Preparation and application of an ultra-long cycle polyatomic doped hollow carbon electrode material

A multi-atom and carbon electrode technology, which is applied in the preparation/purification of carbon, battery electrodes, circuits, etc., can solve the problems affecting the performance of potassium ion batteries, unfavorable potassium ion adsorption, and small specific surface area, so as to achieve abundant defects and active sites point, improved rate performance and cycle stability, and the effect of large specific surface area

Active Publication Date: 2022-04-19
JINAN UNIVERSITY
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent publication CN112079346A discloses a double-shell hollow spherical organometallic framework material and its preparation method. Using sulfonated polystyrene beads as a template, a new nano-spherical organometallic framework compound HS-ZIF was synthesized by a hard template method -8, the material has a double-shell shell structure, but its particle size is too large, which affects the performance of the potassium ion battery
The material has a hollow cubic structure, but the specific surface area is relatively small, which is not conducive to the adsorption of potassium ions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation and application of an ultra-long cycle polyatomic doped hollow carbon electrode material
  • Preparation and application of an ultra-long cycle polyatomic doped hollow carbon electrode material
  • Preparation and application of an ultra-long cycle polyatomic doped hollow carbon electrode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Step 1: Disperse 400 mg of nano magnesium oxide with a particle size of 50 nm in 50 ml of methanol.

[0035] Step 2: Dissolve hexachlorotriphosphazene and 4,4'-dihydroxydiphenylsulfone with a total mass of 228mg and a molar ratio of 1:2.25 in 10ml of methanol.

[0036] Step 3: Add the solution in Step 2 to the solution in Step 1, add 185 μL of triethylamine during stirring, and keep polymerization at room temperature for 6 hours.

[0037] Step 4: The product obtained in Step 3 was centrifuged, washed and dried, and then placed in a tube furnace for heat treatment. In a nitrogen atmosphere, the temperature was raised from room temperature to 900 °C at a heating rate of 2 °C / min, and kept for 2 hours to fully Calcination, after the calcination is completed, a calcined product is obtained.

[0038] Step 5: Remove the magnesium oxide template from the calcined product obtained in Step 4 with 3 mol / L hydrochloric acid to obtain nitrogen, phosphorus, and sulfur-doped hollow ...

Embodiment 2

[0040] Step 1: Disperse 400 mg of nano magnesium oxide with a particle size of 100 nm in 50 ml of methanol.

[0041] Step two to step five are consistent with embodiment 1.

Embodiment 3

[0043] Steps 1 to 3 are consistent with Example 1.

[0044] Step 4: The product obtained in Step 3 was centrifuged, washed and dried, then placed in a tube furnace for heat treatment, and heated from room temperature to 700°C in a nitrogen atmosphere at a heating rate of 2°C / min, and kept for 2 hours for full Calcination, after the calcination is completed, a calcined product is obtained.

[0045] Step 5 is consistent with Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of potassium ion batteries, and discloses a preparation method and application of an ultra-long cycle polyatom-doped hollow carbon electrode material. The invention adopts magnesium oxide particles, hexachlorocyclotripolyphosphazene and dihydroxydiphenylsulfone to prepare magnesium oxide-polycyclotriphosphazene-dihydroxydiphenylsulfone composite material, and after calcining and removing magnesium oxide template, nitrogen and phosphorus are obtained Sulfur polyatom co-doped hollow carbon, that is, ultra-long cycle polyatom-doped hollow carbon electrode material. The synthesis method of the ultra-long-cycle polyatom-doped hollow carbon electrode material is simple, the specific surface area is large, and it has a cross-linked structure and abundant defects and active sites. Rate capability and cycling stability.

Description

technical field [0001] The invention belongs to the field of potassium ion batteries, in particular to a preparation method and application of an ultra-long cycle polyatom doped hollow carbon electrode material. Background technique [0002] Due to the non-renewability of fossil fuel energy and the pollution of the environment caused by the emission of chemical gases, the demand for new green and environmentally friendly energy continues to rise along with the rapid development of the economy and society. As the carrier of new energy, large-scale energy storage equipment is of great significance to its development. Lithium-ion batteries have been commercially used in energy devices, but the lack of lithium resources and lack of excellent battery performance are the bottlenecks that limit the development of potassium-ion batteries. Potassium ion battery is a strong candidate, with its rich potassium resources and standard redox potential close to that of lithium, it can be e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/587H01M10/054C01B32/05
CPCH01M4/587H01M10/054C01B32/05Y02E60/10
Inventor 李宏岩刘喜孙影娟
Owner JINAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com