Aluminum pulp composition of crystal silicon solar cell and preparation method thereof
A technology of solar cells and crystalline silicon, which is applied in circuits, electrical components, semiconductor devices, etc., can solve the problem that the photoelectric conversion efficiency cannot meet the requirements of solar cell development, reduce the cost of aluminum paste for crystalline silicon solar cells, and single crystal silicon solar cell silicon High sheet warpage and other problems, to achieve the effect of easy quality control, strong bonding, and improved rheological properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] 1. Preparation of organic vehicle
[0025] According to mass percentage, ethyl cellulose EK-100 5.0%, epoxy resin 2.0%, castor oil 5%, ethylene glycol phenyl ether 2%, dibutyl phthalate 15%, lecithin 1.0%, furoic acid 0.5%, stearic acid 2.0%, diethyl phthalate 2.5%, terpineol 60%, turpentine 5%, the total amount is 100%; the above substances are mixed and heated in a stainless steel container at 75-96°C in a water bath until the solid resin is completely dissolved to obtain a clear, transparent and uniform organic vehicle.
[0026] 2. Preparation of lead-free glass adhesive powder
[0027] According to mass percentage, it is composed of 16% boron trioxide, 19% silicon dioxide, 32% barium oxide, 18% aluminum oxide and 15% calcium oxide, the total amount is 100%; plus 1% vanadium pentoxide , mix evenly with a double-roller ball mill, put it into a quartz crucible, put it into a program-controlled glass melting furnace, heat it to 1220°C, keep it warm and melt for 1.5h, ...
Embodiment 2
[0036] 1. Preparation of organic vehicle
[0037] According to mass percentage, ethyl cellulose EK-100 5.0%, epoxy resin 2.0%, castor oil 5%, ethylene glycol phenyl ether 1.0%, dibutyl phthalate 18.5%, lecithin 1.0%, o-phthalate Diethyl diformate 2.5%, terpineol 60%, turpentine 5%, the total amount is 100%; the above substances are mixed and heated in a water bath at 75-96°C in a stainless steel container until the solid resin is completely dissolved and a clear and transparent Uniform organic carrier.
[0038] 2. Preparation of lead-free glass adhesive powder
[0039] According to mass percentage, it is composed of 18% boron trioxide, 17% silicon dioxide, 34% barium oxide, 16% aluminum oxide and 15% calcium oxide, the total amount is 100%; plus 2% vanadium pentoxide , melting method is the same as embodiment 1;
[0040] 3, metal aluminum powder: specification is the same as embodiment 1;
[0041] 4. Metal or non-metal powder additive: boron powder with an average particle...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
bulk density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com