PVC (polyvinyl chloride) antistatic glove

An antistatic and antistatic agent technology, applied in the field of PVC antistatic gloves, can solve the problems of poor glove comfort, complex production process, interference with the processing process, etc., and achieve superior antistatic effect, good antistatic effect and simple production process. Effect

Active Publication Date: 2016-12-07
山东蓝帆新材料有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PVC material has high volume resistance and surface resistivity. This high resistance property will carry a large amount of static charge from other media during use, which will interfere with the processing process and affect the product due to discharge. health, or damage the performance of the product, or even cause serious accidents
The internal layer structure of the existing PVC antistatic gloves is an inner PVC film layer-antistatic spray layer-outer PVC film layer, or an antistatic layer is sprayed on the surface of PVC gloves. The production process is complicated or difficult to operate, and there is an antistatic effect. Poor, short duration, poor glove comfort, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC (polyvinyl chloride) antistatic glove
  • PVC (polyvinyl chloride) antistatic glove
  • PVC (polyvinyl chloride) antistatic glove

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] PVC antistatic gloves are made of the following raw materials in parts by weight:

[0028]

[0029] The production process includes the following steps:

[0030] (1) Primary batching: Mix DINCH, ATBC, epoxy fatty acid methyl ester and polyoxyethylene glyceryl ether and stir, then add PVC powder, CZ-F990, and 10 parts of D70 in turn for stirring to obtain primary batching;

[0031] (2) standing defoaming: the primary ingredients are standing defoaming;

[0032] (3) Secondary batching: add 15 parts of viscosity reducer to the material prepared in step (2), and stir evenly;

[0033] (4) Primary impregnation: filter the secondary ingredients prepared in step (3) and add them to the trough, preheat the hand mold to 70°C and then impregnate, the impregnation temperature is 50°C;

[0034] (5) Primary plasticization: put the impregnated hand mold in an oven and bake at 210°C for 6 minutes;

[0035] (6) Secondary impregnation: add water-based PU glue into softened water an...

Embodiment 2

[0043] PVC antistatic gloves are made of the following raw materials in parts by weight:

[0044]

[0045] The production process includes the following steps:

[0046] (1) Primary batching: Mix DINCH, ATBC, epoxy fatty acid methyl ester and polyoxyethylene glyceryl ether and stir, then add PVC powder, CZ-F990, and 10 parts of D70 in turn for stirring to obtain primary batching;

[0047] (2) standing defoaming: the primary ingredients are standing defoaming;

[0048] (3) Secondary batching: add 15 parts of viscosity reducer to the material prepared in step (2), and stir evenly;

[0049] (4) Primary impregnation: filter the secondary ingredients prepared in step (3) and add them to the trough, preheat the hand mold to 70°C and then impregnate, the impregnation temperature is 50°C;

[0050] (5) Primary plasticization: put the impregnated hand mold in an oven and bake at 210°C for 6 minutes;

[0051] (6) Secondary impregnation: add water-based PU glue into softened water an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a PVC (polyvinyl chloride) antistatic glove and belongs to the technical field of plastic gloves. The PVC antistatic glove is made from the following materials, by weight: 100 parts of PVC powder, 25-50 parts of DINCH, 20-40 parts of ATBC (acetyl tributyl citrate), 20-30 parts of epoxidized fatty acid methyl ester, 3-10 parts of an antistatic agent, 0.5-1.8 parts of liquid calcium-zinc stabilizer, 25-30 parts of a viscosity reducer, and 0.5-0.7 part of waterborne PU (polyurethane) rubber. The PVC antistatic glove is good in antistatic effect, durable, comfortable to wear and low in cost, the polymer antistatic agent that is used has excellent antistatic effect, is friendly to transparency of the glove and initial color performance of PVC and can also avoid the problems such as affected normal wearing due to glove adhesion caused by the adding of other antistatic agents to the formula, and a production process of the glove is simple and easy to perform.

Description

technical field [0001] The invention relates to a PVC antistatic glove, which belongs to the technical field of plastic gloves. Background technique [0002] In recent years, PVC gloves have the characteristics of relatively simple production process, low material cost, convenient wearing, good air permeability, comfortable hand feeling, acid and alkali resistance, good isolation effect, no skin allergies, and low price, making PVC gloves The rapid development, widely used in medical, electronics, food processing, scientific research, fast food and other fields. However, PVC material has high volume resistance and surface resistivity. This high resistance property will carry a large amount of static charge from other media during use, which will interfere with the processing process and affect the product due to discharge. hygiene, or damage the performance of the product, or even cause serious accidents. The internal layer structure of the existing PVC antistatic gloves i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L71/02C08L75/04C08K5/098
CPCC08K2201/014C08L27/06C08L2201/04C08L2205/03C08L71/02C08L75/04C08K5/098C08K5/1515
Inventor 王术滨相刚王德玉
Owner 山东蓝帆新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com