High-performance uniform-shrinkage-rate PET composite material and preparation method thereof

A technology of composite material and shrinkage rate, which is applied in the field of high-performance PET composite materials with uniform shrinkage rate and its preparation, can solve the problems of uneven shrinkage rate of PET composite materials, and achieve poor impact strength, uniform shrinkage rate, and mechanical strength. The effect of excellent performance

Inactive Publication Date: 2017-10-20
ANHUI JIANGHUAI AUTOMOBILE GRP CORP LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a high-performance PET composite material with uniform shrinkage and its preparation method to solve the problem of uneven shrinkage of PET composites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance uniform-shrinkage-rate PET composite material and preparation method thereof
  • High-performance uniform-shrinkage-rate PET composite material and preparation method thereof
  • High-performance uniform-shrinkage-rate PET composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] The preparation method of any one of the above-mentioned high-performance and uniform shrinkage PET composite materials includes the following steps:

[0040] (1) Weigh 80 parts to 100 parts of PBT, 6 parts to 10 parts of basalt fiber, 10 parts to 16 parts of mica powder, 0.1 part to 0.5 part of antioxidant, and 0.1 part to 0.3 part of lubricant to mix and stir evenly, Get the mixture

[0041] (2) Extruding and granulating the mixture obtained in step (1) to obtain a PET composite material.

[0042] The step (2) is specifically:

[0043] Put the mixture obtained in step (1) into the hopper of a twin-screw extruder for extruding and pelletizing, wherein the twin-screw extruder includes six temperature zones arranged in sequence, one zone having a temperature of 240~ 260℃, the second zone temperature is 280~300℃, the third zone temperature is 280~300℃, the fourth zone temperature is 280~300℃, the fifth zone temperature is 280~300℃, the sixth zone temperature is 280~300℃, the mac...

Embodiment 1

[0046] (1) Weigh 80 parts of PET, 6 parts of basalt fiber, 10 parts of mica powder, 0.1 part of Irganox168, and 0.1 part of zinc stearate, mix and stir to obtain a mixture;

[0047] (2) Extruding and granulating the mixture obtained in step (1) to obtain the PET composite material P1.

[0048] Preferably, the step (2) is specifically:

[0049] Put the mixture obtained in step (1) into the hopper of a twin-screw extruder for extrusion and granulation to obtain a PET composite material, wherein the twin-screw extruder includes six temperature zones arranged in sequence , The temperature in the first zone is 240℃, the temperature in the second zone is 280℃, the temperature in the third zone is 280℃, the temperature in the fourth zone is 280℃, the temperature in the fifth zone is 280℃, the temperature in the sixth zone is 280℃, the head temperature is 280℃, and the screw speed is 200r / min.

Embodiment 2

[0051] (1) Weigh 100 parts of PET, 10 parts of basalt fiber, 16 parts of mica powder, 0.1 part of Irganox 168, 0.2 part of Irganox 1010, 0.2 part of Irganox 1330, 0.15 part of potassium stearate, 0.15 part of zinc stearate, mix and stir evenly, Get the mixture

[0052] (2) Extruding and granulating the mixture obtained in step (1) to obtain the PET composite material P2.

[0053] Preferably, the step (2) is specifically:

[0054] The mixture obtained in step (1) is put into the hopper of a twin-screw extruder to be extruded and pelletized to obtain a PET composite material, wherein the twin-screw extruder includes six temperature zones arranged in sequence , Zone 1 temperature is 260℃, Zone 2 temperature is 300℃, Zone 3 temperature is 300℃, Zone 4 temperature is 300℃, Zone 5 temperature is 300℃, Zone 6 temperature is 300℃, head temperature is 300℃, screw speed is 280r / min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-performance uniform-shrinkage-rate PET composite material and a preparation method thereof. The PET composite material consists of the following components in parts by weigh as follows: 80-100 parts of PET, 6-10 parts of basalt fibers, 10-16 parts of mica powder, 0.1-0.5 part of an antioxidant and 0.1-0.3 part of a lubricant. According to the invention, the prepared PET composite material has excellent mechanical properties and uniform lateral and longitudinal shrinkage rates, ameliorates the problems that the impact property of PET composite materials is low and the shrinkage rate of the PET composite materials is not uniform. positive nitrogen ions N<+> are introduced to the surfaces of the basalt glass fibers through plasma processing, so that the active sites of the surfaces are increased, and the surface polarity is improved, and accordingly the attractive force and adhesive ability of the glass fiber surfaces are increased and the compatibility of the glass fibers and PET matrix is improved.

Description

Technical field [0001] The invention belongs to the technical field of polymer materials, and particularly refers to a high-performance PET composite material with uniform shrinkage rate and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PET) is a common macromolecular polyester resin. It has good optical properties and weather resistance, but at the same time it also has a small notch impact strength and aspect ratio shrinkage. The shortcomings of unevenness, easy to break and irregular surface. Summary of the invention [0003] The purpose of the present invention is to provide a high-performance PET composite material with uniform shrinkage rate and a preparation method thereof, so as to solve the problem of uneven shrinkage rate of the PET composite material. [0004] The present invention is realized through the following technical solutions: [0005] A high-performance PET composite material with uniform shrinkage, which is composed of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08K13/06C08K9/02C08K9/00C08K7/10C08K3/34C08K5/526C08K5/098C08J5/06C08J5/10
CPCC08J5/06C08J5/10C08J2367/02C08K3/34C08K5/098C08K5/526C08K7/10C08K9/00C08K9/02C08K13/06C08K2201/003C08K2201/014C08L67/02
Inventor 刘凯伏建博王添琪
Owner ANHUI JIANGHUAI AUTOMOBILE GRP CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com