Phosphomolybdate compound, phosphomolybdate nonlinear optical crystal and preparation method and use
A nonlinear optics and crystal technology, applied in the field of phosphomolybdate compounds and phosphomolybdate nonlinear optical crystals, can solve problems such as gray traces and application limitations
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0033] synthetic K 9 P 4 Mo 4 HO 27 The feeding amount of the reagent used in the compound:
[0034] NH 4 h 2 PO 4 34.5 grams (0.3 mole)
[0035] MoO 57.6 g (0.4 mole)
[0036] K 2 HPO 4 17.4 grams (0.1 mole)
[0037] K 2 CO 3 48.3 g (0.35 mole)
[0038] The specific operation steps are as follows:
[0039] Accurately weigh in the operation box according to the above mass, put into the agate mortar, mix well and grind carefully, then put into Put it into a covered platinum crucible, compact it, put it into a muffle furnace, and slowly heat up to 400°C for sintering for 48 hours. The heating rate must be slow at the beginning to prevent the change of the proportion due to decomposition, so that the solid phase reaction can fully proceed. , after cooling down to room temperature, take it out and grind it in the operation box, then put it in a crucible for compaction, put it in a muffle furnace, burn it at 400°C to constant weight as the reaction end point, and...
Embodiment 2
[0042] synthetic K 4 Rb 5 P 4 Mo 4 HO 27 The feeding amount of the reagent used in the compound:
[0043] NH 4 h 2 PO 4 34.5 grams (0.3 mole)
[0044] MoO 57.6 g (0.4 mole)
[0045] K 2 HPO 4 17.4 grams (0.1 mole)
[0046] K 2 CO 3 13.8 grams (0.1 mole)
[0047] Rb 2 CO 3 57.75 g (0.25 mole) compound
[0048] The specific operation steps are as follows:
[0049] Accurately weigh in the operation box according to the above mass, put into the agate mortar, mix well and grind carefully, then put into Put it into a covered platinum crucible, compact it, put it into a muffle furnace, and slowly heat up to 400°C for sintering for 48 hours. The heating rate must be slow at the beginning to prevent the change of the proportion due to decomposition, so that the solid phase reaction can fully proceed. , after cooling down to room temperature, take it out and grind it in the operation box, then put it in a crucible for compaction, put it in a muffle furnace, burn ...
Embodiment 3-9
[0051] Example 3-9, K 9 P 4 Mo 4 HO 27 Examples of Nonlinear Optics Crystal Growth:
PUM
Property | Measurement | Unit |
---|---|---|
wavelength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com