Weather-resistant epoxy polyurethane anticorrosive paint and preparation thereof

A technology of epoxy polyurethane and anti-corrosion coatings, which is applied in the direction of polyurea/polyurethane coatings, anti-corrosion coatings, polyester coatings, etc. It can solve the problems that outdoor steel cannot be used for anti-corrosion, poor light aging resistance, and easy yellowing of the paint film. Achieve excellent adhesion, low price, and excellent salt spray resistance

Inactive Publication Date: 2008-11-05
TIANJIN BO XING ENG SCI & TECH LIMITED COMPANY OF CNPC +1
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing epoxy polyurethane anti-corrosion coatings are generally used for internal anti-corrosion of storage tanks, pipelines, etc., and have good acid, alkali, and salt corrosion resistance. The disadvantages are that the paint film is prone to yellowing, poor weather resistance, and poor light aging resistance. , can not be used for corrosion protection of outdoor steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The invention discloses a method for manufacturing the weather-resistant epoxy polyurethane anticorrosion paint. In the stainless steel barrel, first add 1 part by weight of E-06 bisphenol A type epoxy resin, 0.3 part by weight of bisphenol F type epoxy resin, 0.4 part by weight of 3094 hydroxyl-containing saturated polyester resin, 0.2 part by weight of fluorine Add the carbon resin to a mixed solvent of 0.5 parts by weight of xylene, 0.4 parts by weight of n-butyl acetate, 0.12 parts by weight of methyl isobutyl ketone, and 0.08 parts by weight of methyl ethyl ketone to be dispersed and dissolved. After stirring at a high speed, add 0.15 parts by weight of rutile titanium dioxide, 0.15 parts by weight of talcum powder, 0.12 parts by weight of sericite powder, 0.015 parts by weight of polyacrylate copolymer, 0.011 parts of polymethylalkylsiloxane, 0.02 parts by weight of phenylacrylic triazole, 0.008 Parts by weight of zinc isooctanoate, 0.01 parts by weight of fumed s...

Embodiment 2

[0016] The invention discloses a method for manufacturing the weather-resistant epoxy polyurethane anticorrosion paint. In the stainless steel barrel, first add 1 part by weight of E-06 bisphenol A type epoxy resin, 0.3 part by weight of bisphenol F type epoxy resin, 0.4 part by weight of hydroxyl-containing saturated polyester resin, 0.2 part by weight of fluorocarbon resin Add 0.5 parts by weight of xylene, 0.4 parts by weight of n-butyl acetate, 0.05 parts by weight of methyl isobutyl ketone, and 0.1 parts by weight of methyl ethyl ketone to disperse and dissolve. After stirring at a high speed, add 0.12 parts by weight of Parts of rutile titanium dioxide, 0.11 parts by weight of talcum powder, 0.2 parts by weight of sericite powder, 0.012 parts by weight of polyacrylate interpolymer, 0.013 parts by weight of polymethylalkylsiloxane, 0.03 parts by weight of benzotriazole, 0.02 parts by weight Parts by weight of zinc isooctanoate, 0.02 parts by weight of fumed silica, and th...

Embodiment 3

[0018] The invention discloses a method for manufacturing the weather-resistant epoxy polyurethane anticorrosion paint. In the stainless steel barrel, first add 1 weight part of bisphenol A type epoxy resin, 0.3 weight part of bisphenol F type epoxy resin, 0.4 weight part of hydroxyl-containing saturated polyester resin, and 0.2 weight part of fluorocarbon resin into 0.5 Parts by weight of xylene, 0.4 parts by weight of n-butyl acetate, 0.14 parts by weight of methyl isobutyl ketone, and 0.13 parts by weight of butanone are dispersed and dissolved in a mixed solvent. After high-speed stirring, add 0.2 parts by weight of rutile type Titanium dioxide, 0.18 parts by weight of talcum powder, 0.1 parts by weight of sericite powder, 0.015 parts by weight of polyacrylate copolymer, 0.026 parts by weight of polymethylalkylsiloxane, 0.07 parts by weight of benzotriazole, 0.035 parts by weight of iso Zinc octoate, 0.06 parts by weight of fumed silica, and then grind with a sand mill for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a weather resistant epoxy-polyurethane anti-corrosion coating and a manufacturing method thereof, which adds phenol-A epoxy resin, bisphenol-F epoxy resin, hydroxyl contained saturated polyester resin and fluorocarbon resin into the mixed solvent of dimethylbenzene, n-butyl acetate, methyl isobutyl ketone and butanone; then adds rutile type titanium pigment, saponite, sericite in powder, polyacrylate co-polymer, polymethyl alkyl siloxane, benzotriazole, gas phase silica and iso-caprylic acid znic to make the fluid A of the weather resistant epoxy-polyurethane anti-corrosion coating while adds fatty group polyisocyanate into the mixed liquor of anhydro-dimethylbenzene and the n-butyl acetate to make fluid B, and mix the two components during application. The invention can be applied to the preservation of the surfaces of outdoor steel structures, pipes and concrete requiring weather resistance, light aging resistance and acid, alkali and salt corrosion resistance.

Description

technical field [0001] The invention relates to a weather-resistant epoxy polyurethane anti-corrosion coating and a manufacturing method thereof, which are used for anti-corrosion of steel structures, pipelines and concrete surfaces that require weather resistance, light aging resistance and acid, alkali and salt corrosion resistance outdoors. Background technique [0002] The existing epoxy polyurethane anti-corrosion coatings are generally used for internal anti-corrosion of storage tanks, pipelines, etc., and have good acid, alkali, and salt corrosion resistance. The disadvantages are that the paint film is prone to yellowing, poor weather resistance, and poor light aging resistance. , cannot be used for corrosion protection of outdoor steel. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an epoxy polyurethane anti-corrosion coating with good weather resistance, good light aging resistance and corrosion resis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/02C09D5/08C09D175/00C09D167/00C09D133/08C09D183/04
Inventor 郭晓军杜建伟吕光明白晶贺江
Owner TIANJIN BO XING ENG SCI & TECH LIMITED COMPANY OF CNPC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com