Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method and application of high temperature resistant solvent-type acrylate pressure-sensitive adhesive

A pressure-sensitive adhesive and acrylate technology, applied in the field of pressure-sensitive adhesives, can solve the problem of high cost, achieve low cost, increase the scope of application, and improve high temperature resistance and weather resistance.

Active Publication Date: 2016-09-21
新丰杰力电工材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent 201010521734 is mainly to modify acrylate with silicone resin to improve its temperature resistance, and its cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A high-solvent-resistant acrylate pressure-sensitive adhesive, which is polymerized by the following components according to their weight ratio:

[0049] Isooctyl acrylate 200

[0050] Butyl acrylate 70

[0051] Acrylic 5

[0052] Hydroxyethyl Acrylate 5

[0053] Vinyl acetate 12

[0054] Isobornyl Acrylate 25

[0055] Azoazobisisobutyronitrile 1.6

[0056] N-methylolacrylamide 0.5

[0057] Ethyl acetate 600

[0058] The preparation method of the above-mentioned high-temperature-resistant solvent-type acrylate pressure-sensitive adhesive, its preparation steps are:

[0059] The first step: select 400% ethyl acetate according to the above weight ratio, and dissolve 1 azoazobisisobutyronitrile in it, and add 200% isooctyl acrylate, 70% butyl acrylate, 25% isobornyl acrylate and 12% vinyl acetate to prepare mixed monomer solution A; dissolve 0.5 N-methylol acrylamide, 5% acrylic acid, and 5% hydroxyethyl acrylate with 100% ethyl acetate to prepare mixed monomer solut...

Embodiment 2

[0066] A high-solvent-resistant acrylate pressure-sensitive adhesive, which is polymerized by the following components according to their weight ratio:

[0067] Isooctyl acrylate 150

[0068] Butyl acrylate 90

[0069] Acrylic 5

[0070] Hydroxyethyl Acrylate 5

[0071] Vinyl acetate 12

[0072] Isobornyl Acrylate 18

[0073] Azoazobisisobutyronitrile 1.6

[0074] N-methylolacrylamide 0.7

[0075] Ethyl acetate 500

[0076] The preparation method of the above-mentioned high-temperature-resistant solvent-type acrylate pressure-sensitive adhesive, its preparation steps are as follows:

[0077] The first step: according to the above weight ratio, select 300% ethyl acetate to dissolve 1 azoazobisisobutyronitrile, and add 150% isooctyl acrylate, 90% butyl acrylate, 18% isobornyl acrylate and 12 parts 100% vinyl acetate to prepare mixed monomer solution A; then dissolve 0.7% N-methylolacrylamide, 5% acrylic acid, and 5% hydroxyethyl acrylate with 100% ethyl acetate to prepar...

Embodiment 3

[0084] 1. A high-solvent-resistant acrylate pressure-sensitive adhesive, which is polymerized by the following components according to their weight ratio:

[0085] Isooctyl acrylate 180

[0086] Butyl acrylate 60

[0087] Acrylic 5

[0088] Hydroxyethyl Acrylate 5

[0089] Vinyl acetate 12

[0090] Isobornyl Acrylate 22

[0091] Azoazobisisobutyronitrile 1.6

[0092] N-methylolacrylamide 0.5

[0093] Ethyl acetate 500

[0094] The preparation method of the above-mentioned high-temperature-resistant solvent-type acrylate pressure-sensitive adhesive, its preparation steps are:

[0095] The first step: select 300% ethyl acetate according to the above weight ratio and dissolve 1% of azoazobisisobutyronitrile in it, and add 180% of isooctyl acrylate, 60% of butyl acrylate, and 22% of isobornyl acrylate ester and 12 vinyl acetate to prepare mixed monomer solution A; dissolve 1 N-methylol acrylamide, 5 parts of acrylic acid, and 5 parts of hydroxyethyl acrylate to prepare mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high temperature solvent resistant acrylate pressure sensitive adhesive which comprises the following components in parts by weight: 150-250 parts of 2-ethylhexyl acrylate, 50-100 parts of butyl acrylate, 3-10 parts of acrylic acid, 3-10 parts of hydroxyethyl acrylate, 10-20 parts of vinyl acetate, 15-35 parts of bornyl isoacrylate, 0.5-3 parts of azobisisobutyronitrile, 0.3-2 parts of N-hydroxymethyl acrylamide and 400-600 parts of ethyl acetate. The mechanical property, high temperature resistance and weather resistance of the emulsion type acrylate pressure sensitive adhesive are improved, so that the application range of the emulsion type acrylate pressure sensitive adhesive is widened, and the pressure sensitive adhesive has the characteristics of high viscidity, high temperature resistance, damp-heat aging resistance and low cost.

Description

technical field [0001] The invention belongs to the technical field of pressure-sensitive adhesives, and relates to a preparation method and application of a high-temperature-resistant solvent-type acrylate pressure-sensitive adhesive. Background technique [0002] At present, the adhesive tape used on the microwave oven door is mainly acrylic pressure-sensitive adhesive, and its main purpose is to protect the door body, and has the functions of explosion-proof and microwave radiation-proof. The main requirement is high temperature resistance. Ordinary microwave oven door stickers usually require a high temperature resistance of 180°C, while high-end microwave ovens with a high-power barbecue function require a high temperature resistance of 210°C. Therefore, one development direction of solvent-based acrylate pressure-sensitive adhesives is high temperature resistance. [0003] Patent CN 102516892 A relates to solvent-based acrylate pressure-sensitive adhesives for high-t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/08C09J11/06C09J7/02C08F220/18C08F220/28C08F218/08C08F220/58
Inventor 何俊李国烜
Owner 新丰杰力电工材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More