A corundum refractory ball for a ball-type hot blast stove and its preparation method

A technology of corundum and refractory balls, which is applied in the direction of brick blast furnaces, etc., can solve the problems of short ball replacement cycle, low strength of magnesium-aluminum balls, poor chemical corrosion resistance, etc., and achieve favorable high-temperature performance, high normal temperature compressive strength, The effect of high softening temperature under load

Inactive Publication Date: 2011-12-07
巩义市金岭耐火材料有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, magnesium-aluminum balls and high-alumina balls have been mostly used in the high-temperature and medium-temperature sections of large and medium-sized blast furnace ball-type hot blast stoves. Although magnesium-aluminum balls have the advantages of high density, high heat capacity, strong heat storage capacity, and good alkali resistance, However, magnesium aluminum balls have low strength, poor thermal shock resistance, easy hydration damage during use, are not suitable for acid slag erosion, and have a low service life.
The high alumina ball has low strength, low density, poor chemical corrosion resistance, and is easy to deform and block the gas passage during use, so that the ball replacement cycle is short, which cannot meet the use of large and medium-sized ball hot blast stoves.
In order to adapt to the large-scale technology of the ball hot blast furnace and solve the problem of low life of the pebble bed, it is imperative to develop new material refractory balls

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A corundum refractory ball for a ball-type hot blast stove and its preparation method
  • A corundum refractory ball for a ball-type hot blast stove and its preparation method
  • A corundum refractory ball for a ball-type hot blast stove and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030]a. Weigh α-Al with a particle size of less than 0.2 mm according to the raw materials, specifications, and weight percentages corresponding to Example 1 in Attached Table 2 2 o 3 Granules, zirconia-containing materials with a particle size of less than 0.044mm, and additives with a particle size of less than 0.088mm (either fused magnesia or lightly burned magnesia powder or a combination of the two), are prepared by dry co-milling into a particle size of all Fine powder less than 0.02mm (500 mesh) (the inner lining of the ball mill adopted in the method of joint mixing and grinding is a corundum ceramic grinding lining brick, and the ceramic grinding medium ball is a corundum ceramic grinding medium ball or a zirconia ceramic grinding medium Balls, including corundum ceramic grinding lining bricks and corundum ceramic grinding media balls Al 2 o 3 The content of ≥95%, zirconia ceramic grinding media ball ZrO 2 The content of ≥94%. ), spare;

[0031] b. High alumina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

A corundum refractory ball for a spherical hot blast stove and a preparation method thereof, characterized in that: the corundum refractory ball includes the following main ingredients, binders and additives; wherein the main ingredients include the following raw materials in weight percentages: 0-15% of corundum with a particle size of 5-3mm, 30-60% of corundum with a particle size of 3-1mm, 5-30% of corundum with a particle size of 1-0.088mm, 0-10% of corundum with a particle size of less than 0.044mm, and 0-10% of corundum with a particle size of less than 0.088mm High alumina bauxite clinker 10-25%, α-Al2O3 particles 2-10%, zirconia-containing material 1-10%, clay 2-8%, mullite or mullite-containing main phase material 2-10% %; the added amount of the binder is 1-6% of the weight of the main material; the added amount of the additive is 0-1% of the weight of the main material. The preparation method of the present invention adopts trapping, back-rolling, machine-pressing, drying the green body, and then firing in a tunnel kiln at a firing temperature of 1450°C to 1600°C.

Description

technical field [0001] The invention relates to the technical field of refractory material production, in particular to a corundum refractory ball for a ball-type hot blast stove and a preparation method thereof. The corundum refractory ball can be used in the high-temperature section and the medium-temperature section of the large and medium-sized blast furnace ball-type hot blast stove. technical background [0002] At present, the spherical hot blast stove is replacing the traditional hot blast stove with its advantages of small footprint, high thermal efficiency and low investment. In order to improve the stability of large and medium-sized ball hot blast stoves and increase their wind temperature, high-quality refractory balls are needed to support them. So far, magnesium-aluminum balls and high-alumina balls have been mostly used in the high-temperature and medium-temperature sections of large and medium-sized blast furnace ball-type hot blast stoves. Although magnesi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66C04B35/622C21B9/06
Inventor 刘永春刘永升宋继昌潘之雄
Owner 巩义市金岭耐火材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com