Water metal anti-corrosion paint and preparation method thereof

A metal anti-corrosion, water-based technology, used in anti-corrosion coatings, coatings, etc., can solve the problems of waste, the protective layer can not be durable, the adhesion is not very strong, etc., to achieve fast drying time, excellent salt spray resistance, construction process simple effect

Inactive Publication Date: 2008-03-26
山西天时涂料装饰有限公司
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main body of water-based metal anti-corrosion paint is an organic product, while the steel structure is an inorganic product. The adhesion between the inorganic product and the organic product is not very strong. Therefore, the current ordinary water-based metal anti-corrosion paint simply applies the paint to the steel structure. On the surface, the protective layer cannot last long, and the old paint film needs to be removed regularly, and the anti-corrosion paint should be repainted, so there is a lot of waste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] Add 2.5g of adipic dihydrazide into 180mL of deionized water, stir at a low speed of 600 rpm for 3 to 5 minutes to dissolve completely, then add 20g of propylene glycol, 6g of dispersant 5040, and 1.5g of defoamer DX- 48. 1g of preservative PROXEL-AQ and 1g of pH value stabilizer AMP-95, after stirring at low speed for 5-10 minutes, keep stirring, add 230g of 902 titanium dioxide, 100g of wollastonite powder and 50g of kaolin in sequence, and disperse at 1500 rpm for 60- 75min, the detection fineness is ≤45um, reduce the speed to 800 rpm, add 120g water-based fluorocarbon resin, 60g silicone emulsion, 200g pure acrylic emulsion and 20g film-forming aid TEXNOL in sequence, after each raw material is added, first Stir for 3 to 5 minutes, then add the next raw material. Finally, add 1.5g of wetting agent X-405, 1.5g of defoamer DX-48, and adjust the viscosity of the product with 3g of 2020 leveling thickener and appropriate amount of SCT-275 thickener. The adjustment speed...

Embodiment 2

[0073] Add 3g of adipic acid dihydrazide into 180mL of deionized water, stir at a low speed of 600 rpm for 3 to 5 minutes to dissolve completely, then add 25g of propylene glycol, 8g of dispersant 1124, and 2g of defoamer DX- 48. 2g preservative LEX and 0.5g pH value stabilizer AMP-95, stir at low speed for 5-10min, keep stirring, add 180g 902 titanium dioxide, 150g wollastonite powder, 50g kaolin and 60g phthalocyanine green slurry in turn, and then Disperse at a high speed of 60-75min at a speed of 1 / min, until there are no large particles, and the detection fineness is ≤45um, reduce the speed to 800 rpm, add 150g of water-based fluorocarbon resin, 50g of silicone emulsion, 180g of pure acrylic emulsion and 25g of film-forming Additive TEXNOL, after adding a raw material, it should be stirred for 3-5 minutes before adding the next raw material. Finally, add 1.5g of wetting agent X-405, 2g of defoamer DX-48, and mix 2g of WL-720 polyurethane rheology modifier and appropriate ...

Embodiment 3

[0076] Add 4.0g of adipic acid dihydrazide to 150mL of deionized water, stir at a low speed of 600 rpm for 3-5 minutes to dissolve completely, then add 20g of propylene glycol, 5g of dispersant 731A, and 2.5g of defoamer in sequence DX-46, 2g preservative PROXEL-XL2 and 1gpH value stabilizer AMP-95, stir at low speed for 5-10min, keep stirring, add 200g902 titanium dioxide, 80g wollastonite powder, 60g kaolin and 70g iron red slurry in sequence, and then add 1500 Disperse at high speed for 60 to 75 minutes at a speed of rev / min until there are no large particles and the detection fineness is ≤45um. Reduce the speed to 800 rev / min, add 160g of water-based fluorocarbon resin, 40g of silicone emulsion, 250g of pure acrylic emulsion, and 40g of synthetic Membrane additive lauryl alcohol ester, add one raw material and stir for 3 to 5 minutes before adding the next raw material. Finally, add 2g of wetting agent X-405, 2.5g of defoamer DX-46, mix 2g of 2020 leveling thickener and ap...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The water soluble anticorrosive paint for metal is prepared with deionized water, titanium white powder, wollastonite powder, kaolin, water soluble fluorocarbon resin, organosilicon emulsion, acrylate emulsion, hydrazyl adipate, film forming assistant and other materials, and through dispersing and mixing. The water soluble anticorrosive paint for metal has high weather resistance, high water resistance, high scrubbing resistance, good adhering performance, great adhesion, capacity of being painted onto rusty surface and wide application range. It may be applied for anticorrosive protection of iron and steel structure in building decoration, petrochemical, bridge, ship, container, etc.

Description

technical field [0001] The invention relates to a metal anti-corrosion paint, in particular to a water-based metal anti-corrosion paint used for anti-corrosion treatment of the surface of metal substrates. The invention also relates to a preparation method of the water-based anticorrosion paint. Background technique [0002] Metal is an indispensable and important engineering material for national economic development and national defense construction, especially steel occupies a larger proportion. However, metal materials are easily damaged by corrosion due to the chemical or electrochemical action of the environmental medium. Therefore, for a long time, people have been devoting themselves to using various technologies to protect metals and prevent corrosion. [0003] The most effective and commonly used metal anti-corrosion method is to coat the metal surface with an anti-corrosion coating to isolate the corrosive medium from the metal substrate. [0004] Most of the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/00C09D5/08C09D127/12C09D183/04
Inventor 姚红星刘爱虎
Owner 山西天时涂料装饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap