A kind of ultrasoft ultrafine polyester fiber and preparation method thereof

An ultra-fine polyester fiber and ultra-soft technology, applied in fiber type, fiber treatment, dyeing method, etc., can solve the problems of poor tow cohesion, difficulty in oiling, and difficulty in evenly attaching oil agents, etc., to reduce surface tension, Improved smoothness and soft luster

Active Publication Date: 2017-11-03
江苏轩达高分子材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The production of ultra-soft and ultra-fine polyester filament polyester filaments has many single filaments, large specific surface area, and is not easy to apply oil. head

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultrasoft ultrafine polyester fiber and preparation method thereof
  • A kind of ultrasoft ultrafine polyester fiber and preparation method thereof
  • A kind of ultrasoft ultrafine polyester fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A preparation method of super soft and ultra-fine polyester fiber. Firstly, an oiling agent is prepared. The specific preparation steps are: blending the initiator butanol and strong alkali potassium hydroxide, and then heating to 105°C, and then adding Mix evenly ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl]ethylene oxide and propylene oxide, the amount of butanol is ethylene oxide, [(1, 1,2,2-Tetrafluoroethoxy)methyl]ethylene oxide and propylene oxide are 1‰ of the total mass, and the amount of strong alkali potassium hydroxide is ethylene oxide, [(1,1,2, 2-Tetrafluoroethoxy) methyl] 1‰ of the total mass of ethylene oxide and propylene oxide, ethylene oxide, [(1,1,2,2-tetrafluoroethoxy) methyl] ring The molar ratio of ethylene oxide and propylene oxide is 10:1:20, and the polymerization reaction is carried out under a protective atmosphere of nitrogen. The reaction pressure is 0.4MPa and the relative molecular weight is 1000, and then fluorine-containing polyethe...

Embodiment 2

[0068] A preparation method of super soft and ultra-fine polyester fiber. Firstly, an oiling agent is prepared. The specific steps are: blending the starter butanol and strong alkali sodium hydroxide, then heating to 125°C, then adding and mixing uniformly The amount of ethylene oxide, [(1,1,2,2-tetrafluoroethoxy) methyl] ethylene oxide and propylene oxide, the amount of butanol is ethylene oxide, [(1,1, 2,2-Tetrafluoroethoxy) methyl] ethylene oxide and propylene oxide total mass 5‰, the amount of strong alkali sodium hydroxide is ethylene oxide, [(1,1,2,2- Tetrafluoroethoxy) methyl] ethylene oxide and propylene oxide total mass 5‰, ethylene oxide, [(1,1,2,2-tetrafluoroethoxy) methyl] ethylene oxide The molar ratio of alkane and propylene oxide is 20:3:30. The polymerization reaction is carried out under an inert gas atmosphere under a protective atmosphere. The reaction pressure is 0.5MPa and the relative molecular weight is 4000. After that, neutralization, adsorption and vac...

Embodiment 3

[0082] A preparation method of super soft and ultra-fine polyester fiber. Firstly, an oiling agent is prepared. The specific steps are: blending the initiator butanol and strong alkali sodium hydroxide, then heating to 115°C, and then adding and mixing uniformly The amount of ethylene oxide, [(1,1,2,2-tetrafluoroethoxy) methyl] ethylene oxide and propylene oxide, the amount of butanol is ethylene oxide, [(1,1, 2,2-Tetrafluoroethoxy) methyl] 2‰ of the total mass of ethylene oxide and propylene oxide, the amount of strong alkali sodium hydroxide is ethylene oxide, [(1,1,2,2- Tetrafluoroethoxy) methyl] ethylene oxide and propylene oxide 1.5‰ of the total mass, ethylene oxide, [(1,1,2,2-tetrafluoroethoxy) methyl] ethylene oxide The molar ratio of alkane and propylene oxide is 12:1:30, and the polymerization reaction is carried out under an inert gas atmosphere as a protective atmosphere. The reaction pressure is 0.8MPa, and after reaching a relative molecular weight of 3000, neutra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a kind of ultra-soft and ultra-fine polyester fiber and its preparation method. The super-soft and ultra-fine polyester fiber is mainly prepared by melt-spinning polyester through spinneret holes, oiling agent and high-speed winding; the above The oil agent of the oil agent includes at least fluorine-containing polyether, and the quality of the fluorine-containing polyether ≥ 45% of the quality of the oil agent; the fluorine-containing polyether is ethylene oxide, [(1,1,2,2 ‑Tetrafluoroethoxy) methyl] random copolymer of oxirane and propylene oxide, its structural formula is: the preparation method of the present invention is that polyester is measured, extruded, cooled, oiled, stretched , heat setting and high-speed winding to produce ultra-soft and ultra-fine polyester fibers. The ultra-soft and ultra-fine polyester fiber of the present invention, because its monofilament fineness is very fine, its fabric has the advantages of particularly soft and delicate hand feeling, soft luster, comfortable and breathable, easy to care and good texture of appearance, and has been increasingly obtained. users' favor.

Description

Technical field [0001] The invention relates to a super soft and super fine polyester fiber and a preparation method thereof. Background technique [0002] Since the advent of polyethylene terephthalate (PET) fiber, it has developed rapidly due to its excellent properties, and its output has become the world's top synthetic fiber. Polyester fiber has a series of excellent properties such as high breaking strength and elastic modulus, moderate resilience, excellent heat setting, good heat and light resistance, acid and alkali resistance and corrosion resistance, and the fabric has the advantages of wrinkle resistance and good stiffness, so , Polyester fiber is widely used in clothing, home textiles and other fields. [0003] With the rapid expansion of polyester production capacity and changes in the international situation, people have higher requirements for the comfort, functionality, diversification and safety of clothing. Polyester 22dtex / 48f, 22dtex / 72f, 33dtex / 72f and other ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F11/08D01D13/00D01D5/08D01D5/096D06M15/53D06M13/02D06M13/292D06M13/256C08G65/22D06P1/16D06P3/54D06M101/32
Inventor 印成韦开顺朱冬妹
Owner 江苏轩达高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap