Preparation method of anti-aging and anti-bacterial PE pipe

An anti-aging and pipe technology, applied in the field of PE pipe preparation, can solve problems such as negative effects on the liver, and achieve good anti-aging, strong practicability and good dispersibility.

Active Publication Date: 2014-06-25
GUANGXI JIALI IND & TRADE
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For improving the antibacterial and bacteriostatic effects of PE pipes, the existing technology is mainly realized by adding inorganic antibacterial agents such as silver, copper, zinc, titanium, etc. Although simple inorganic antibacterial agents have good thermal stability, they cannot be used in plastic extrusion and processing It will not decompose and deteriorate during the process, but long-term drinking of drinking water containing inorganic antibacterial agents such as silver, copper, zinc, and titanium will have a negative impact on the human liver, so this also limits the application of inorganic antibacterial agents , the use of organic antibacterial agents instead of inorganic antibacterial agents has become a current research hotspot and development trend

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Add 5% nano-modified bamboo charcoal plastic particles to PE resin and mix evenly. After heating to 200°C, extrude through a twin-screw extruder, cool and vacuum shape to obtain anti-aging and antibacterial PE pipes.

[0020] The preparation method of the nano-modified bamboo charcoal plastic particles is: adding 5 parts of nano-modified bamboo charcoal powder, 3 parts of No. 10 white oil, 5 parts of polyethylene wax, 0.3 parts of silane coupling agent and 22 parts of PE resin into a high-speed mixer mixing, and extruding and granulating through a twin-screw extruder after mixing to obtain nano-modified bamboo charcoal plastic particles.

[0021] The molecular weight of polyethylene wax is 3000-5000, and the melt index of PE resin is 10-30g / min.

[0022] The preparation method of the nano-modified bamboo charcoal powder is as follows: dissolving and stirring the nano-titanium dioxide-zinc oxide composite powder in boiling water to form an emulsion, then making the 80-me...

Embodiment 2

[0025] Add 7% nano-modified bamboo charcoal plastic particles to PE resin and mix evenly. After heating to 208°C, extrude through a twin-screw extruder, cool and vacuum shape to obtain anti-aging and antibacterial PE pipes.

[0026] The preparation method of the nano-modified bamboo charcoal plastic particles is as follows: 5 parts of nano-modified bamboo charcoal powder, 0.2 parts of No. 10 white oil, 7 parts of polyethylene wax, 2.4 parts of silane coupling agent and 38 parts of PE resin are added to a high-speed mixer mixing, and extruding and granulating through a twin-screw extruder after mixing to obtain nano-modified bamboo charcoal plastic particles.

[0027] The molecular weight of polyethylene wax is 3000-5000, and the melt index of PE resin is 10-30g / min.

[0028] The preparation method of the nano-modified bamboo charcoal powder is as follows: dissolving and stirring the nano-titanium dioxide-zinc oxide composite powder in boiling water to form an emulsion, then ma...

Embodiment 3

[0031] Add 3% nano-modified bamboo charcoal plastic particles to PE resin and mix evenly. After heating to 179°C, extrude through a twin-screw extruder, cool and vacuum shape to obtain anti-aging and antibacterial PE pipes.

[0032] The preparation method of the nano-modified bamboo charcoal plastic particles is as follows: 5 parts of nano-modified bamboo charcoal powder, 4.5 parts of No. 10 white oil, 2.7 parts of polyethylene wax, 4.7 parts of silane coupling agent and 30 parts of PE resin are added to a high-speed mixer mixing, and extruding and granulating through a twin-screw extruder after mixing to obtain nano-modified bamboo charcoal plastic particles.

[0033] The molecular weight of polyethylene wax is 3000-5000, and the melt index of PE resin is 10-30g / min.

[0034] The preparation method of the nano-modified bamboo charcoal powder is as follows: dissolving and stirring the nano-titanium dioxide-zinc oxide composite powder in boiling water to form an emulsion, then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an anti-aging and anti-bacterial PE pipe. The preparation method comprises the following steps: adding 3-8% of nano-modified bamboo charcoal plastic particles into PE resin, uniformly mixing, heating to 170-210 DEG C, then extruding by a twin-screw extruder, cooling and performing vacuum shaping to obtain the anti-aging and anti-bacterial PE pipe. The core of the invention is that the nano-modified bamboo charcoal plastic particles are adopted to replace carbon black and an inorganic metal antibacterial agent, so that the PE pipe has good anti-aging and anti-bacterial performances. The preparation method disclosed by the invention has the advantages of strong practicality, low cost, greenness and environmental friendliness, the nano-modified bamboo charcoal plastic particles have good dispersibility and stable natures, and the obtained PE pipe has excellent anti-aging and anti-bacterial performances, as well as relatively strong actual application value and market development prospects.

Description

technical field [0001] The invention relates to a preparation method of a PE pipe, and the prepared PE pipe has good anti-aging and antibacterial properties. Background technique [0002] PE pipe is a thermoplastic resin pipe with high crystallinity and non-polarity. Because PE pipe is non-toxic, tasteless, odorless, good cold resistance, heat resistance and chemical stability, high rigidity and toughness, and mechanical With many advantages such as good performance and convenient installation, it is widely used in the fields of building water supply and drainage, buried drainage pipes, gas pipelines and telecommunications engineering. [0003] However, when PE pipes are stored or used in the open air, under the action of ultraviolet light, they are prone to aging, discoloration, brittleness and even pulverization, thus losing their mechanical properties and affecting the use of PE pipes. Therefore, PE pipes need to be improved. It has good anti-aging performance, prolongs ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08K13/02C08K3/04C08K3/08C08K3/14C08K3/22C08K5/01B29C47/92B29B9/06B29C48/92
CPCB29B9/06B29C48/92B29C2948/92704C08K2201/011C08L23/06C08L2201/08C08L2203/18C08L2205/025C08L2205/03C08K2003/2241C08K2003/2296C08K3/04B29C48/09B29C48/40B29C48/90B29C48/904B29C48/911B29C48/916B29C2948/92695B29C2948/92895
Inventor 苏桂榕张德王瑞平盘小琴
Owner GUANGXI JIALI IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products