Alloy material for high wear-resistant cold rolls and preparation method thereof

A technology of alloy materials and cold rolls, which is applied in the field of alloy materials for high wear-resistant cold rolls and its preparation, can solve the problems of high requirements and harshness, achieve good toughness, increase yield, high hardness and wear resistance Effect

Active Publication Date: 2014-04-23
马鞍山市方圆材料工程股份有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]Pumps and valves work in various and harsh environments, and have high requirements for materials. At present, there are many kinds of alloy steels used for pumps and valves, and the technology has made great progress, but There are still many problems, such as wear resistance, hardness, antirust performance, corrosion resistance, high and low temperature resistance, brittleness, toughness, etc., which cannot meet the production requirements in many occasions, and further improvement is needed to increase production efficiency. , reduce costs, improve safety, provide guarantee for the development of high-precision technology, and provide impetus for social development, the task is still very arduous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] An alloy material for high wear-resistant cold rolling rolls, which contains chemical element components and mass percentages: carbon 0.8-0.9, tungsten 2.1-2.3, molybdenum 1.2-1.5, vanadium 2.2-2.4, chromium 2.1-2.5, niobium 0.05 -0.10, lanthanum 0.15-0.20, neodymium 0.05-0.10, Mn0.4-0.6, Co0.03-0.05, P≤0.030, S≤0.030, and the balance is iron.

[0014] The production method of the alloy material for the high wear-resistant cold roll is as follows:

[0015] (1) Prepare pig iron and scrap iron as the source of iron matrix in a ratio of 1:0.7, put pig iron into the furnace for melting, perform desulfurization, deoxidation, use refining agent for one-time refining, add alloy components for alloying, and then add scrap iron to melt , adding refining agent for secondary refining, testing and adjusting the content of chemical elements to pass, casting, post-casting heat treatment, etc.;

[0016] (2) The order of batches of alloying elements added to the furnace during the all...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
impact absorption energyaaaaaaaaaa
Login to View More

Abstract

The invention discloses an alloy material for high wear-resistant cold rolls and a preparation method thereof. The alloy material comprises the following chemical elements in percentage by mass: 0.8-0.9% of carbon, 2.1-2.3% of tungsten, 1.2-1.5% of molybdenum, 2.2-2.4% of vanadium, 2.1-2.5% of chromium, 0.05-0.10% of niobium, 0.15-0.20% of lanthanum, 0.05-0.10% of neodymium, 0.4-0.6% of Mn, 0.03-0.05% of Co, not more than 0.030% of P, not more than 0.030% of S and the balance of ferrum. The alloy disclosed by the invention not only has high hardness and wear resistance, but also has good toughness and can resist cracking and stripping caused by bending stress, torsion stress and shearing stress, meanwhile, the alloy has high contact fatigue strength and high breaking tenacity and thermal shock strength, thereby being suitable for making cold rolls. The refining agent disclosed by the invention is applied to casting production, the porosity in a casting is reduced by 1-2 degrees, and oxide inclusions are reduced by about 2 grades.

Description

technical field [0001] The invention relates to the field of metal material preparation, in particular to an alloy material for high wear-resistant cold rolling rolls and a preparation method thereof. Background technique [0002] The working environment of pump valves is diverse and harsh, and the requirements for materials are very high. At present, there are many kinds of alloy steel used in pump valves, and the technology has made great progress, but there are still many problems, such as wear resistance, hardness, rust resistance Performance, corrosion resistance, high and low temperature resistance, brittleness, toughness, etc., cannot meet the production requirements in many occasions, and further improvement is needed to improve production efficiency, reduce costs, and improve safety. Guaranteeing and providing impetus for social development are still arduous tasks. Contents of the invention [0003] The object of the present invention is to provide an alloy mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/30C21D6/00
CPCY02P10/20
Inventor 何玉平陶国斌史承海晏绍斌屠明安
Owner 马鞍山市方圆材料工程股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products