A stainless steel faucet shell welding process

A faucet shell and welding process technology, applied in welding equipment, laser welding equipment, manufacturing tools, etc., can solve the problems of easy damage to the faucet shell, large influence on welding effect, insufficient bonding force, etc., and achieve excellent mechanical properties and safety Good hygienic performance and small deformation of the workpiece

Active Publication Date: 2016-02-24
HUAQIAO UNIVERSITY
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method does not disclose the detailed welding process, because argon arc welding often causes deformation, hardness reduction, sand holes, local annealing, cracking, pinholes, wear, scratches, undercuts, or bonding due to the large heat-affected zone. Insufficient force and internal stress damage, etc. The specific welding method has a great influence on the welding effect. In addition, this method still needs polishing after welding, which is easy to damage the faucet shell

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A stainless steel faucet shell welding process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention will be further described below with reference to the accompanying drawings and specific embodiments.

[0034] The welding process of the stainless steel faucet shell of this implementation includes the following steps:

[0035] (1) Material selection: choose austenitic stainless steel 1Cr18Ni8 plate with a thickness of 2mm-3mm as the material, and the specific plate thickness can be selected according to actual needs.

[0036] (2) Parts preparation: The austenitic stainless steel 1Cr18Ni8 plate is made into the body and bottom plate of the faucet shell by pressure processing. During the processing, the unevenness and dislocation of the corresponding welding positions on the body and the bottom plate should be It should be controlled within 0.3mm. When the pressure processing method cannot achieve the required unevenness and dislocation, the unevenness and dislocation of the corresponding welding positions on the body and the bottom plate should be...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a water faucet shell production technology, in particular to a stainless steel water faucet shell welding technology. The stainless steel water faucet shell welding technology comprises the following steps of material selection, part preparation, cleaning before welding, part clamping, part welding and post-welding checking. In the part clamping process, a welding clamp needs to be adjusted so that a welding position of a base plate can be embedded in a welding position of a body. A laser penetration fusion welding method is adopted for part welding. Due to the facts that the welding position of the base plate is embedded in the welding position of the body, and the body and the base plate are welded together through the laser penetration fusion welding method which is highly centralized in energy density, weld strength of weld joints is high, and the weld joints are compact and beautiful in appearance.

Description

technical field [0001] The invention relates to a production process of a faucet shell, in particular to a welding process of a stainless steel faucet shell. Background technique [0002] At present, the casting method is commonly used in the industry to produce the faucet shell, and the main material used is copper alloy or zinc alloy, which is costly. The general production process of the faucet shell is: sand core forming - sand core inspection - casting alloy smelting - chemical composition analysis - gravity casting - subsequent processing and so on. However, due to the overall soft and porous nature of the sand, the dimensional accuracy of the casting is low, and the surface is also rough and prone to defects, which makes the forming quality of the faucet poor. At the same time, each sand casting mold can only be poured once. After the casting is obtained, the casting mold is damaged and must be recast, which greatly increases the production cost and reduces the produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K26/14B23K26/60
CPCB23K26/14B23K26/28B23K2103/04
Inventor 周广涛王立鹏陈强陈志伟陈聪彬刘骏梁国俐
Owner HUAQIAO UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com