A kind of PVC coating cured by uv-led light source and preparation method thereof

A UV-LED, light source technology, used in polyester coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of short service life of high-pressure mercury lamps, substrate deformation, equipment corrosion, etc., and achieve broad market application prospects , The effect of preventing oxygen inhibition and good adhesion

Active Publication Date: 2019-06-14
TIANJIN JIURI NEW MATERIALS CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, only 20% of the power of ultraviolet light bulbs is transformed into ultraviolet rays, visible light accounts for 10%, and infrared rays and heat energy account for 70%. The temperature of the tube wall of a general mercury lamp can reach about 600°C; , ABS, PE, PS, PET and other printing materials with poor heat resistance and printing and thermal influence are greater, which often cause deformation and damage to the substrate. The service life of the high-pressure mercury lamp is short, generally at most 2000-3000 Hours, the amount of ultraviolet rays will be reduced by 15-20% when approaching the later stage, so the reflector should be cleaned regularly, and the equipment needs to be replaced and maintained frequently, which increases the cost of use; the ozone produced by the high-pressure mercury lamp will cause damage to the surrounding equipment. Corrosion, ozone itself has adverse effects on the human respiratory system, and high-pressure mercury lamps contain mercury, which is harmful to the environment. The European Union also has regulations to limit the scope of use of mercury lamps. Therefore, it is the general trend to develop and use new energy-saving and environmentally friendly curing light sources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of PVC coating cured by uv-led light source and preparation method thereof
  • A kind of PVC coating cured by uv-led light source and preparation method thereof
  • A kind of PVC coating cured by uv-led light source and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The invention will be further illustrated by the following non-limiting examples.

[0026] The present invention also provides a kind of preparation method of the PVC coating composition cured by UV-LED light source, comprises the following steps:

[0027] Step 1, under the condition of avoiding sunlight or ultraviolet light, mix polyurethane acrylate, hyperbranched acrylate oligomer, some monomers, and photoinitiator in sequence according to the ratio, and control the temperature of the mixed material during the stirring process When the temperature is less than 50°C, the stirring speed is 500-8000 rpm for 5 minutes;

[0028] Step 2: Add fillers and pigments according to the above ratio, fully disperse at a stirring speed of 800-1000 rpm, then add additives to disperse evenly, and finally add amine-modified acrylate oligomer and remaining monomers and stir at room temperature and adjust the viscosity. After uniform dispersion, the PVC coating cured by UV-LED light so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
Login to View More

Abstract

The invention aims to provide a PVC (polyvinyl chloride) coating cured by using a UV (ultraviolet)-LED (light-emitting diode) light source and a preparation method of the PVC coating. The coating is prepared from the following raw materials by weight percent: 40-50% of polyurethane acrylate, 5-15% of modified acrylate oligomer, 5-10% of hyperbranched acrylate oligomer, 30-40% of acrylate reactive diluent, 3-7% of photoinitiator, 0.2-0.4% of auxiliary and 0-20% of color filler. The PVC coating has the advantages that the coating can be fast cured under the UV-LED light source, and has good adhesive force on PVC. The problems of slow curing speed and poor surface dryness of a photocured PVC coating under the UV-LED light source are completely solved.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a PVC coating which can be cured by using a UV-LED light source and a preparation method thereof. Background technique [0002] Compared with general coatings, UV-curable coatings have the following advantages: ①The curing time is short, the speed is fast, and can be cured within a few seconds, and can be applied to occasions that require fast curing; Materials that are not suitable for heating such as plastics and materials with large heat capacity such as concrete and thick metal plates are very useful; ③ can be formulated into solvent-free products to reduce air pollution and benefit environmental protection; ④ save energy, and the efficiency of ultraviolet light sources is higher than that of ovens; ⑤ The curing process can be automated to improve the degree of automation in production, thereby improving production efficiency and economic benefits. [0003] Alth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/14C09D167/06C08J7/04C08L27/06
CPCC08J7/0427C08J2327/06C08J2475/14C08L2205/025C08L2205/035C09D175/14C08L75/14C08L67/06
Inventor 姚娜王俊权武瑞王晓蒙董月国赵建新李静雨张齐
Owner TIANJIN JIURI NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products