Modified sepiolite used for a polyethylene corrugated pipe material and a preparing method of the modified sepiolite
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A corrugated pipe and sepiolite technology, which is applied in the field of modified sepiolite for polyethylene corrugated pipe materials and its preparation, can solve the problems of difficult sepiolite dispersion, easy layering, and much dust, and improve the dispersion performance , Improve mechanical strength, solve the effect of difficult dispersion
Inactive Publication Date: 2014-10-29
HEFEI HEAN MACHINERY MFG
View PDF6 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The purpose of the present invention is to provide a modified sepiolite for polyethylene corrugated pipe material and its preparation method, which solves the problems of difficult sepiolite dispersion, easy delamination, and much dust
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0010] A modified sepiolite for polyethylene corrugated pipe material, made of the following raw materials in weight (kg): sepiolite 95, nanometer zirconia 15, shell powder 22, perfluoroalkyl ethyl acrylate 6, Buty fatty acid 3, glucose pentaacetate 12, dammar resin 10, shellac 8, walnut shell powder 7, ozokerite 5, distearyl dimethyl ammonium chloride 1.5, polybutylene terephthalate 45. Ethylene-vinyl alcohol copolymer 30, polydibromophenylene ether 10, calcium hypophosphite 8, zinc laurate 2.5, additive 6;
[0011] The preparation method of described auxiliary agent is as follows: a, get the raw material of following weight (kg): tri-tert-butylphosphine tetrafluoroborate 4, aluminum triacetylacetonate 3, stearyl methacrylate 7, hexamethylenetetramine 3. Lingkite 10, dicyclopentadiene 6, zinc p-toluene sulfinate 2, waste glass powder 10, bamboo charcoal powder 10, mannide monooleate 2.5, tetramethyltetravinyl cyclotetra Siloxane 1.5, bisphenol s1, N-phenylmaleimide 2; b, mag...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
Modified sepiolite used for a polyethylene corrugated pipe material and a preparing method of the modified sepiolite are disclosed. The modified sepiolite is prepared from following raw materials by weight: 85-105 parts of sepiolite, 10-15 parts of nanometer zirconium dioxide, 18-26 parts of shell powder, 4-7 parts of perfluoro alkyl ethyl acrylate, 2-5 parts of tallow fatty acid, 9-16 parts of glucose pentaacetate, 10-15 parts of gum dammar, 6-12 parts of shellac, 5-10 parts of walnut shell powder, 4-8 parts of ozokerite, 1-2 parts of distearyl dimethyl ammonium chloride, 40-50 parts of polybutylene terephthalate, 25-35 parts of an ethylene-ethenol copolymer, 10-15 parts of polybrominated diphenyl ethers, 5-10 parts of calcium hypophosphite, 2-3 parts of zinc laurate and 5-7 parts of auxiliary agents. The modified sepiolite and the method can significantly improve the dispersing property of the sepiolite in a polyethylene base material, intensifying adhesion of sepiolite-polyethylene interfaces, effective overcome problems that are hard dispersion, easy layering, much dust, and the like of the sepiolite at present, and improve mechanical strength, wear resistance, fatigue resistance, elasticity, machinability, and other properties of the polyethylene material.
Description
technical field [0001] The invention relates to a modified sepiolite for polyethylene corrugated pipe material and a preparation method thereof, belonging to the technical field of inorganic fillers. Background technique [0002] Sepiolite is a kind of natural magnesium silicate containing water, porous, high specific area and fibrous structure. Because of its high aspect ratio, large specific surface area and good thermal stability, it is used as a A new inorganic semi-reinforcing filler has been widely used in the plastics industry. However, in the filling process of polyethylene materials, traditional sepiolite is often prone to uneven dispersion, layering, and excessive dust during production and construction, which limits its application in the field of polyethylene materials. To further improve its performance and broaden its application field, sepiolite must be modified. Contents of the invention [0003] The purpose of the present invention is to provide a modifi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.