Ultraviolet-aging-resistant asphalt

A technology of aging asphalt and UV resistance, which can be used in building components, building insulation materials, buildings, etc., and can solve the problems of aging of polymer materials

Inactive Publication Date: 2015-03-25
JIANGSU JIANSHEN BIOLOGY AGROCHEM
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, since the use environment of asphalt is mainly used outdoors, the aging phenomenon of polymer materials caused by strong ultraviolet radiation is very prominent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] A kind of preparation method of anti-ultraviolet aging asphalt comprises the steps:

[0031] (1) Heat the asphalt to 170°C-180°C, and measure it for later use;

[0032] (2) Add the weighed rubber powder, paraffin wax, tackifying resin and glyceryl stearate, and shear at a medium speed in a high-speed shearer for 30 minutes;

[0033] (3) Add the weighed anti-ultraviolet aging additive into the asphalt in step (2), and stir at a high speed for 30 minutes;

[0034] (4) Raise the temperature to 190°C-200°C, add rubber powder, and stir for 1-2 hours until there are no visible particles to the naked eye.

[0035] The asphalt used is 90# heavy traffic asphalt;

[0036] The rubber powder used is one or more of 80 mesh styrene-butadiene rubber, chloroprene rubber, butadiene rubber, EPDM rubber and binary ethylene-propylene rubber.

[0037] The tackifying resin used is hydrogenated petroleum resin.

Embodiment 1

[0039] A kind of anti-ultraviolet aging asphalt is composed of the following components by mass percentage:

[0040] 80 mesh styrene-butadiene rubber 10%

[0041] Paraffin 5%

[0042] Hydrogenated Petroleum Resin 25%

[0043] Anti-ultraviolet aging additive 6%

[0044] Glyceryl Stearate 15%

[0045] The balance is 90# heavy traffic asphalt.

[0046] Wherein, the anti-ultraviolet aging additive consists of the following components by mass percentage:

[0047] Resorcinol Monobenzoate 15%

[0048] Phenyl salicylate 40%

[0049] Aromatic Oil 25%

[0050] Carbon Black 6%

[0051] Ceria 4%

[0052] Sulfur 10%.

Embodiment 2

[0054] A kind of anti-ultraviolet aging asphalt is composed of the following components by mass percentage:

[0055] 80 mesh neoprene 25%

[0056] Paraffin 35%

[0057] Hydrogenated Petroleum Resin 5%

[0058] Anti-ultraviolet aging additive 2%

[0059] Glyceryl Stearate 15%

[0060] The balance is 90# heavy traffic asphalt.

[0061] Wherein, the anti-ultraviolet aging additive consists of the following components by mass percentage:

[0062] Resorcinol Monobenzoate 35%

[0063] Phenyl salicylate 25%

[0064] Aromatic Oil 25%

[0065] Carbon Black 6%

[0066] Ceria 4%

[0067] Sulfur 5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of petrochemical engineering and particularly relates to ultraviolet-aging-resistant asphalt. The ultraviolet-aging-resistant asphalt is prepared from the following components in percentage by mass: 10-25% of rubber powder, 5-35% of paraffin, 5-25% of tackifying resin, 2-16% of ultraviolet-aging-resistant auxiliaries, 15% of glyceryl stearate and the balance of asphalt. The ultraviolet-aging-resistant asphalt provided by the invention can be used for greatly relieving natural attenuation of three indexes of evaporated residues of the asphalt, so that the high temperature resistance is greatly improved relative to the original asphalt, the temperature shrinkage cracks are reduced, the road surface fracturing is avoided; the ultraviolet-aging-resistant auxiliaries are added, so that the ultraviolet ageing resistance of the asphalt is greatly improved, and the service life of the asphalt is effectively prolonged.

Description

technical field [0001] The invention relates to the technical field of petrochemical industry, in particular to an ultraviolet aging-resistant asphalt. Background technique [0002] Asphalt is a dark brown complex mixture composed of different molecular weight hydrocarbons and their non-metallic derivatives. It is in liquid state and is a waterproof, moisture-proof and anti-corrosion organic gelling material. [0003] With the rapid development of my country's highway construction, high-grade highways have higher and higher requirements for modified asphalt materials. Although the use of polymer modified asphalt has become an effective way to improve the performance of asphalt pavement, its price is high and the cost is high; while the use of rubber powder modified road asphalt has abundant raw material rubber powder resources, low price, and simple processing technology. It can improve the elasticity of asphalt, and can improve the high and low temperature performance of a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L95/00C08L9/06C08L11/00C08L9/00C08L23/16C08L57/02C08L91/06C08K5/103C08K5/01C08K3/04C08K3/22C08K5/134C08K3/06
Inventor 杨月忠
Owner JIANGSU JIANSHEN BIOLOGY AGROCHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com