Polyethylene talcum powder master batch

A technology of talc masterbatch and polyethylene, which is applied in the field of plastic materials, can solve the problems of inability to effectively improve plastic dispersibility, poor thermal stability, etc., and achieve easy feeding, good thermal stability, and improved dispersibility. Effect

Inactive Publication Date: 2017-09-08
苏州优矿塑新材料股份有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polyethylene talcum powder masterbatch is a kind of plastic modified filler, which refers to the granules formed by mixing and granulating the main component of talc powder with polymers or other carriers. It is mainly used to improve the properties of rubber, plastic resins, etc. Improve the stiffness, high temperature creep resistance, heat resistance and other properties of the filling material; but the existing polyethylene talcum powder masterbatch cannot effectively improve the dispersion of plastics; and the thermal stability is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The present invention will be further described in detail below in conjunction with specific embodiments.

[0010] A polyethylene talcum powder masterbatch, which comprises the following components in terms of weight percentage: 19.5-20.5% polyethylene, 0.1-1.1% polyethylene wax and 78.9-79.9% talcum powder; Add polyethylene, and then add polyethylene wax, heat the mixture to 150°C, heat for 12 minutes, then enter the twin-screw extruder for mixing, extrude, cool and pelletize after mixing.

[0011] Described talcum powder adopts density as 2.8g / cm 3 , hardness Mohs hardness value 1, loose bulk density: 0.11g / cm 3 The talcum powder, the water content at 105 ℃: 0.2%; The talcum powder includes: silicon dioxide 60.9%, magnesium oxide 31.5%, calcium oxide 0.2%, ferric oxide 0.20%, aluminum oxide 0.2% %, T-4 type talc powder composed of 7% loss on ignition at 1050°C; the T-4 type talc powder is measured by the particle size distribution of the sedimentation diagram D50: 0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyethylene talcum powder master batch. The polyethylene talcum powder master batch is prepared from, by weight, 19.5-20.5% of polyethylene, 0.1-1.1% of polyethylene wax and 78.9-79.9% of talcum powder. During preparation, talcum powder is put at first, polyethylene is added, then, the polyethylene wax is added, the mixture is subjected to smelting to be heated to 150 min, heating is performed for 12 min, then, the mixture enters a double-screw extruder to be mixed, mixing is performed, and then extruding, cooling and grain dicing are performed. In this way, the polyethylene talcum powder master batch is applicable to plastic modification, and due to the compact form and the higher compound quantity, the plastic is good in dispersity, resistant to wear and scraping, capable of achieving feeding easily and good in heat stability.

Description

technical field [0001] The invention relates to the field of plastic materials, in particular to a plastic material that is very suitable for plastic modification. Due to its compacted form and higher compounding amount, the plastic has good dispersion, wear resistance, scratch resistance, and easy feeding. , Polyethylene talcum powder masterbatch with good thermal stability. Background technique [0002] Polyethylene talcum powder masterbatch is a kind of plastic modified filler, which refers to the granules formed by mixing and granulating the main component of talc powder with polymers or other carriers. It is mainly used to improve the properties of rubber, plastic resins, etc. Improve the stiffness, high temperature creep resistance, heat resistance and other properties of the filling material; but the existing polyethylene talcum powder masterbatch cannot effectively improve the dispersion of plastics; and the thermal stability is not good. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08K7/00C08K3/34C08K3/36C08K3/22C08J3/22
CPCC08L23/06C08J3/226C08J2323/06C08K2003/2206C08K2003/222C08K2003/2227C08K2003/2272C08L2201/08C08L2205/025C08K7/00C08K3/34C08K3/36C08K3/22
Inventor 王银木
Owner 苏州优矿塑新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com