Long fibre enhanced polypropylene/nylon composite material and preparation method thereof

A nylon composite material and polypropylene technology, applied in the field of polymer materials, can solve the problems of limited application, inability to obtain mechanical properties of long-fiber reinforced polypropylene/nylon composite materials, easy delamination, etc., and achieve the effect of excellent mechanical properties

Inactive Publication Date: 2008-06-04
SHANGHAI PRET COMPOSITES
View PDF1 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since polypropylene is non-polar and incompatible with highly polar nylon resins, it is prone to delamination when mixed, so this method cannot obtain long-fiber reinforced polypropylene / nylon composites with excellent mechanical properties, which limits application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Long fibre enhanced polypropylene/nylon composite material and preparation method thereof
  • Long fibre enhanced polypropylene/nylon composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Mix 59kg of homopolypropylene resin PP-1 and 1kg of maleic anhydride grafted polypropylene (PP-g-MAH), and use pultrusion to make a long glass fiber reinforced polypropylene composite resin with a glass fiber content of 40kg Masterbatch, the glass fibers are arranged parallel to each other along the length direction of the masterbatch particles, and the length is the same as that of the masterbatch particles, which is 6mm; the processing temperature is 210°C.

[0028] At the same time, 20kg of homopolypropylene resin PP-1, 10kg of maleic anhydride grafted polypropylene (PP-g-MAH) and 70kg of nylon 6 (PA6) were mixed, and melt kneaded and blended using a twin-screw extruder , to obtain polypropylene / nylon alloy diluted resin.

[0029] Then, 95kg of long glass fiber reinforced polypropylene masterbatch was blended with 5kg of polypropylene / nylon alloy diluted resin, and injection molded into a standard mechanical test sample for testing. The test results are shown in Tabl...

Embodiment 2

[0036] Mix 45kg of homopolypropylene resin PP-1 and 5kg of maleic anhydride grafted polypropylene (PP-g-MAH), and use the pultrusion process to make a long glass fiber reinforced polypropylene composite resin with a glass fiber content of 50kg Masterbatch, the glass fibers are arranged parallel to each other along the length direction of the masterbatch particles, and the length is the same as that of the masterbatch particles, which is 12mm; the processing temperature is 250°C.

[0037] At the same time, 20kg of homopolypropylene resin PP-1, 10kg of maleic anhydride grafted polypropylene (PP-g-MAH) and 70kg of nylon 66 (PA66) were mixed, and melt kneaded and blended using a twin-screw extruder. , to obtain polypropylene / nylon alloy diluted resin.

[0038] Then, 80kg of long glass fiber reinforced polypropylene masterbatch was blended with 20kg of polypropylene / nylon alloy diluted resin, and injection molded into a standard mechanical test sample for testing. The test results ...

Embodiment 3

[0040]Mix 40kg of homopolypropylene resin PP-1 and 5kg of maleic anhydride grafted polypropylene (PP-g-MAH), and use the pultrusion process to make a long glass fiber reinforced polypropylene composite resin with a glass fiber content of 50kg Masterbatch, the glass fibers are arranged parallel to each other along the length direction of the masterbatch particles, and the length is the same as that of the masterbatch particles, which is 12mm; the processing temperature is 250°C.

[0041] At the same time, 20kg of homopolypropylene resin PP-1, 10kg of maleic anhydride grafted polypropylene (PP-g-MAH) and 70kg of nylon 6 (PA6) were mixed, and melt kneaded and blended using a twin-screw extruder , to obtain polypropylene / nylon alloy diluted resin.

[0042] Then, 80kg of long glass fiber reinforced polypropylene masterbatch was blended with 20kg of polypropylene / nylon alloy diluted resin, and injection molded into a standard mechanical test sample for testing. The test results are ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a long-fiber strengthened polypropylene / nylon composite and the preparation method thereof. The composite is produced by mixing 5-95% (weight) of master batch of long-fiber strengthened polypropylene and 5-95% (weight) of polypropylene / nylon ally diluted resin. The long-fiber strengthened polypropylene / nylon composite of the invention has the advantages of excellent physic performance, color stability and manufacturing and processing stability, etc. At the same time, the invention has the advantages of simple control and low cost, etc.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a long fiber reinforced polypropylene / nylon composite material and a preparation method thereof. Background technique [0002] Long fiber reinforced thermoplastic resin is a reinforced thermoplastic resin in which the reinforcing fibers are arranged in one direction and the length is the same as that of the resin pellets. Compared with conventional short fiber reinforced thermoplastic resins, it has more excellent mechanical properties, dynamic fatigue resistance, creep resistance, etc.; especially the impact resistance of the material is extremely excellent. [0003] Polypropylene has the characteristics of light weight, low water absorption, good electrical insulation performance, good fluidity and easy molding, but the mechanical properties and heat resistance of long fiber reinforced polypropylene materials are far inferior to long fiber reinforced nylon resins; on the other ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L23/26C08L77/00C08J5/04C08K7/02
Inventor 陈永东李宏张祥福周文
Owner SHANGHAI PRET COMPOSITES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com