mixer Misai Carat cylinder, pre-mixing, mixing time: low speed 2 minutes, high speed 6 minutes; low speed speed is 100r / min, high speed speed is 280r / min;

[0077] c. Put the h...

Embodiment 3

[0083] Produce a kind of automobile exhaust pipe and muffler powder coating, its specific steps are as follows:

[0084] a. Weigh the raw materials and prepare the following raw materials in parts by mass:

[0085] Methylphenyl silicone resin 60kg;

[0086] Lead-free low-temperature molten glass powder (300 mesh) 30kg;

[0087] Polyimide powder (300 mesh) 20kg;

[0088] Leveling agent 5kg;

[0089] Silane coupling agent KH550 3kg;

[0090] Titanate coupling agent 2kg;

[0091] Inorganic ceramic pigment 20kg;

[0092] Benzoin 1kg;

[0093] White carbon black 0.8kg;

[0094] b. Add the methyl phenyl silicone resin prepared in step a, lead-free low temperature molten glass powder, leveling agent, silane coupling agent KH550, titanate coupling agent, inorganic ceramic pigment and benzoin into the mixer Misai Carat cylinder, pre-mixing, mixing time: low speed 2 minutes, high speed 6 minutes; low speed speed is 100r / min, high speed speed is 280r / min;

[0095] c. Put the hom...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a powder coating for an automobile exhaust pipe and a silencer and a preparation method thereof. The adopted materials in parts by weight are as follows: 50-60 parts of methyl phenyl silicone resin, 20-30 parts of unleaded low-temperature fused glass powder, 15-20 parts of polyimide powder, 3-5 parts of a flatting agent, 2-3 parts of a silane coupling agent KH550, 1-2 parts of a titanate coupling agent, 15-20 parts of inorganic ceramic pigment, 1 part of benzoin and 0.8 part of white carbon black. The prepared powder coating is uniform and bright in color, has a better decorating effect, has an excellent high temperature resisting property and can meet the requirement on the surface coating of the automobile exhaust pipe and the silencer.

Description

technical field [0001] The invention belongs to the technical field of powder coatings, in particular to an automobile exhaust pipe and muffler powder coating and a preparation method thereof. Background technique [0002] Automobile exhaust pipe and muffler are used to discharge the exhaust gas produced by the combustion of fuel in the combustion chamber of the automobile engine. The temperature in the combustion chamber of the automobile can reach up to 2000°C, and the temperature of the exhaust gas is relatively high. The exhaust gas passes through the exhaust pipe and muffler to make the exhaust pipe The surface temperature of the muffler and muffler reaches 300-400°C, and under high load conditions, it can reach 500-600°C. The high temperature resistance of the coating on the surface of the automobile exhaust pipe and muffler is high. [0003] Powder coating is a new type of solvent-free, easy-to-operate, 100% solid powder-like environmentally friendly coating. The powd...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/04C09D179/08C09D5/03C09D7/61C09D7/63
CPCC08L2203/18C09D5/033C09D183/04C08L79/08C08K13/02C08K3/40C08K3/36C08K5/10C08K5/544
Inventor 黎永新田晖华鹤林陈传东
Owner ZHANGJIAGANG JIANGNAN POWDER COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com