Attapulgite-based acid soil conditioner and preparation method thereof

A technology of soil conditioner and attapulgite, which is applied in the field of attapulgite acidic soil conditioner and its preparation, and can solve problems such as environmental pollution, energy consumption, and increased cost of soil improvement

Active Publication Date: 2021-10-01
白银丰宝农化科技有限公司 +2
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, quicklime is easy to cause soil compaction and destroy the soil ecological balance
Moreover, in the process of acidic soil improvement, the application amount of acidic soil conditioner per mu often exceeds 100 kilograms, so a large amount of natural limestone resources or other organic matter improvers need to be mined and calcined, which will undoubtedly greatly increase the cost of soil improvement. At the same time, it will also cause new environmental pollution and energy consumption.
[0005] Patent application CN106433650A discloses an acidic soil conditioner, which is made of dolomite, potassium feldspar, quicklime, lime nitrogen, limestone powder, slaked lime, calcium magnesium phosphate fertilizer, boron mud, carbonated lime and diatomaceous earth, etc. However, its application rate is high, and the improvement of soil pH is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Attapulgite-based acid soil conditioner and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A preparation method of attapulgite-based acidic soil conditioner, the specific steps are as follows:

[0030] (1) First use urea, ferric chloride hexahydrate and succinic acid as raw materials to make doped graphite phase carbon nitride, and then add doped graphite phase carbon nitride to the mixed aqueous solution of sodium molybdate-thioacetamide, Hydrothermal reaction to obtain doped graphite phase carbon nitride-molybdenum disulfide composite;

[0031] (2) 1 kg of fresh Enteromorpha pulverized and added to 60 kg of water, beaten to obtain Enteromorpha pulp, heated and pressurized to obtain pretreated Enteromorpha pulp;

[0032] (3) Finally, add 55kg attapulgite, 2kg soda lime and 0.05kg doped graphite phase carbon nitride-molybdenum dioxide compound to the pretreated Enteromorpha pulp, dipping treatment, and drying to obtain the conditioner .

[0033] In step (1), the preparation method of carbon nitride doped with graphite phase is as follows: First, 10 kg of ur...

Embodiment 2

[0043] A preparation method of attapulgite-based acidic soil conditioner, the specific steps are as follows:

[0044] (1) First use urea, ferric chloride hexahydrate and succinic acid as raw materials to make doped graphite phase carbon nitride, and then add doped graphite phase carbon nitride to the mixed aqueous solution of sodium molybdate-thioacetamide, Hydrothermal reaction to obtain doped graphite phase carbon nitride-molybdenum disulfide composite;

[0045] (2) 1 kg of fresh Enteromorpha pulverized and added to 70 kg of water, beaten to obtain Enteromorpha pulp, heated and pressurized to obtain pretreated Enteromorpha pulp;

[0046] (3) Finally, add 45kg attapulgite, 3kg soda lime and 0.03kg doped graphite phase carbon nitride-molybdenum dioxide compound to the pretreated Enteromorpha pulp, dipping treatment, and drying to obtain the conditioner .

[0047] In step (1), the preparation method of carbon nitride doped with graphite phase is as follows: First, 10 kg of ur...

Embodiment 3

[0057] A preparation method of attapulgite-based acidic soil conditioner, the specific steps are as follows:

[0058] (1) First use urea, ferric chloride hexahydrate and succinic acid as raw materials to make doped graphite phase carbon nitride, and then add doped graphite phase carbon nitride to the mixed aqueous solution of sodium molybdate-thioacetamide, Hydrothermal reaction to obtain doped graphite phase carbon nitride-molybdenum disulfide composite;

[0059] (2) Add 1 kg of fresh Enteromorpha into 65 kg of water after pulverization, beating to obtain Enteromorpha pulp, heat and pressurize to obtain pretreated Enteromorpha pulp;

[0060] (3) Finally, add 50kg attapulgite, 2.5kg soda lime and 0.04kg doped graphite phase carbon nitride-molybdenum dioxide compound to the pretreated Enteromorpha pulp, dipping treatment, drying, and obtain the conditioning agent.

[0061] In step (1), the preparation method of carbon nitride doped with graphite phase is as follows: First, 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an attapulgite-based acidic soil conditioner and a preparation method thereof. Attapulgite and soda lime are used as main raw materials, enteromorpha and a doped graphite phase carbon nitride-molybdenum dioxide compound are used as auxiliary materials, the conditioner is prepared, and the pH of acidic soil can be greatly increased with a low application amount. The doped graphite phase carbon nitride-molybdenum disulfide compound is prepared by the following method: firstly, preparing doped graphite phase carbon nitride from urea, ferric chloride hexahydrate and succinic acid, then adding the doped graphite phase carbon nitride into a sodium molybdate-thioacetamide mixed aqueous solution, and carrying out hydrothermal reaction to obtain the doped graphite phase carbon nitride-molybdenum disulfide compound. The soil conditioner prepared by the invention can be used for improving the pH value of acid soil at a relatively low application amount.

Description

technical field [0001] The invention relates to the technical field of soil improvers, in particular to an attapulgite acidic soil conditioner and a preparation method thereof. Background technique [0002] Soil is an important medium for plant growth. With the continuous growth of population and the rapid development of urban and rural construction, the demand for crops continues to increase, so the requirements for soil quality also become higher. There is a large amount of red soil in my country, which is generally acidic, with a pH between 4.5 and 6.0. With the rapid development of industry, the content of acid gas in the air increases rapidly. When it settles into the soil in the form of acid rain, it also causes the pH value of the soil to drop, resulting in acidification of the soil. Moreover, with the extensive application of chemical fertilizers in recent years, soil acidification has become more and more serious. [0003] The root cause of soil acidification is t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K17/40C09K109/00
CPCC09K17/40C09K2109/00
Inventor 张哲邹童魏玉祥
Owner 白银丰宝农化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap