Modified asphalt composition with creeping characteristic and preparation method thereof

A technology of modified asphalt and creep characteristics, which is applied to building structures, building components, building insulation materials, etc., can solve problems such as difficulty in finding the source of leakage, difficulty in repair work, water channeling, etc., to prolong service life, The effect of improving reliability and good fluidity

Inactive Publication Date: 2011-04-20
ZHEJIANG WOPUMAN HIGH NEW MATERIALS
View PDF6 Cites 59 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But another problem has arisen from this, that is, once the waterproof layer produces small holes or cracks in a certain part and leaks water, there will be water channeling under the waterproof layer, resulting in multiple leaks in the room, and it is difficult to find the leak. The source of the leakage brings great difficulty to the repair work

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified asphalt composition with creeping characteristic and preparation method thereof
  • Modified asphalt composition with creeping characteristic and preparation method thereof
  • Modified asphalt composition with creeping characteristic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The various raw material ratios of the present embodiment are as follows:

[0033] Table 1

[0034] name

Proportion

Specification

Softener (low volatile aromatic oil)

24

Modified material (SBS)

5

Modified material (PP)

1

asphalt

25.3

Inorganic powder (stone powder)

22

120 mesh

rubber powder

10

80 mesh

Viscosity modifier (rosin resin)

4

Viscosity modifier (paraffin)

1

Viscosity modifier (terpene resin)

1

Asbestos wool

6

Peptizer (sodium pyrophosphate)

0.5

Peptizer (maleic anhydride)

0.08

[0035] Coupling agent (aluminate)

0.12

[0036] The asphalt in Table 1 is made by mixing 100# and 10# petroleum asphalt at a ratio of 5:1, and the softening point and ductility of the asphalt are adjusted.

[0037] According to the raw material pro...

Embodiment 2

[0043] The various raw material ratios of the present embodiment are as follows:

[0044] Table 2

[0045] name

Proportion

Specification

Softener (low volatility paraffin oil)

28

Modified material (SBS)

4

asphalt

20

Inorganic powder (stone powder)

27.3

200 mesh

rubber powder

10

80 mesh

Viscosity modifier (rosin resin)

4

Viscosity modifier (paraffin)

1

Viscosity modifier (terpene resin)

1

Asbestos wool

4

Peptizer (sodium pyrophosphate)

0.5

[0046] Coupling agent (silane coupling agent)

0.2

[0047] The asphalt in Table 2 is made by mixing 100# and 10# petroleum asphalt at a ratio of 4:1, and the softening point and ductility of the asphalt are adjusted.

[0048] According to the ratio of raw materials in Table 2, the production is carried out, and the specific steps are ...

Embodiment 3

[0059] The various raw material ratios of the present embodiment are as follows:

[0060] Table 6

[0061] name

Proportion

Specification

[0062] Softener (low volatility naphthenic oil)

15

Modified material (SEBS)

12

asphalt

40

Inorganic powder (talc powder)

40

230 mesh

rubber powder

30

50 mesh

Viscosity modifier (microcrystalline wax)

2

Viscosity modifier (polyethylene wax)

1

Viscosity modifier (polypropylene wax)

1

Asbestos wool

6

Peptizer (sodium pyrophosphate)

0.2

Peptizer (maleic anhydride)

0.1

Coupling agent (chromium complex)

0.8

[0063] The asphalt in Table 6 is made by mixing 100# and 10# petroleum asphalt at a ratio of 4.2:1, and the softening point and ductility of the asphalt are adjusted.

[0064] According to the ratio of raw materials in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a modified asphalt composition with a creeping characteristic, which comprises the following components in parts by weight: 15-60 parts of asphalt, 3-15 parts of modifying material, 5-30 parts of rubber powder, 15-60 parts of softening agent, 15-60 parts of inorganic powder, 3-25 parts of viscosity regulating agent, 0.3-1.5 parts of peptizing agent and 0.1-2 parts of coupling agent. A preparation method of the modified asphalt composition comprises the following steps of: adding the softening agent into a reaction kettle, heating to 170 to 200 DEG C, adding the modifying material, agitating, adding the asphalt and the rubber powder, and agitating for 1-2 h to obtain an intermediate raw material; levigating the intermediate raw material to 150-250 meshes, and putting back to the reaction kettle; and finally, adding the inorganic powder, the viscosity regulating agent, the peptizing agent and the coupling agent into the reaction kettle, agitating and dispersing uniformly. The modified asphalt composition has the characteristics of excellent water-proof performance, strong binding capability and continuous binding capability, large elongation percentage and good low-temperature flexibility.

Description

technical field [0001] The invention relates to a modified asphalt composition with creep properties and a preparation method thereof, belonging to the technical field of chemical industry. Background technique [0002] Asphalt is an excellent basic building material with a series of advantages such as impervious, non-absorbent, non-conductive, corrosion-resistant, good adhesion and impact resistance. It is also the leftovers after petroleum refining, and it is cheap, and has the functions of bonding, waterproofing and anticorrosion. As construction materials and raw materials, it is widely used in various industries such as transportation (roads, railways, aviation, etc.), construction, agriculture, water conservancy projects, industry (extraction industry, manufacturing industry), and civil use. Disadvantages of asphalt are temperature sensitivity and climatic instability. After decades of polymer modification, the performance of asphalt has been greatly improved, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08L21/00C08L53/02C08L9/06C08L23/08C08L31/04C08L23/12C08K13/02
Inventor 张文华项桦太梁才
Owner ZHEJIANG WOPUMAN HIGH NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap