Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Acrylic resin paint composition

A technology of acrylic resin and resin composition, which is applied in the field of acrylic resin composition and wear-resistant acrylic resin coating composition to achieve the effects of wide sources, reduced wear and high wear resistance

Inactive Publication Date: 2013-04-03
SUZHOU TAIZHENG CHEM TECH CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In the prior art, there is no report of adding polytetrafluoroethylene to acrylic resin in nanometer size

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylic resin paint composition
  • Acrylic resin paint composition
  • Acrylic resin paint composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention will be further described below in conjunction with embodiment.

[0023] Composition formula (mass ratio) in the embodiment of table 1 and comparative example

[0024] Embodiment one Embodiment two Embodiment Three Embodiment four Comparative example one Comparative example two Acrylic 100 100 100 100 100 100 Melamine 60 40 35 70 Methyl ether acetate 80 30 40 75 Nano PTFE 1 1.5 1.1 1.3 Butanol 100 60 50 60 60 50 Xylene 20 100 100 90 80 60

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses an acrylic resin composition which has excellent scratch resistance and friction resistance. Particularly, the scheme adds polytetrafluoroethylene, which has chemical resistance, heat resistance and applicability to occasions with high frictional property requirements, into the traditional acrylic resin paint in the form of nano dimensions, and obtains the acrylic resin paint, which has improved properties and is suitable for industrialization, without changing the original paint processing technique.

Description

technical field [0001] The invention relates to an acrylic resin composition, in particular to a wear-resistant acrylic resin coating composition, which belongs to the field of polymer materials. Background technique [0002] The copolymers synthesized with vinyl monomers such as acrylate, methacrylate and styrene as the main raw materials are called acrylic resins. In terms of composition, acrylic resins include pure acrylic resins, styrene acrylic resins, silicone acrylic resins, Acrylic resin, fluoropropylene resin, tert-acrylic (tert-carbonate-acrylate) resin, etc. The coatings with acrylic resin as film-forming base material are called acrylic resin coatings. This type of coating has the advantages of light color, color retention, gloss retention, weather resistance, corrosion resistance and pollution resistance. It has been widely used in automobiles, aircrafts, machinery, electronics, etc. , furniture, construction, leather finishing, papermaking, printing and dyeing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D133/04C09D127/18C09D7/12
Inventor 杨赢偲
Owner SUZHOU TAIZHENG CHEM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com