Artificial brushed nickel appearance and anti-tarnish surface treatment method for metal base material

A metal substrate and surface treatment technology, which is applied in the direction of metal material coating process, pretreatment surface, and surface coating liquid device, etc., can solve problems such as darkening, achieve simple process, low cost, and improve anti-corrosion performance Effect

Active Publication Date: 2015-05-06
NINGBO RUNNER INDAL CORP
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, among the commonly used surface treatment methods for steel, there is the method of adopting PVD vacuum coating. Chinese patent CN101691653A discloses a process for surface treatment of stainless steel plates, which includes steps in turn: Kaiping preparation, grinding and polishing, cleaning, drying, inspection, PVD vacuum coating and film packaging can effectively improve the anti-corrosion performance of the surface of stainless steel sheets; however, the treatment of this process on the surface of cold-rolled steel materials cannot solve the problem of darkening after coating curing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1: A manufacturing method of a metal decorative panel assembly:

[0037] Including the following steps:

[0038] 1) Automatic mechanical oil grinding, polishing, and wire drawing of cold-rolled steel coils;

[0039] 2) The wire-drawn steel strip is covered with a layer of protective film to prevent the steel strip from rusting;

[0040] 3) According to the size of the component, the steel strip vermicelli is stamped and formed into a workpiece;

[0041] 4) Remove the protective film, carry out vacuum ultrasonic hydrocarbon removal of film residue glue on the machine, ultrasonic hydrocarbon degreasing and cleaning, and vacuum microwave drying;

[0042] 5) Transfer to a vacuum coating machine for physical vapor deposition of metal nickel-chromium alloy / zirconium metal, ceramic film zirconium nitride or nickel-chromium alloy metal layer; Make the vacuum degree reach 8.0*10 -3 After Pa, close the throttle valve, start to pass in 210sccm argon gas, open the b...

Embodiment 2

[0044] Embodiment 2: A method of making a metal decorative panel assembly:

[0045] Including the following steps:

[0046] 1) Automatic mechanical oil grinding, polishing, and wire drawing of cold-rolled steel coils;

[0047] 2) The wire-drawn steel strip is covered with a layer of protective film to prevent the steel strip from rusting;

[0048] 3) According to the size of the component, the steel strip vermicelli is stamped and formed into a workpiece;

[0049] 4) Remove the protective film, carry out vacuum ultrasonic hydrocarbon removal of film residue glue on the machine, ultrasonic hydrocarbon degreasing and cleaning, and vacuum microwave drying;

[0050]5) Transfer to a vacuum coating machine for physical vapor deposition of metal nickel-chromium alloy / zirconium metal, ceramic film zirconium nitride or nickel-chromium alloy metal layer; Make the vacuum degree reach 8.0*10 -3 After Pa, close the throttle valve, start to feed 220sccm argon gas, open the bias voltag...

Embodiment 3

[0052] Embodiment 3: A method for manufacturing a metal decorative panel assembly:

[0053] Including the following steps:

[0054] 1) Automatic mechanical oil grinding, polishing, and wire drawing of cold-rolled steel coils;

[0055] 2) The wire-drawn steel strip is covered with a layer of protective film to prevent the steel strip from rusting;

[0056] 3) According to the size of the component, the steel strip vermicelli is stamped and formed into a workpiece;

[0057] 4) Remove the protective film, carry out vacuum ultrasonic hydrocarbon removal of film residue glue on the machine, ultrasonic hydrocarbon degreasing and cleaning, and vacuum microwave drying;

[0058] 5) Transfer to a vacuum coating machine for physical vapor deposition of metal nickel-chromium alloy / zirconium metal, ceramic film zirconium nitride or nickel-chromium alloy metal layer; Make the vacuum degree reach 8.0*10 -3 After Pa, close the throttle valve, start to feed 230sccm argon gas, open the bi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
mechanical propertiesaaaaaaaaaa
Login to View More

Abstract

The invention provides an artificial brushed nickel appearance and anti-tarnish surface treatment method for a metal base material and a metal decorative assembly obtained by the method. The method provided by the invention comprises the following steps: polishing and drawing the metal base material by virtue of an abrasive tape, adhering a layer of protective film to effectively prevent the drawn metal base material surface from rusting; removing the protective film, removing glue and oil by a vacuum ultrasonic hydrocarbon solvent; carrying out vacuum microwave drying, so that the metal base material is not injured, and no three wastes are discharged; sequentially applying a physical gas-phase deposition layer, an ion glow activation layer, a non-reacting deposition layer and a reacting deposition layer, effectively improving the adhesive force and the appearance chromatism between the coating and the metal base material; and finally, spraying transparent powder. The appearance of the sprayed metal decorative assembly does not change color due to high-temperature baking, so that the antiseptic property, the anti-tarnish property and other properties of the metal base material can be effectively improved.

Description

technical field [0001] The invention relates to a surface treatment method for a metal base material, in particular to a surface treatment method for imitating the brushed nickel appearance and preventing discoloration on the metal base material. Background technique [0002] At present, iron-based accessories are mechanically polished and wire-drawn to form wire-drawn lines. After cleaning, physical vapor deposition (PVD) vacuum coating is performed. The coating is only micron-sized. darken. [0003] The problem of discoloration is also easy to appear in the decorative imitation brushed nickel green coating on the iron substrate, and it cannot be solved from the coating process. No matter whether it is water-based polishing and then mechanical drawing, or dry polishing and then drawing, it will be cured at the coating temperature. Finally, iron substrates are very easy to darken. [0004] In order to overcome the above problems, one of the feasible methods is to directly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/16C23C14/06B05D7/14B05D3/02
Inventor 牛虎东王应泉王飞明松
Owner NINGBO RUNNER INDAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com