Stainless steel/silicon carbide ceramic-based composite material and preparation method thereof

A technology of silicon carbide ceramic matrix and composite materials, which is applied in the field of ceramic production, can solve the problems of limiting the application of silicon carbide ceramics, brittleness, and insufficient toughness, and achieve the effects of short cycle, improved sintering performance, and lower sintering temperature

Inactive Publication Date: 2015-05-27
ANHUI HEHAN OPTOELECTRONICS TECH
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, silicon carbide ceramics still have the disadvantages of brittleness and insufficient toughness, which limit the application of silicon carbide ceramics in aerospace, nuclear industry, large petrochemical and other fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] specific implementation plan

[0013] The present invention will be described in detail below through specific examples.

[0014] A stainless steel / silicon carbide ceramic matrix composite material and its preparation method, which is made of the following raw materials in parts by weight (kg): silicon carbide 70, stainless steel powder 10, titanium powder 9, starch 4, fly ash 3, titanate Coupling agent 2, absolute ethanol 15, high wear-resistant carbon black 4, calcium stearate 2, liquid paraffin 2, sintering aid 3, deionized water 95;

[0015] The sintering aid is made of the following raw materials in parts by weight (kg): aluminum oxide 5, yttrium oxide 2, ammonium chloride 2, iridium nitrate 6, carbon nanoparticles 5, clay powder 4, dimethyl silicone oil 2, Liquid paraffin 3, silane coupling agent KH-5501, artificial diamond powder 3, vinyl acetate resin 2, tricresyl phosphate 1, purified water 5; the preparation method is to combine aluminum oxide, yttrium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Elastic modulusaaaaaaaaaa
Flexural strengthaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a stainless steel / silicon carbide ceramic-based composite material and a preparation method thereof. The stainless steel / silicon carbide ceramic-based composite material is characterized by being prepared from the following raw materials in parts by weight: 60-70 parts of silicon carbide, 9-12 parts of stainless steel powder, 7-9 parts of titanium powder, 2-4 parts of starch, 3-5 parts of coal ash, 1-2 parts of titanate coupling agent; 10-15 parts of absolute ethyl alcohol, 3-4 parts of highly wearable carbon black, 1-2 parts of calcium stearate, 1-3 parts of liquid paraffin, 2-4 parts of sintering aid and 80-100 parts of deionized water; according to the stainless steel / silicon carbide ceramic-based composite material, the added stainless steel powder and the titanium powder are capable of improving the high temperature resistance, the corrosion resistance, the strength and the toughness of the silicon carbide ceramics, increasing the relative density of the material, improving the sintering performance and expanding the application range of the ceramics; and the method has the advantages of easily available raw materials, short period, reduction of the sintering temperatures, reduction of the cost, and conservation of resources.

Description

technical field [0001] The invention relates to a stainless steel / silicon carbide ceramic matrix composite material and a preparation method thereof, belonging to the technical field of ceramic production. Background technique [0002] Silicon carbide ceramics have the characteristics of high strength, high hardness, wear resistance, heat resistance, corrosion resistance to almost all chemicals, etc., and also have superior high temperature mechanical, thermal properties, radiation resistance and oxidation resistance. However, silicon carbide ceramics still have the disadvantages of brittleness and insufficient toughness, which limit the application of silicon carbide ceramics in aerospace, nuclear industry, large-scale petrochemical and other fields. Therefore, composite ceramic matrix materials are an effective way to improve the performance of silicon carbide ceramics. The stainless steel powder and titanium powder added in the invention improve the high temperature, co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C29/02C22C1/05
CPCC22C29/065C22C1/051
Inventor 夏云
Owner ANHUI HEHAN OPTOELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com