Flame-retardant and smoke-inhibition type non-cured rubber asphalt waterproof coating material

A technology of asphalt waterproof coating and non-curing rubber, which is applied in the direction of asphalt coating, recycled rubber coating, fireproof coating, etc., and can solve the problems of releasing a large amount, affecting human health, melting at high temperature, etc.

Inactive Publication Date: 2016-01-13
天长市金牛防水防腐材料有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the non-curing rubber asphalt waterproof coating needs to be melted at high temperature before construction. During the high-temperature melting process, the non-curing rubber asphalt waterproof coating will release a lot of smoke
These smog contain a large amount of substances harmful to the human body, which affect people's health and damage the surrounding environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant and smoke-inhibition type non-cured rubber asphalt waterproof coating material
  • Flame-retardant and smoke-inhibition type non-cured rubber asphalt waterproof coating material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A flame-retardant and smoke-suppressing non-curing rubber asphalt waterproof coating, its raw materials include: 25 parts of No. 90 road asphalt, styrene-butadiene- 7 parts of styrene block copolymer, 12 parts of octane oil, 7 parts of paraffin oil, 16 parts of 40 mesh reclaimed rubber powder, 28 parts of 200 mesh talcum powder, 5 parts of 100 mesh limestone powder, 5 parts of rosin resin, C5 petroleum resin 3 parts, 2 parts of paraffin, 2 parts of p-diphenylamine, 6220.2 parts of light stabilizer, 0.7 parts of 2-hydroxy-4-methoxybenzophenone, 1 part of PP-g-MAH, 0.8 parts of dicumyl peroxide , 0.2 parts of stearic acid, 0.2 parts of zinc oxide, 1 part of 3-aminopropyltriethoxysilane, 4 parts of microencapsulated red phosphorus, 3 parts of ammonium polyphosphate, 3 parts of modified smoke suppressant, coumarone 0.8 parts of resin;

[0022] Among them, the preparation method of the modified smoke suppressant is: adding 1000 mesh expandable graphite into isopropanol, hea...

Embodiment 2

[0024] A flame-retardant and smoke-suppressing non-curing rubber asphalt waterproof coating, its raw materials include: 30 parts of No. 90 road asphalt, styrene-butadiene- 3 parts of styrene block copolymer, 16 parts of octane oil, 4 parts of paraffin oil, 10 parts of 70 mesh reclaimed rubber powder, 22 parts of 300 mesh talcum powder, 3 parts of 200 mesh limestone powder, 8 parts of rosin resin, C5 petroleum resin 1 part, 4 parts of paraffin, 1 part of p-diphenylamine, 6220.6 parts of light stabilizer, 0.4 part of 2-hydroxy-4-methoxybenzophenone, 2 parts of PP-g-MAH, 0.4 part of dicumyl peroxide , 0.4 parts of stearic acid, 0.1 parts of zinc oxide, 2 parts of 3-aminopropyltriethoxysilane, 2 parts of microencapsulated red phosphorus, 5 parts of ammonium polyphosphate, 1 part of modified smoke suppressant, coumarone 1.2 parts of resin;

[0025] Among them, the preparation method of the modified smoke suppressant is: adding 1200 mesh expandable graphite to isopropanol, heating ...

Embodiment 3

[0027]A flame-retardant and smoke-suppressing non-curing rubber asphalt waterproof coating, its raw materials include: 29 parts of No. 90 road asphalt, styrene-butadiene-butadiene with a block ratio of styrene and butadiene of 32:68 4 parts of styrene block copolymer, 15 parts of octane oil, 5 parts of paraffin oil, 12 parts of 65 mesh reclaimed rubber powder, 24 parts of 270 mesh talcum powder, 3.5 parts of 180 mesh limestone powder, 7 parts of rosin resin, C5 petroleum resin 1.5 parts, 3.5 parts of paraffin, 1.3 parts of p-diphenylamine, 6220.5 parts of light stabilizer, 0.5 parts of 2-hydroxy-4-methoxybenzophenone, 1.8 parts of PP-g-MAH, dicumyl peroxide 0.5 parts, 0.35 parts of stearic acid, 0.12 parts of zinc oxide, 1.8 parts of 3-aminopropyltriethoxysilane, 2.5 parts of microencapsulated red phosphorus, 4.5 parts of ammonium polyphosphate, 1.5 parts of modified smoke suppressant, ancient Malone resin 1.1 parts;

[0028] Among them, the preparation method of the modified...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a flame-retardant and smoke-inhibition type non-cured rubber asphalt waterproof coating material, wherein the raw materials comprise, by weight, 25-30 parts of asphalt, 3-7 parts of a styrene-butadiene-styrene block copolymer, 12-16 parts of octane oil, 4-7 parts of paraffin oil, 10-16 parts of recycled rubber powder, 22-28 parts of talc powder, 3-5 parts of limestone powder, 5-8 parts of a rosin resin, 1-3 parts of a C5 petroleum resin, 2-4 parts of paraffin, 1-2 parts of p-phenylenediamine, 0.2-0.6 part of a light stabilizer 622, 0.4-0.7 part of 2-hydroxy-4-methoxy benzophenone, 1-2 parts of PP-g-MAH, 0.4-0.8 part of dicumyl peroxide, 0.2-0.4 part of stearic acid, 0.1-0.2 part of zinc oxide, 1-2 parts of 3-aminopropyl triethoxysilane, 5-9 parts of a flame retardant agent, 1-3 parts of a modified smoke suppressant, and 0.8-1.2 parts of a coumarone resin. The flame-retardant and smoke-inhibition type non-cured rubber asphalt waterproof coating material of the present invention has characteristics of good waterproof performance, good flame retardant performance, and good smoke suppression performance.

Description

technical field [0001] The invention relates to the technical field of waterproof coatings, in particular to a flame-retardant and smoke-suppressing non-curing rubber asphalt waterproof coating. Background technique [0002] The non-curing rubber asphalt waterproof coating solves the problems of waterproof layer fracture, bending fatigue damage or premature aging of the waterproof layer caused by the cracking stress of the base layer transmitted to the waterproof layer; at the same time, due to the viscosity of the coating , so that it can well seal the capillary pores and cracks of the base, can adapt to the complex construction work surface, and can automatically find the leaking part, repair the damaged waterproof layer, solve the problem of water channeling in the waterproof layer, and make the waterproof reliability be greatly improved. [0003] However, the non-curing rubber asphalt waterproof coating needs to be melted at high temperature before construction. During ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D195/00C09D153/02C09D117/00C09D191/06C09D193/04C09D157/02C09D151/06C09D5/18C09D7/12
Inventor 张利奎
Owner 天长市金牛防水防腐材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com