Method for producing multi-difference multi-functional polyester low elastic yarn

A technology of polyester low elastic yarn and a manufacturing method, which is applied in the field of textile fiber manufacturing, can solve the problems affecting the appearance quality of the fabric, the appearance is not ideal, the manufacturing process is complicated, etc., and achieves a good abnormal shrinkage appearance effect and excellent melt processing fluidity. , the effect of reducing the lattice packing density

Active Publication Date: 2017-02-15
ZHEJIANG SHENGYUAN CHEM FIBER
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the weakness of the cohesion force between the tows, the network-bonded fibers often have unsatisfactory appearance after shrinkage
In addition, due to mechanical reasons in the plying process, it is easy to cause unevenness of the tow, which affects the use of the subsequent process, and even ultimately affects the appearance quality of the fabric.
[0004] Chinese patent CN1403639 discloses a special-shaped self-curling polyester fiber, different shrinkage T400 fiber, etc., but these fibers belong to side-by-side bi-component fibers, and have the disadvantage of complicated manufacturing process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing multi-difference multi-functional polyester low elastic yarn
  • Method for producing multi-difference multi-functional polyester low elastic yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1: A kind of manufacture method of multi-different multifunctional polyester low stretch yarn, adopts following steps:

[0031] A) In parts by mass, 2 parts of organic calcium carbonate whiskers whose characteristic parameters are 3um in diameter and 20um in length, 3 parts of nanoscale diameter sepiolite fibers, 2 parts of 800 mesh mica powder, and 75 parts of ethylene glycol EG , 5 parts of 1,3-propanediol PDO, 5 parts of 1,4-butanediol BDO, 4 parts of p-hydroxybenzoic acid, and 0.3 parts of sodium germanate were mixed, and the mixed solution was stirred and ground in a ball mill at 70°C for 4 hours to obtain a A kind of enhanced compound alcohol solution, kept warm at 70°C for use;

[0032] B) According to the number of parts by mass, 2 parts of organic magnesium hydroxide whiskers with a characteristic parameter diameter of 5um and a length of 25um, 1 part of organic barium sulfate nanopowder, 8 parts of polyethylene glycol PEG with a molecular weight of ...

Embodiment 2

[0036] Embodiment 2: a kind of manufacture method of multi-different multifunctional polyester low elastic yarn, adopts following steps:

[0037] A) In parts by mass, 1.5 parts of organic calcium carbonate whiskers whose characteristic parameters are 1.7um in diameter and 12um in length, 2.5 parts of nanoscale diameter sepiolite fibers, 1.5 parts of 800 mesh mica powder, and 70 parts of ethylene glycol EG, 6.5 parts of 1,3-propanediol PDO, 6.5 parts of 1,4-butanediol BDO, 5 parts of p-hydroxybenzoic acid, and 0.2 parts of sodium germanate are mixed, and the mixed solution is stirred at 70 ° C for 3 hours in a closed ball mill for reaction to obtain An enhanced complex alcohol solution, kept at 70°C for use;

[0038] B) According to the number of parts by mass, 1.5 parts of organic magnesium hydroxide whiskers with a characteristic parameter diameter of 2.6um and a length of 17um, 0.7 parts of organic barium sulfate nanopowder, and 9 parts of polyethylene glycol PEG with a mole...

Embodiment 3

[0042] Embodiment 3: a kind of manufacture method of multi-different multifunctional polyester low elastic yarn, adopts following steps:

[0043] A) In parts by mass, 1 part of organic calcium carbonate whisker whose characteristic parameter diameter is 0.5um and length is 5um, 2 parts of nanoscale diameter sepiolite fiber, 1 part of 800 mesh mica powder, 65 parts of ethylene glycol EG, 8 parts of 1,3-propanediol PDO, 8 parts of 1,4-butanediol BDO, 6 parts of p-hydroxybenzoic acid and 0.1 part of sodium germanate are mixed, and the mixed solution is stirred and ground in a ball mill at 70 ° C for 2 hours to obtain An enhanced complex alcohol solution, kept at 70°C for use;

[0044] B) According to the number of parts by mass, 1 part of organic magnesium hydroxide whisker with a characteristic parameter diameter of 0.2um and a length of 10um, 0.5 part of organic barium sulfate nanopowder, 10 parts of polyethylene glycol PEG with a molecular weight of 15000, Mix 10 parts of 1,3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Sizeaaaaaaaaaa
Sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for producing multi-difference multi-functional polyester low elastic yarn. The method comprises 1) mixing calcium carbonate whisker, sepiolite fibers, mica powder, ethylene glycol, propylene glycol, butanediol, p-hydroxybenzoic acid and sodium germanate to obtain an enhanced composite alcoholic solution, 2) mixing magnesium hydroxide whisker, barium sulfate powder, polyethylene glycol, propylene glycol, a high temperature antioxidant 1098, ethylene glycol antimony and protonating agent phosphoric acid to obtain an enhanced composite promoter, 3) carrying out multielement copolycondensation on the enhanced composite multi-functional alcohol solution, the enhanced composite promoter, refined terephthalic acid and ethylene glycol to obtain an enhanced modified polyester, ejecting the melt of the enhanced modified polyester through antiparallelogram-like spinneret orifices, and preparing the multi-difference multi-functional polyester low elastic yarn through a specific cooling curing method and an elasticity improvement technology. The method is simple. The produced fibers are one-component different shrinkage fibers, which have different crystallinity, different orientation and different shrinkage performances, and the appearance and form of the fiber subjected to different shrinkage are good.

Description

technical field [0001] The invention relates to a method for manufacturing multi-different and multi-functional polyester low elastic yarns, belonging to the technical field of textile fiber manufacturing. Background technique [0002] At present, the different shrinkage fibers that are common in the market are mostly produced by using two or three strands of filaments with different shrinkage ratios for network plying; there are also parallel two-component spinning methods. [0003] Chinese patent 103484967A discloses a method for preparing copolyester melt ultra-high-speed direct spinning controllable multi-differential shrinkage composite fiber, Chinese patent 102140700A discloses a preparation method for double different shrinkage mixed fiber yarns, and Chinese patent 101962838A discloses The invention discloses a method for preparing polyester superfine different-shrinkage composite filaments, but these fibers belong to network ply different-shrinkage fibers. Due to th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92D01F1/10C08G63/64C08G63/66
CPCC08G63/64C08G63/66D01F1/10D01F6/92
Inventor 方千瑞吴金亮刘奇良闫科周志祥李丕疑封建沫
Owner ZHEJIANG SHENGYUAN CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com