Thermoplastic elastomer for filming dacron cloth

A thermoplastic elastomer and cloth technology, applied in textiles and papermaking, can solve the problems of low peel strength and hard hand feeling, and achieve high peel strength, soft and comfortable feel, and good acid and alkali resistance

Inactive Publication Date: 2007-03-21
CGN JUNER NEW MATERIALS
View PDF0 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the thermoplastic elastomer based on SBS is currently used for coating with polyester materials, it has the disadvantages of low peel strength and slightly hard hand feeling. Adhesive properties of thermoplastic elastomer materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Thoroughly mix the base resin and filler oil evenly. After the filler oil is completely absorbed by the resin, add tackifiers, mineral fillers, coupling agents, processing aids, composite light stabilizers and other components in the following proportions by weight: Mix well in a mixer. The mixed materials are sent into the twin-screw extruder by the feeder, the temperature of the twin-screw extruder is set at 220°C, the feeding frequency is 20 Hz, and the speed of the main engine is 25 Hz. Raw materials are sheared and mixed at high speed by twin-screws, extruded by the machine head, drawn, air-cooled, pelletized, dried and packaged.

[0028] SBS (Baling Petrochemical) YH 792: 100 copies

[0029] Extender oil (PW-90): 50 parts

[0030] Tackifier (SEBS-maleic anhydride graft): 150 parts

[0031] Mineral filler (talc): 50 parts

[0032] Coupling agent (KH-550): 1 part

[0033] Processing aid (stearic acid): 5 parts

[0034] Composite stabilizer (UV-531): 5 parts

...

Embodiment 2

[0037] A thermoplastic elastomer was prepared according to the process in Example 1 and the following proportions by weight.

[0038] SBS (Baling Petrochemical) YH 788: 100 copies

[0039] Extender oil (PW-90): 250 parts

[0040] Tackifier (EPDM rubber-maleic anhydride graft): 150 parts

[0041] Mineral filler (talc): 50 parts

[0042] Coupling agent (KH-550): 4 parts

[0043] Processing aid (calcium stearate): 5 parts

[0044] Composite stabilizer (UV-531): 5 parts

Embodiment 3

[0046]A thermoplastic elastomer was prepared according to the process in Example 1 and the following proportions by weight.

[0047] SBS (Baling Petrochemical) 4202: 100 copies

[0048] Extender oil (PW-90): 50 parts

[0049] Tackifier (polyethylene oxide-maleic anhydride graft): 150 parts

[0050] Mineral filler (mica powder): 50 parts

[0051] Coupling agent (KR-TTS): 2 parts

[0052] Processing aid (zinc stearate): 1 part

[0053] Composite stabilizer (Irganox1076): 1 part

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The thermoplastic elastomer for filming Dacron cloth used as box lining, sportswear lining, etc. consists of matrix resin 10-80 wt%, filler oil 0-60 wt%, tackifier 5-50 wt%, mineral filler 0-25 wt%, coupling agent 0.1-0.8 wt%, machining assistant 0.1-2 wt%, and composite stabilizer 0.1-2 wt%. By means of the improved recipe and preparation process, the present invention solves the problem of adhering non-polar matrix with Dacron or other polar chemical fiber fabric, so that the film on the Dacron material has high peeling strength, soft and comfortable handing, high weather resistance, and high acid and alkali resistance and other advantages.

Description

technology field. [0001] The invention relates to the field of polymer materials, in particular to a thermoplastic elastomer coated with polyester, mainly coated with commonly used chemical fiber cloth such as polyester to be used as a lining material for luggage and sports clothes. Background technique [0002] For the coating process of cloth, the polymer materials currently used mainly include polyethylene (PE), polyvinyl chloride (PVC), polyvinyl acetate (EVA), polyurethane (TPU) and the like. Polyethylene material has the advantages of low price, good weather resistance and thermal stability, but it has poor hand feeling, so it is rarely used at present. Polyvinyl chloride material has been widely used in the production of artificial leather, but PVC has poor weather resistance, especially low temperature performance. At the same time, the use of plasticizers and other components in PVC materials and formula systems does not meet the current consumption concepts of non...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08K5/24D06N3/04C08L51/00C08K3/00C08K5/00
Inventor 宋克东
Owner CGN JUNER NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap