Alkali-resistant and corrosion-resistant aluminum alloy surface composite coating and its process

A technology of aluminum alloy surface and composite coating, applied in the direction of surface reaction electrolytic coating, coating, metal layered products, etc., can solve the problems of parts such as loss of light and color, achieve strong alkali resistance and corrosion resistance, excellent Effect of corrosion resistance and dense structure

Active Publication Date: 2018-10-16
NINGBO MINTH AUTOMOTIVE PARTS RES&DEV CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in order to maintain the durability of the decoration, the current car manufacturers have higher and higher requirements for the corrosion resistance of the surface protection layer of aluminum alloy parts, especially the widespread use of strong alkaline car washes, because this traditional anode Oxidation coatings are difficult to resist the erosion of strong alkaline (pH value > 13) solutions, which will cause the parts to lose light and color. Performance and competitiveness of related auto parts products in the market research and development of this process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alkali-resistant and corrosion-resistant aluminum alloy surface composite coating and its process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The following are specific embodiments of the present invention and in conjunction with the accompanying drawings, the technical solutions of the present invention are further described, but the present invention is not limited to these embodiments.

[0019] In the figure, substrate 1; anodized film layer 2; organosilane coating 3.

[0020] Such as figure 1 As shown, the alkali-resistant and corrosion-resistant aluminum alloy surface composite coating is used on automobile exterior parts, including aluminum or aluminum alloy substrate 1 and anodized film layer 2 attached to the outside of aluminum or aluminum alloy substrate 1, anodized film layer 2. An organosilane coating 3 is attached to the outside, and the thickness of the additional organosilane coating 3 is 1 μm to 5 μm. Preferably, the thickness of the organosilane coating 3 is 3 μm to 5 μm, and the anodic oxidation film layer 2 is a natural color layer, or the A colored layer is added on the oxide film layer 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of metal surface treatment, and provides an alkali-resistant and corrosion-resistant aluminum alloy surface composite coating and its process, including an aluminum or aluminum alloy substrate and an anodized film layer attached to the aluminum or aluminum alloy substrate, an anodized film There is an organosilane coating attached to the outside of the layer. The organosilane coating is a composite layer composed of epoxy-modified silicone resin and methyl methacrylate. After the surface layer is flash-dried, it is cured at 180°C for 20-25 minutes, and it is firmly attached to the anodized surface, blocking the penetration of corrosive or alkaline substances into the inner oxide film and aluminum matrix. The aluminum treated by this process Alloy products have strong alkali resistance and corrosion resistance, high temperature resistance can be increased to 180 ° C without cracking, and can meet the performance standards of car manufacturers without changing the original appearance requirements.

Description

technical field [0001] The invention belongs to the technical field of metal surface treatment, and relates to an alkali-resistant and corrosion-resistant aluminum alloy surface composite coating and a process. Background technique [0002] At present, the interior and exterior areas of many cars are equipped with decorative parts made of aluminum plates or aluminum profiles that show the true color of the metal. The surface protection is mainly to form a layer of porous aluminum oxide film on the surface of aluminum or aluminum alloy through anodic oxidation. It is achieved by sealing the pores of the membrane layer by a certain chemical method. However, in order to maintain the durability of the decoration, the current car manufacturers have higher and higher requirements for the corrosion resistance of the surface protection layer of aluminum alloy parts, especially the widespread use of strong alkaline car washes, because this traditional anode Oxidation coatings are di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25D11/24B32B15/04B32B9/04B32B27/38
Inventor 于震宇胡磊
Owner NINGBO MINTH AUTOMOTIVE PARTS RES&DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More