Root-resistant water-based spraying and non-cured rubber asphalt waterproof coating

A kind of asphalt waterproof coating and non-curing rubber technology, which is applied in the direction of asphalt coating, coating, conjugated diene coating, etc., can solve the problems such as unsatisfactory adhesion effect of wet interface, health hazards of construction workers, long construction period, etc. Creep property and self-healing ability, improvement of construction efficiency and quality, strong bonding effect

Active Publication Date: 2017-12-08
JIANGYIN CHAMPION CHEM +1
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned non-curing rubber asphalt waterproof coating has the following disadvantages: heating is required for construction, not only energy waste exists, the construction period is long due to low construction efficiency, and the VOC emission in the construction environment will cause harm to the health of construction workers due to the large energy consumption of heating construction; wet interface The adhesion effect is not ideal, and it cannot be directly pasted
It requires high-temperature construction, which leads to the loss of the effective flow of the root-blocking agent during the heating process, and the process is not environmentally friendly, and cannot achieve a satisfactory root-blocking effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Root-resistant water-based spraying and non-cured rubber asphalt waterproof coating
  • Root-resistant water-based spraying and non-cured rubber asphalt waterproof coating
  • Root-resistant water-based spraying and non-cured rubber asphalt waterproof coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The anti-root puncture water-based spraying non-curing rubber asphalt waterproof coating composition of embodiment 1 comprises by weight parts:

[0030] 70 parts of anionic rubber elastomer modified emulsified asphalt, 8 parts of modified resin emulsion with a solid content of 70%, 2 parts of coagulation accelerator, 0.1 part of chemical root inhibitor, 0.005 part of defoamer, 0.3 part of dispersant, stabilizer 0.05 parts, 20 parts of filler;

[0031] Among them, the main composition of anionic rubber modified emulsified asphalt is 70 parts of base asphalt, 2 parts of SBS rubber particles, 4 parts of SBR rubber powder, 3 parts of NBR rubber powder, 40 parts of deionized water, 1 part of anionic emulsifier, nonionic surface active 2 parts of agent, 1 part of aromatic oil. Wherein the anionic emulsifier is selected from the group consisting of sulfate ester salt and nonionic surfactant alkylphenol polyoxyethylene ether; the modified resin emulsion is terpene resin emulsi...

Embodiment 2

[0034] The difference between embodiment 2 and embodiment 1 is that the anti-root puncture water-based spraying non-curing rubber asphalt waterproof coating composition includes by weight parts:

[0035] 80 parts of anionic rubber elastomer modified emulsified asphalt, 13 parts of modified resin emulsion with a solid content of 42%, 0.05 parts of coagulant, 3 parts of chemical root inhibitor, 0.9 part of defoamer, 0.003 part of dispersant, stabilizer 1 part, 5 parts of filler;

[0036] The composition and parts by weight of anionic rubber modified emulsified asphalt are: 60 parts of base asphalt, 2 parts of SBS rubber particles, 4 parts of SBR rubber powder, 3 parts of NBR rubber powder, 40 parts of deionized water, 1 part of anionic emulsifier, 2 parts of ionic surfactant, 1 part of naphthenic oil.

Embodiment 3

[0038] The difference between Example 3 and Example 1 is that there are 80 parts of anionic rubber elastomer modified emulsified asphalt, 13 parts of modified resin emulsion with a solid content of 42%, 0.05 parts of coagulation accelerator, 0.9 parts of defoamer, and 0.003 parts of dispersant 15 parts of chemical root inhibitor, 1 part of stabilizer, 5 parts of filler;

[0039] The composition and parts by weight of anionic rubber modified emulsified asphalt are: 40 parts of base asphalt, 5 parts of SBS rubber particles, 1 part of SBR rubber powder, 7 parts of NBR rubber powder, 10 parts of deionized water, 3 parts of anionic emulsifier, non- 0.5 parts of ionic surfactant, aromatic oil and naphthenic oil are added in a weight ratio of 1:1, and the sum of parts by weight is 3 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a root-resistant water-based spraying and non-cured rubber asphalt waterproof coating which is prepared from the following components in parts by weight: 70-80 parts of anionic rubber elastomer modified emulsified asphalt, 8-13 parts of modified resin emulsion with the solid content being 42-70%, 0.1-15 parts of chemical root resisting agent, 0.05-2 parts of coagulation accelerator, 0.005-0.9 part of antifoaming agent, 0.003-0.3 part of dispersing agent, 0.05-1 part of stabilizer and 5-20 parts of filler, wherein the anionic rubber modified emulsified asphalt is mainly prepared from matrix asphalt, SBS rubber particles, SBR rubber powder, NBR rubber powder, deionized water, anionic emulsifier, nonionic surfactant and at least one of arene oil and naphthene oil. A formed waterproof layer material has the advantages of no curing, high creep property, strong seal-healing ability and excellent root resistance; moreover, the root resistance can be maintained for 15 years or longer.

Description

technical field [0001] The invention relates to the technical field of rubber asphalt coating compositions, in particular to a root puncture-resistant water-based spraying non-curing rubber asphalt waterproof coating. Background technique [0002] Non-curing rubber asphalt waterproof coatings and coatings have good adhesion, extensibility, self-healing properties, good low temperature flexibility, and can achieve seamless construction in waterproof construction. It is a new type of asphalt waterproof material. For example, the non-curing rubber asphalt waterproof coating disclosed in Chinese patent CN105199600A consists of the following components in parts by weight: 10-50 parts of petroleum asphalt, 5-40 parts of waste rubber powder, 10-25 parts of waste engine oil, styrene-butadiene 0.5-8 parts of olefinic block copolymer, 2-15 parts of styrene-butadiene rubber, 2-10 parts of recycled plastic particles, 8-12 parts of terpene resin, 4-6 parts of coumarone resin, 0.1-3 parts...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D153/02C09D109/06C09D109/02C09D145/00C09D123/00C09D7/12
CPCC08K2003/162C08K2003/287C08K2003/3045C08L2205/02C08L2205/035C09D195/00C08L53/02C08L9/06C08L9/02C08L45/00C08K3/346C08K3/28C08L23/00C08K3/34C08K3/16C08K3/30
Inventor 冯永
Owner JIANGYIN CHAMPION CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com