Solid lubricant and preparation method thereof

A technology for solid lubricants and preparation steps, applied in lubricating compositions, petroleum industry, etc., can solve the problems of reducing the strength, toughness and wear resistance of composite materials, continuous damage of matrix, and loss of lubricity, etc., to improve strength, toughness, Protects against oxidation damage and improves lubricating performance

Inactive Publication Date: 2021-07-30
许伟纯
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, solid lubricants will partially lose their lubricity during high-temperature sintering, and their uneven distribution and damage to matrix continuity will significantly reduce the strength, toughness and wear resistance of composites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid lubricant and preparation method thereof
  • Solid lubricant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Weigh expandable graphite and put it into a vacuum freeze-drying box to freeze-dry, then put the dried expandable graphite into a microwave reactor, treat it with a power of 1.3kW for 30s, then cool it naturally to room temperature, and heat and expand it by circulating microwave treatment for 5 times, to obtain expanded graphite;

[0037] In parts by weight, 70 parts of nickel nitrate, 60 parts of molybdenum chloride, 40 parts of aluminum chloride, 8 parts of cobalt nitrate and 8 parts of yttrium chloride were weighed to obtain a mixed salt, and the mixed salt was heated to 200 ° C. Put the mixed salt into the electrolytic cell after melting, use the aluminum sheet as the positive electrode, and use the above-mentioned expanded graphite as the negative electrode, keep the distance between the two stages at 40mm, and the current density is 1.06A / dm 2 After electroplating for 4 hours under certain conditions, remove the electroplated negative electrode, which is composit...

Embodiment 2

[0043] Weigh the expandable graphite and put it into a vacuum freeze-drying box to freeze-dry, then put the dried expandable graphite into a microwave reactor, treat it with a power of 1.3 kW for 31 seconds, then cool it down to room temperature naturally, and heat and expand it by circulating microwave treatment for 5 times, to obtain expanded graphite;

[0044] In parts by weight, 72 parts of nickel nitrate, 62 parts of molybdenum chloride, 42 parts of aluminum chloride, 8 parts of cobalt nitrate and 8 parts of yttrium chloride were weighed to obtain a mixed salt, and the mixed salt was heated to 205 ° C. Put the mixed salt into the electrolytic cell after melting, use the aluminum sheet as the positive electrode, and use the above-mentioned expanded graphite as the negative electrode, keep the distance between the two stages at 40mm, and the current density is 1.06A / dm 2 After electroplating for 4 hours under certain conditions, remove the electroplated negative electrode, ...

Embodiment 3

[0050] Weigh the expandable graphite and put it into a vacuum freeze-drying box to freeze-dry, then put the dried expandable graphite into a microwave reactor, treat it with a power of 1.4kW for 33s, then cool it naturally to room temperature, and heat and expand it by cyclic microwave treatment for 6 times, to obtain expanded graphite;

[0051] In parts by weight, 75 parts of nickel nitrate, 65 parts of molybdenum chloride, 45 parts of aluminum chloride, 9 parts of cobalt nitrate and 9 parts of yttrium chloride were weighed to obtain a mixed salt, and the mixed salt was heated to 210° C. Put the mixed salt into the electrolytic cell after melting, use the aluminum sheet as the positive electrode, and use the above-mentioned expanded graphite as the negative electrode, keep the distance between the two stages at 40mm, and the current density is 1.06A / dm 2 After electroplating for 4 hours under certain conditions, remove the electroplated negative electrode, which is composite ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a solid lubricant and a preparation method thereof, and belongs to the technical field of lubricant preparation. The preparation method comprises the steps of preparing a solid lubricant matrix, loading a soft metal lubricant into the solid lubricant matrix through a vacuum hot pressing method to prepare a solid lubricant crude product, and finally carrying out orthosilicic acid precipitation and hydrolysis modification on the surface of the solid lubricant crude product to finally prepare a solid lubricant finished product. The solid lubricant finished product prepared by the invention is excellent in mechanical strength, good in lubricating effect and wide in application prospect.

Description

technical field [0001] The invention relates to a solid lubricant and a preparation method thereof, belonging to the technical field of lubricant preparation. Background technique [0002] At present, solid lubrication is to replace lubricating grease with solid micropowder, thin film or composite material, and isolate the friction surface of relative motion to achieve the purpose of reducing friction and wear resistance. With the advancement of modern science and technology, in order to solve the mechanical lubrication problems under special working conditions such as high load, high vacuum, high and low temperature, strong radiation and strong corrosion, solid lubricating materials have been developed from a single micropowder, adhesive film or unit material. As a composite material composed of multiple components, the research on its mechanism of action and application methods has been developed rapidly, and many new techniques and technologies for the preparation and app...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/04C10N50/08
CPCC10M169/04C10M2201/0413C10M2201/081C10M2201/082C10M2201/102C10M2201/105
Inventor 许伟纯
Owner 许伟纯
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap