Non-flame spread CPE rubber sheath material and preparation method thereof

A sheath material and rubber technology, applied in rubber insulators, plastic/resin/wax insulators, organic insulators, etc., can solve the problems of insufficient high temperature resistance, flammability and delay in case of open fire, etc., to achieve good flame retardant effect, Excellent high temperature resistance and improved safety effect

Active Publication Date: 2014-01-15
安徽天民电气科技有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The CPE sheath material also has the disadvantages of not being high enough in high temperature resistance, flammable and delayed in case of an open flame

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-flame spread CPE rubber sheath material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A non-flammable CPE rubber sheath material, made of the following raw materials (kg): chlorinated polyethylene 70, polytetrafluoroethylene 18, dimethyl silicone rubber 12, chlorinated paraffin 15, precipitated white carbon black 35. Gas-mixed carbon black 20, calcium silicate 8, nano wollastonite 12, octyl epoxy stearate 5, dioctyl maleate 10, dicumyl peroxide 3, diallyl phthalate Ester 5, ammonium polyphosphate 15, coated red phosphorus 8, calcium hydroxide 4, zinc stearate 1.5, antioxidant 40200.8, antioxidant DLTP0.6, composite filler 4;

[0013] The preparation method of the described composite filler is as follows: a. get the raw materials of the following weight (kg): attapulgite 8, sepiolite 8, potassium feldspar 4, two (dioctyloxypyrophosphate) ethylene titanic acid Ester 1.5, titanium dioxide 4, nano-silica 5, nano-alumina 3, paraffin oil 6, polyisobutylene 4, ferrocene 2, zinc methacrylate 1, p-tert-octylphenol formaldehyde resin 8; b. Roast clay, sepiolite a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a non-flame spread CPE rubber sheath material and a preparation method thereof. The sheath material is prepared from the following raw materials in parts by weight: 60-80 parts of chlorinated polyethylene, 15-20 parts of Teflon, 10-15 parts of dimethyl silicone rubber, 12-18 parts of chlorinated paraffin, 30-40 parts of precipitated white carbon black, 20-30 parts of gas-mixture carbon black, 5-10 parts of calcium silicate, 10-15 parts of nanometer wollastonite, 4-6 parts of octyl epoxy stearate, 10-15 parts of dioctyl maleate, 3-4 parts of dicumyl peroxide, 4-6 parts of diallyl phthalatem, 10-15 parts of ammonium polyphosphate, 5-10 parts of encapsulated red phosphorus, 3-5 parts of calcium hydrate, 1-2 parts of zine stearate, 0.5-1 part of antiager 4020, 0.5-1 part of antioxidant DLTP and 3-6 parts of a composite filling material. The sheath material of the invention is good in flame retardation effect, is not combusted when contacting with naked fire, can be quickly extinguished automatically, has non-flame spread performance and excellent fireproofness and high-temperature resistance, overcomes the defects that conventional flame-retardant cable sheath materials still can be combusted and has flame spread performance, and helps to substantially improve the usage security of cables.

Description

technical field [0001] The invention relates to a cable material and a preparation method thereof, in particular to a non-flammable CPE rubber sheath material and a preparation method thereof. Background technique [0002] Chlorinated polyethylene is a polymer synthetic material made from polyethylene modified by chlorination. CPE has many advantages as wire and cable sheath material: (1) excellent ozone resistance and corona resistance; (2) good aging resistance and atmospheric aging resistance; (3) good oil resistance and chemical resistance; (4) Good tear resistance and physical and mechanical properties. The CPE sheath material also has the disadvantages of insufficient high temperature resistance, flammable and delayed combustion in case of an open flame. Contents of the invention [0003] The object of the present invention is to provide a non-flammable CPE rubber sheath material and a preparation method thereof. The sheath material has the characteristics of high ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L27/18C08L83/04C08K13/06C08K9/02C08K3/34C08K3/22C08K3/36C08K5/521C08K3/32H01B3/44H01B3/28H01B7/295
CPCC08K2201/011C08K2201/014C08L23/286C08L2201/02C08L2203/202C08L2205/03H01B3/441H01B7/18H01B7/295C08L27/18C08L83/04C08K13/06C08K9/02C08K3/346C08K2003/222C08K3/36C08K5/521C08K2003/323
Inventor 曹悦煕
Owner 安徽天民电气科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com