Low-alloy high-wear-resistance cast steel

A high wear-resistant, low-alloy technology, applied in the field of wear-resistant cast steel manufacturing, can solve the problems of high production cost, complicated process, difficult to control, etc., and achieve the effect of good strength and toughness, simplified process, and simple composition

Inactive Publication Date: 2013-04-24
张芝莲
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

(3) Not all mechanical properties of typical lower bainite are superior
However, the process of this production method is complex and difficult to control, and the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-alloy high-wear-resistance cast steel
  • Low-alloy high-wear-resistance cast steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] 1) Use scrap steel, ferrosilicon, ferromanganese, ferrosilicon, ferromolybdenum, ferrochrome, ferrotitanium, ferrovanadium, ferroniobium, and rare earth silicon as raw materials for smelting, and make ingredients according to the following components: C: 0.25 wt.%;

[0052] Si: 0.9 wt.%;

[0053] Mn: 0.3 wt.%;

[0054] Cr: 0.7 wt.%;

[0055] Mo: 0.15 wt.%;

[0056] Ti: 0.05 wt.%;

[0057] Nb: 0.01 wt.%;

[0058] V: 0.05 wt.%;

[0059] RE: 0.01 wt.%;

[0060] P, S≤0.01 wt.%

[0061] The rest is Fe and unavoidable impurities;

[0062] 2) Using medium frequency induction furnace for smelting, first heat and melt ordinary steel scrap and ferrochrome, and conduct pre-furnace analysis;

[0063] 3) Add ferromanganese, ferrosilicon, and ferromolybdenum in turn, wait until all are melted, then add ferrochrome and then further melt, deoxidize with aluminum wire, then pour molten steel into it and place ferrotitanium, ferrosilicon, ferroniobium, and rare earth at the same ...

Embodiment 2

[0070] 1) Use steel scrap, ferrosilicon, ferromanganese, ferrosilicon, ferromolybdenum, ferrochrome, ferrotitanium, ferrovanadium, ferroniobium, and rare earth silicon as raw materials for smelting, and make ingredients according to the following components: C: 0.3 wt.%;

[0071] Si: 1.2 wt.%;

[0072] Mn: 1.0 wt.%;

[0073] Cr: 0.85 wt.%;

[0074] Mo: 0.2 wt.%;

[0075] Ti: 0.25 wt.%;

[0076] Nb: 0.03 wt.%;

[0077] V: 0.15 wt.%;

[0078] RE: 0.06 wt.%;

[0079] P, S≤0.02 wt.%

[0080] The rest is Fe and unavoidable impurities;

[0081] 2) Using medium frequency induction furnace for smelting, first heat and melt ordinary steel scrap and ferrochrome, and conduct pre-furnace analysis;

[0082] 3) Add ferromanganese, ferrosilicon, and ferromolybdenum in turn, wait until all are melted, then add ferrochrome and then further melt, deoxidize with aluminum wire, then pour molten steel into it and place ferrotitanium, ferrosilicon, ferroniobium, and rare earth at the same t...

Embodiment 3

[0089] 1) Use scrap steel, ferrosilicon, ferromanganese, ferrosilicon, ferromolybdenum, ferrochrome, ferrotitanium, ferrovanadium, ferroniobium, and rare earth silicon as raw materials for smelting, and make ingredients according to the following components: C: 0.35 wt.%;

[0090] Si: 1.6 wt.%;

[0091] Mn: 1.8 wt.%;

[0092] Cr: 1.0 wt.%;

[0093] Mo: 0.3 wt.%;

[0094] Ti: 0.35 wt.%;

[0095] Nb: 0.05 wt.%;

[0096] V: 0.25 wt.%;

[0097] RE: 0.1 wt.%;

[0098] P, S≤0.03 wt.%

[0099] The rest is Fe and unavoidable impurities;

[0100] 2) Using medium frequency induction furnace for smelting, first heat and melt ordinary steel scrap and ferrochrome, and conduct pre-furnace analysis;

[0101] 3) Add ferromanganese, ferrosilicon, and ferromolybdenum in turn, wait until all are melted, then add ferrochrome and then further melt, deoxidize with aluminum wire, then pour molten steel into it and place ferrotitanium, ferrosilicon, ferroniobium, and rare earth at the same time...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Impact toughnessaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a low-alloy high-wear-resistance cast steel which comprises the following components: 0.25-0.35wt.% of C, 0.9-1.6wt.% of Si, 0.3-1.8wt.% of Mn, 0.7-1.0wt.% of Cr, 0.15-0.3wt.% of Mo, 0.05-0.35wt.% of Ti, 0.01-0.05wt.% of Nb, 0.05-0.25wt.% of V, 0.01-0.1wt.% of RE, at most 0.03wt.% of P and S, and the balance of Fe and inevitable impurities. The invention has the advantages of simple preparation process and favorable toughness compatibility.

Description

technical field [0001] The invention relates to a manufacturing technology of wear-resistant cast steel used under impact, in particular to a low-alloy high wear-resistant cast steel. [0002] Background technique [0003] Wear is a common phenomenon in the industrial field and daily life, and it is also an important cause of material and energy loss. This ancient and complex problem has always been one of the focuses of people's attention. Abrasion is one of the main failure modes of materials, and the economic loss it causes is very huge. For example, according to figures released by the United States in the 1980s, the annual loss due to wear and tear was as high as one billion U.S. dollars, the loss caused by wear and tear in the former Soviet Union reached 12 billion rubles each year, and the loss caused by friction and wear in the Federal Republic of Germany exceeded 10 billion West Deutschmarks each year. . At present, my country still lacks comprehensive statistics...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/38C22C38/34C22C38/28C21D1/28
CPCY02P10/20
Inventor 张芝莲
Owner 张芝莲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com