Casting method of metal substrate cooling wall

A metal matrix and cooling wall technology, applied in cooling devices, casting and forming equipment, metal processing equipment, etc., can solve the problems of easy deformation and melt-through of cooling pipes, reduce overhaul costs, eliminate thermal resistance, and improve blast furnace life. Effect

Inactive Publication Date: 2004-07-21
MAANSHAN IRON & STEEL CO LTD
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a method for producing cast steel staves and other cast steel staves with a high melting point of the metal matrix, so as to overcome the disadvantages of easy deformation and melting of cooling pipes in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Casting method of metal substrate cooling wall
  • Casting method of metal substrate cooling wall
  • Casting method of metal substrate cooling wall

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 4-8

[0014] Get embodiment 4-8 and pour cast steel cooling stave by following casting pouring process:

[0015] The pouring process is as follows: firstly make the wooden mold, and at the same time, according to the design requirements, 20 # The low-carbon steel hot-rolled seamless steel pipe is cold-bent to form a serpentine cooling water pipe, which is sandblasted and derusted. After being assembled into a whole, the box is then filled. The cooling water pipe is filled with cooling medium. # The low-carbon steel molten steel is poured and formed, and the sand is cleaned after completion, and finally heat-treated.

[0016] In the above process, if figure 2 The open gating system 7 with bottom injection is shown in the figure. The gate of the gating system 7 is placed between the cooling water pipes 1 to prevent the high-temperature molten steel from directly rinsing the cooling water pipe 1. An insulation riser 6 is provided at the opposite end of the gate. The thermal insulati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
Login to View More

Abstract

A technology for casting the steel-based cooling wall features that the cooling medium which is the mixture of corundum powder, iron powder and electrode powder is filled in its cooling pipeline. Said cooling medium features strong cooling action, low thermal expansibility, not adhering to pipe wall, and easy removing it.

Description

Technical field: [0001] The technical solution to be protected by the present invention belongs to the technical field of casting technology, specifically, it is a casting method of stave with high melting point metal steel as the matrix. Background technique: [0002] Cooling walls are widely used in steelmaking blast furnaces, launders and other equipment. Compared with the currently widely used nodular cast iron stave, the cast steel stave, as a new generation of blast furnace stave, has the advantages of high elongation, high tensile strength, high melting point, thermal shock resistance and good overall thermal conductivity. The base body of the steel stave is integrated with the cooling pipe, which eliminates the gap between the base body and the cooling pipe in the ductile iron stave, reduces thermal resistance, and thus improves the service life of the blast furnace. The base material of the cast steel stave is low-carbon alloy steel with a high melting point. Gener...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C9/24B22D19/08C21B7/10
Inventor 朱童斌李小静苏允隆何云石玮王黎明
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com