Rapid macromolecule machine-sprayable demulsification solidification filming waterproof coating and preparation method thereof

A waterproof coating and polymer technology, applied in polyester coatings, natural rubber coatings, polyurea/polyurethane coatings, etc., can solve the problems of limited application range, affecting efficacy, low solid content, etc., to achieve convenient construction and increase construction speed , the effect of high solid content

Inactive Publication Date: 2015-01-28
浙江鲁班建筑防水有限公司
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The polymer coatings currently used all use water-emulsified emulsion-based water-emulsion coatings. It uses cold construction, but its solid content is low, generally not exceeding (60-70%), and the thickness of each coating must be cured Conditions are limited, it is impossible to be very thick, and the film needs to be painted multiple times. Under humid conditions, the water in the emulsion cannot be volatilized, so it cannot be cured, which is very inconvenient
To meet the requirements of waterproof technical specifications, the thickness must be painted multiple times, which greatly affects the efficacy
limited scope of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The present invention is used for the water-proof paint that can be machine-sprayed fast demulsification and coagulation to form the waterproof coating that the raw material each component ratio is as follows:

[0043] A component:

[0044] Acrylic resin 38.5%

[0045] water 30%

[0046] Fatty acid ester polypeptide condensate 3%

[0047] Neoprene Latex 17%

[0048] SBR Latex 16%

[0049] Activated calcium carbonate (stearic acid coating) 3%;

[0050] B component:

[0051] Alkaline earth metal halide electrolyte 30%

[0052] Water 70%.

[0053] Above-mentioned waterproof coating preparation method is as follows:

[0054] 1) Melt acrylic resin and heat to 180-210°C, stir for 60-120 minutes, add emulsifier (fatty acid ester polypeptide condensate) at 140-160°C, stir and mix into the colloid mill, and grind together with emulsifier for 20-40 Minutes; the temperature drops to 60°C and distilled water is added to form a stable emulsion; the solid content reaches abo...

Embodiment 2

[0063] The present invention is used for the rapid demulsification and coagulation film-forming waterproof coating that can be sprayed by the machine. The ratio of each component of the raw materials is as follows:

[0064] A component:

[0065] Polyurethane resin 5%

[0066] Petroleum resin 32%

[0067] Zwitterionic emulsifier imidazoline type 2.5%

[0068] Neoprene Latex 13%

[0069] Natural rubber latex 13%

[0070] Bentonite 1%

[0071] Water 33.5%;

[0072] B component:

[0073] Polyamide-amine dendrimers 30%

[0074] Polyamine Condensate Demulsifier 3%

[0075] Water 67%.

[0076] Above-mentioned waterproof coating preparation method is as follows:

[0077] 1) Melt polyurethane resin and petroleum resin together and heat to 150-155°C, stir for 60-120 minutes, add emulsifier (zwitterionic emulsifier imidazoline type) at 140-160°C, stir and mix into the colloid mill, and emulsifier Grind together for 20-40 minutes; add distilled water to lower the temperature be...

Embodiment 3

[0086] The present invention can use the rapid demulsification solidification film-forming waterproof coating that can be sprayed by the machine. The ratio of each component of the raw materials is as follows:

[0087] A component:

[0088] Acrylic 7%

[0089] Alkyd 30%

[0090] Petroleum Sulfonate 3%

[0091] Butyl Rubber Latex 12%

[0092] Styrene Butadiene Rubber Latex 10%

[0093] Wollastonite powder 1%

[0094] Water 37%;

[0095] B component:

[0096] Alkaline earth metal halide electrolyte, 25%

[0097] Contains Alkyl Ether Sulfates 3%

[0098] Water 72%.

[0099] The above-mentioned polymer waterproof coating preparation method is as follows:

[0100] 1) Use alkyd resin and acrylic resin to grind together, pour the mixture into a heating tank to melt and heat to about 180°C, stir for 60-120 minutes, add emulsifier (petroleum sulfonate) and stir at 120°C to enter the colloid mill , Grind with emulsifier for 20-40 minutes; add distilled water to lower the temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of waterproof coatings, and in particular relates to a rapid macromolecule machine-sprayable demulsification solidification filming waterproof coating and a preparation method thereof. The rapid macromolecule machine-sprayable demulsification solidification filming waterproof coating consists of a component A and a component B, wherein the component A consists of the following components in percentage by weight: 25-35% of macromolecule, 20-40% of water, 1-5% of an emulsifying agent, 20-50% of rubber latex and 0-5% of packing; the component B consists of the following components in percentage by weight: 30-40% of a demulsification agent and 60-70% of water. The waterproof coating can be rapidly demulsified and dehydrated to form a coating waterproof protecting layer which is excellent in waterproof property, after the coating is sprayed, the coated layer is dried into a film, the high elasticity, the low temperature flexibility and the aging resistance of a rubber material are maintained, and the coating has the advantages of high puncture force resistance, water permeation prevention, temperature resistance, freezing resistance, chemical corrosion resistance, cracking resistance and the like.

Description

technical field [0001] The invention belongs to the technical field of waterproof coatings, in particular to a polymer machine-sprayable rapid demulsification and solidification film-forming waterproof coating and a preparation method thereof. Background technique [0002] The current waterproof materials are mainly waterproof membranes and waterproof coatings. [0003] Modified asphalt membranes, such as SBS and APP membranes, which are more popular in the waterproof material market at present, require flame spray guns to carry out on-site surface melting, require open flames, have high technical requirements, and easily cause the surface hot melt adhesive to coke. The width of the membrane is only one meter, and there are many overlaps during laying. Due to the shape requirements of the base layer, it needs to be cut, and the amount of overlap is increased, which is likely to cause hidden dangers of joint waterproofing; self-adhesive asphalt waterproof membranes have weak ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/00C09D157/02C09D167/08C09D175/04C09D107/02C09D109/08C09D123/22C09D111/02C09D7/12
CPCC09D133/00C08L2205/025C08L2205/03C08L2205/035C08L2207/53C09D7/40C09D7/61C09D7/63C09D7/65C09D7/67C09D157/02C09D167/08C08L11/02C08L9/08C08K2003/265C08L7/02C08L75/04C08L79/02C08K3/346C08L23/22C08L33/00C08L57/02C08K3/34C08K3/16C08K5/41
Inventor 项晓睿
Owner 浙江鲁班建筑防水有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap