Corrosion-resisting ferroalloy material for fastener
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A ferroalloy and fastener technology, which is applied in the field of corrosion-resistant ferroalloy materials for fasteners, can solve problems such as low elongation, broken bolts, broken edges, etc., and achieve the effect of improving uniformity and strength
Inactive Publication Date: 2013-04-03
NINGBO TENGLING IND & TRADE
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Fasteners such as bolts and nuts are generally made of carbon steel, stainless steel, high-strength steel, etc. Except for stainless steel, other materials have poor corrosion resistance. During use, severe corrosion will occur and cause bolts and nuts to Inseparable, especially outdoors or in harsh environments, fasteners produced from the above materials are disposable and must be replaced when repairs or maintenance are performed
However, stainless steel fasteners can only be used in some special places due to high cost.
Moreover, the above-mentioned material also has a disadvantage of insufficient wear resistance and low elongation. In actual use, when the fastening force is large, the bolts will break or the nuts will crack.
[0003] There are also technologies that use chromium-manganese-nitrogen series iron alloys to produce fasteners, but the cold work hardening rate of this type of iron alloys rises too fast, the processing is difficult, and the cold pier and stamping performance is poor, and there is a broken edge phenomenon
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] A corrosion-resistant iron alloy material for fasteners, its composition is by weight percentage, 0.08% carbon, 15% manganese, 0.3% silicon, 14.5% chromium, 0.03% molybdenum, 0.5% nickel, 0.03% vanadium, 0.1% titanium, 0.01% zirconium, 0.01% boron, 0.3% copper, 0.15% nitrogen, 0.001% lanthanum, and the balance is iron.
Embodiment 2
[0027] A corrosion-resistant iron alloy material for fasteners, its composition is by weight percentage, 0.10% carbon, 15.5% manganese, 0.6% silicon, 15.0% chromium, 0.05% molybdenum, 1.0% nickel, 0.05% vanadium, 0.3% titanium, 0.03% zirconium, 0.03% boron, 0.5% copper, 0.25% nitrogen, 0.002% lanthanum, and the balance is iron.
Embodiment 3
[0029] A corrosion-resistant iron alloy material for fasteners, its composition is by weight percentage, 0.09% carbon, 15.2% manganese, 0.5% silicon, 14.8% chromium, 0.04% molybdenum, 0.8% nickel, 0.035% vanadium, 0.2% titanium, 0.02% zirconium, 0.025% boron, 0.45% copper, 0.20% nitrogen, 0.0015% lanthanum, 0.015% niobium, and the balance is iron.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a corrosion-resisting ferroalloy material for a fastener. The ferroalloy material comprises the following components in percentage by weight: 0.08-0.10% carbon, 15-15.5% manganese, 0.3-0.6% silicon, 14.5-15.0% of chromium, 0.03-0.05% of molybdenum, 0.5-1.0% of nickel, 0.03-0.05% of vanadium, 0.1-0.3% of titanium, 0.01-0.03% of zirconium, 0.01-0.03% of boron, 0.3-0.5% of copper, 0.15-0.25% of nitrogen, 0.001-0.002% of lanthanum, and the balance of iron. The ferroalloy produced by the technical scheme is a ferroalloy material with relatively high mechanical properties, wear resistance, tenacity and wear resistance.
Description
technical field [0001] The invention belongs to the field of corrosion-resistant ferroalloys, in particular to a corrosion-resistant ferroalloy material for fasteners. Background technique [0002] Fasteners such as bolts and nuts are generally made of carbon steel, stainless steel, high-strength steel, etc. Except for stainless steel, other materials have poor corrosion resistance. During use, severe corrosion will occur and the bolts and nuts will be damaged. Inseparable, especially outdoors or in harsh environments, fasteners made of the above materials are disposable and must be replaced when repairs or maintenance are performed. The production of fasteners made of stainless steel can only be used in some special places due to the high cost. Moreover, the above-mentioned materials also have a disadvantage of insufficient wear resistance and low elongation. In actual use, when the fastening force is large, the bolts will break or the nuts will crack. [0003] There is a...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more