High-temperature-oil-resistant thermoplastic elastomer and preparation method thereof

A plastic-elastic, high-temperature-resistant technology, applied in the field of thermoplastic elastomers, can solve the problems of unsustainable high-temperature oil resistance and inability to recycle, achieve excellent mechanics and high-temperature oil resistance, maintain mechanical properties, and good mechanical properties. Effect

Active Publication Date: 2016-03-23
HUBEI YANGTIAN PLASTIC PROD CO LTD
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the problems existing in the prior art that high temperature resistant oil cannot be sustained and cannot be recycled, and provide a sustainable high temperature resistant oil, recyclable high temperature resistant oil thermoplastic elastomer and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] A method for preparing the high-temperature oil-resistant thermoplastic elastomer, including the preparation of toughening masterbatch, oil-resistant masterbatch and elastomer, the preparation of the elastomer is located in the preparation of toughening masterbatch, oil-resistant masterbatch after the preparation of the material;

[0029] The preparation of the toughening masterbatch refers to: firstly add linear low density polyethylene, methyl vinyl silicone rubber, toughening agent, radiation crosslinking auxiliary agent, and reinforcing agent into the internal mixer according to the required proportion. After refining, it is discharged into a single-screw extruder for extrusion, drawing, winding and receipt to obtain material strands, and then the material strands are irradiated by an electron accelerator and crushed into powders with a fineness below 60 mesh. , the toughened masterbatch is obtained;

[0030] The preparation of the oil-resistant masterbatch refers ...

Embodiment 1

[0050] A high temperature resistant oil thermoplastic elastomer, its raw material composition and weight ratio are: toughening masterbatch 8, oil resistant masterbatch 20, polypropylene powder 5, nitrile rubber powder 40, wherein the toughening masterbatch The raw material composition and weight ratio are: linear low density polyethylene 10, methyl vinyl silicone rubber 30, toughening agent 30, radiation crosslinking auxiliary agent 1, reinforcing agent 10, the raw material composition of the oil-resistant masterbatch And the weight ratio is: nitrile silicone rubber 80, lubricant 3, reinforcing agent 10, filler 10, radiation crosslinking auxiliary agent 1, heat-resistant auxiliary agent 3, and the polypropylene powder is polypropylene resin. The toughening agent is acrylate rubber, the radiation crosslinking auxiliary agent is triallyl isocyanurate, the reinforcing agent is white carbon black, and the lubricant is methyl phenyl silicone oil. The filler is magnesium hydroxide, ...

Embodiment 2

[0056] Step is with embodiment 1, and difference is:

[0057] The raw material composition and weight ratio of the high-temperature oil-resistant thermoplastic elastomer are: toughening masterbatch 10, oil-resistant masterbatch 30, polypropylene powder 8, nitrile rubber powder 50, wherein the toughening masterbatch The raw material composition and weight ratio are: linear low density polyethylene 20, methyl vinyl silicone rubber 40, toughening agent 40, radiation crosslinking auxiliary agent 2, reinforcing agent 15, the raw material composition of the oil-resistant masterbatch And the weight ratio is: nitrile silicone rubber 100, lubricant 5, reinforcing agent 20, filler 20, radiation crosslinking auxiliary agent 2, heat-resistant auxiliary agent 5;

[0058] In the preparation of the toughened masterbatch, the banburying temperature is 95°C, the banburying time is 8min, the irradiation dose is 16 Mrad, and the crushing temperature is minus 65°C;

[0059] In the preparation of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-temperature-oil-resistant thermoplastic elastomer. The high-temperature-oil-resistant thermoplastic elastomer is prepared from the following raw material components in parts by weight: 8-10 parts of toughening master batch, 20-30 parts of oil-resistant master batch, 5-8 parts of polypropylene powder and 40-50 parts of acrylonitrile-butadiene rubber powder, wherein the toughening master batch is prepared from the following raw material components in parts by weight: 10-20 parts of linear low density polyethylene, 30-40 parts of methyl vinyl silicone rubber, 30-40 parts of a toughening agent, 1-2 parts of a radiation crosslinking agent and 10-15 parts of a reinforcing agent; and the oil-resistant master batch is prepared from the following raw material components in parts by weight: 80-100 parts of nitrile silicone rubber, 3-5 parts of a lubricating agent, 10-20 parts of a reinforcing agent, 10-20 parts of a filling agent, 1-2 parts of a radiation crosslinking agent and 3-5 parts of a thermal controller. A preparation method of the high-temperature-oil-resistant thermoplastic elastomer comprises the following steps: firstly respectively preparing the toughening master batch and the oil-resistant master batch, then mixing the polypropylene powder, the acrylonitrile-butadiene rubber powder, the toughening master batch and the oil-resistant master batch in required ratio, extruding, and granulating, so that the high-temperature-oil-resistant thermoplastic elastomer is obtained. The high-temperature-oil-resistant thermoplastic elastomer not only can continuously resist to high-temperature oil but also can be recycled.

Description

technical field [0001] The invention relates to a thermoplastic elastomer, specifically a high-temperature oil-resistant thermoplastic elastomer and a preparation method thereof, which are mainly used for parts under the hood of automobiles, injection molded parts of machine tools, oil-resistant materials for oil fields, oil-resistant cable materials for locomotives, and motors Winding lead wires (Grade F), photovoltaic cable materials, automotive air intake pipes, turbocharger hoses, intercoolers, crankcase ventilation parts, oil seals, sealing rings and other parts that are in direct contact with oil and solvents. Background technique [0002] At present, the parts under the hood of automobiles, injection molded parts of machine tools, oil-resistant materials for oil fields, oil-resistant cable materials for locomotives, flexible wires for motor winding leads (F grade), photovoltaic cable materials, etc. all require materials to be resistant to high temperature oil, solvent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L23/08C08L83/04C08L83/07C08L23/12C08L33/04C08K13/02C08K3/36C08K3/22
CPCC08J3/226C08J2309/02C08J2423/08C08J2483/04C08J2483/07C08L9/02C08L2201/08C08L2205/035C08L23/0815C08L83/04C08L23/12C08L33/04C08K13/02C08K3/36C08K2003/2224C08K2003/2272
Inventor 胡承鹏
Owner HUBEI YANGTIAN PLASTIC PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap