Stainless steel roll-grinding hot-pasting laser cutting protective film and preparation process thereof

A laser cutting, stainless steel technology, applied in the direction of film/sheet adhesive, adhesive type, ester copolymer adhesive, etc., to solve focusing and reflection problems, strong cohesive strength and stability, initial good sticky effect

Inactive Publication Date: 2021-11-02
海阳市凌晖包装有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the laser cutting protective film for stainless steel plate in my country's domestic market mainly relies on imported products, which are mainly monopolized by France's Novasell, Germany's Polyfim and Japan's Nitto, especially the stainless steel coil grinding wire has a fast drawing speed. High efficiency, the temperature of the stainless steel film is about 50 degrees, the technical requirements for the protective film are extremely high, and there is an urgent need for a protective film that can solve the focusing and reflection problems of fiber laser cutting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stainless steel roll-grinding hot-pasting laser cutting protective film and preparation process thereof
  • Stainless steel roll-grinding hot-pasting laser cutting protective film and preparation process thereof
  • Stainless steel roll-grinding hot-pasting laser cutting protective film and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A protective film for laser cutting of stainless steel coils, made of the following raw materials according to weight percentage: 30% low-density polyethylene, 40% linear polyethylene, 10% metallocene, 10% high-density polyethylene, special coloring masterbatch Granules 10%.

[0022] The glue is made of the following raw materials according to weight percentage: 4% acrylic acid, 25% butyl acrylate, 50% isooctyl acrylate, 11% vinyl acetate, 5% methyl methacrylate, and 5% hydroxyethyl acrylate.

[0023] A kind of preparation technology of stainless steel roll grinding thermal paste laser cutting protective film comprises the following steps:

[0024] (1) Substrate preparation: mix 30% low-density polyethylene, 40% linear polyethylene, 10% metallocene, 10% high-density polyethylene, and 10% special coloring masterbatch, and use melt co-extrusion blow molding Process to make the base material, the temperature of the main engine of the blow molding unit is 160 degrees, the ...

Embodiment 2

[0033] A protective film for laser cutting of stainless steel coils, made of the following raw materials according to weight percentage: 30% low-density polyethylene, 40% linear polyethylene, 10% metallocene, 10% high-density polyethylene, special coloring masterbatch Granules 10%.

[0034] The glue is made of the following raw materials according to weight percentage: 4% acrylic acid, 25% butyl acrylate, 50% isooctyl acrylate, 11% vinyl acetate, 5% methyl methacrylate, and 5% hydroxyethyl acrylate.

[0035] A kind of preparation technology of stainless steel roll grinding thermal paste laser cutting protective film comprises the following steps:

[0036] (1) Substrate preparation: mix 30% low-density polyethylene, 40% linear polyethylene, 10% metallocene, 10% high-density polyethylene, and 10% special coloring masterbatch, and use melt co-extrusion blow molding Process to make the base material, the main machine temperature of the blow molding unit is 190 degrees, the die te...

Embodiment 3

[0045] A protective film for laser cutting of stainless steel coils, made of the following raw materials according to weight percentage: 35% low-density polyethylene, 38% linear polyethylene, 10% metallocene, 7% high-density polyethylene, special coloring masterbatch Granules 10%.

[0046] The glue is made of the following raw materials according to weight percentage: 4% acrylic acid, 25% butyl acrylate, 50% isooctyl acrylate, 11% vinyl acetate, 5% methyl methacrylate, and 5% hydroxyethyl acrylate.

[0047] A kind of preparation technology of stainless steel roll grinding thermal paste laser cutting protective film comprises the following steps:

[0048] (1) Substrate preparation: mix 34% low-density polyethylene, 38% linear polyethylene, 10% metallocene, 7% high-density polyethylene, and 10% special coloring masterbatch, and use melt co-extrusion blow molding Process to make the base material, the temperature of the main machine of the blow molding unit is 175 degrees, the tem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of laser cutting protective films, and discloses a stainless steel roll-grinding hot-pasting laser cutting protective film which is prepared from the following raw materials in percentage by weight: 30%-40% of low-density polyethylene, 35%-40% of linear polyethylene, 10% of metallocene, 5%-10% of high-density polyethylene and 10% of special coloring master batch. The glue is prepared from the following raw materials in percentage by weight: 4% of acrylic acid, 25% of butyl acrylate, 50% of 2-ethylhexyl acrylate, 11% of vinyl acetate, 5% of methyl methacrylate and 5% of hydroxyethyl acrylate, and the preparation process comprises the following steps: (1) producing a PE base material in a blow molding manner;, (2) producing the glue; (3) coating in a net wire roller transfer coating manner; (4) carrying out high-temperature curing in a curing chamber for 48 hours; and (5) cutting. The problems of focusing and reflection in fiber laser cutting can be solved, the technology that a stainless steel plate is thermally pasted with a fiber laser cutting protective film is broken through, the actual application requirement can be met, and the application range is wide.

Description

technical field [0001] The invention belongs to the technical field of laser cutting protective films, and in particular relates to a laser cutting protective film for stainless steel roll grinding and thermal paste and a preparation process thereof. Background technique [0002] At present, the laser cutting protective film for stainless steel plate in my country's domestic market mainly relies on imported products, which are mainly monopolized by France's Novasell, Germany's Polyfim and Japan's Nitto, especially the stainless steel coil grinding wire has a fast drawing speed. The efficiency is high, and the temperature of the stainless steel film is about 50 degrees. The technical requirements for the protective film are extremely high. There is an urgent need for a protective film that can solve the focusing and reflection problems of fiber laser cutting. Contents of the invention [0003] In order to solve the technical problems existing in the prior art, the present in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/24C09J7/30C09J133/08C08L23/06
Inventor 孙强云黄自军高晓梅邓迎春
Owner 海阳市凌晖包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com