Grinding paste for processing dendrite macroscopic examination samples and preparation method of grinding paste

A technology of low magnification inspection and inspection of samples, applied in the field of abrasive paste, can solve the problem of high production cost of surface roughness, and achieve the effects of bright surface of billet samples, simple production process and improved accuracy

Active Publication Date: 2016-12-07
SHANGHAI MEISHAN IRON & STEEL CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The object of the present invention is to provide a grinding paste for dendrite low-magnification inspection sample processing and its preparation method, so as to solve the problem that the existing grinding paste cannot meet the requirements of different steel dendrite low-magnification inspections at the same time. The surface roughness of the billet sample is Ra≤0.1 µm, high production cost technical problems, thereby improving the accuracy of continuous casting billet defect inspection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A grinding paste for dendritic low-magnification inspection sample processing, composed of W5 green silicon carbide grinding powder, 3# high temperature wear-resistant lithium base grease, grinding aid, the weight parts of each component are W5 green silicon carbide grinding 60 parts of powder, 25 parts of 3# high-temperature wear-resistant lithium base grease, 15 parts of grinding aid, and described grinding aid is common Chinese brand white toothpaste.

[0028] The preparation method of the grinding paste for processing the dendrite low magnification inspection sample comprises the following steps:

[0029] a. Accurately weigh each component according to the above parts by weight;

[0030] b. Mix the components uniformly at a temperature of 75°C;

[0031] c. Cool to 0°C to obtain the finished product.

Embodiment 2

[0033] A grinding paste for dendritic low-magnification inspection sample processing, consisting of W3.5 green silicon carbide grinding powder, 2# high temperature wear-resistant lithium-based grease, grinding aid, the weight of each component is W3.5 40 parts of green silicon carbide grinding powder, 35 parts of 2# high-temperature wear-resistant lithium base grease, 25 parts of grinding aid, and described grinding aid is ordinary Zhonghua brand white toothpaste.

[0034] The preparation method of the grinding paste for processing the dendrite low magnification inspection sample comprises the following steps:

[0035] a. Accurately weigh each component according to the above parts by weight;

[0036] b. Mix the components uniformly at a temperature of 70°C;

[0037] c. Cool to 0°C to obtain the finished product.

Embodiment 3

[0039] A grinding paste for dendritic low-magnification inspection sample processing, consisting of W3.5 green silicon carbide grinding powder, 2# high temperature wear-resistant lithium-based grease, grinding aid, the weight of each component is W3.5 35 parts of green silicon carbide grinding powder, 35 parts of 2# high-temperature wear-resistant lithium base grease, 30 parts of grinding aid, and described grinding aid is ordinary Zhonghua brand white toothpaste.

[0040] The preparation method of the grinding paste for processing the dendrite low magnification inspection sample comprises the following steps:

[0041] a. Accurately weigh each component according to the above parts by weight;

[0042] b. Mix the components uniformly at a temperature of 70°C;

[0043] c. Cool to 0°C to obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to grinding paste for processing dendrite macroscopic examination samples and a preparation method of the grinding paste, and solves the technical problems that conventional grinding paste cannot meet requirement that the surface roughness Ra of dendrite macroscopic examination billet samples of different steel kinds is smaller than or equal to 0.1[mu]m, and the production cost is high. The grinding paste for processing the dendrite macroscopic examination samples is prepared from 35-60 parts of green silicon carbide grinding powder, 25-35 parts of a lubricant and 15-35 parts of a grinding aid, wherein the lubricant is lithium lubricating grease, and the grinding aid is toothpaste. The grinding paste disclosed by the invention is used for performing polishing processing on the steel strand dendrite macroscopic examination samples.

Description

[0001] technical field [0002] The invention relates to the technical field of grinding paste, in particular to a grinding paste for dendritic low-magnification inspection sample processing and a preparation method thereof. [0003] Background technique [0004] Low-magnification inspection is the main means to judge the quality of continuous casting slabs. Iron and steel enterprises often use low-magnification inspection methods to detect internal quality defects after continuous casting slabs solidify. Commonly used low-magnification inspection methods include sulfur stamp inspection, hot acid corrosion, and cold acid corrosion. Corrosion, electrolytic corrosion and dendrite inspection; Compared with other low-magnification inspection methods, dendrite inspection can accurately display the internal defects of continuous casting slabs, and clearly display the solidification structure of continuous casting slabs. Proportionality shows that it does not expand or narrow the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09G1/02G01N1/32
Inventor 林学武张斌王长豪
Owner SHANGHAI MEISHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com