A kind of ceramic roller for tempered glass furnace and its manufacturing process

A tempered glass and manufacturing process technology, applied in glass manufacturing equipment, manufacturing tools, glass tempering, etc., can solve problems such as poor strength of ceramic roller rods, achieve simple and easy production methods, improve hardness and strength, and improve compactness sexual effect

Active Publication Date: 2022-08-05
福建安溪马斯特陶瓷有限公司
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this patent only uses the same type of alumina micropowder with different particle sizes for preparation, and the strength of the manufactured ceramic roller is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ceramic roller for tempered glass furnace and its manufacturing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of ceramic roller for tempered glass furnace and its manufacturing process

[0029] The manufacturing process of ceramic roller for tempered glass furnace includes the following steps:

[0030] Step S10, prepare materials: 30kg of mullite, 32kg of alumina, 12kg of refractory clay, 14kg of kaolin, 6.5kg of zirconium silicate, 1.4kg of talc, 1.5kg of vanadium pentoxide, 2.0kg of boron nitride and 1.1kg of magnesium oxide; Mullite is light-fired mullite with particle size ≤ 10μm and fused mullite with particle size ≤ 1mm, and the weight ratio of light-burned mullite and fused mullite is 20:80; the above alumina is particle size ≤ 1mm 10μm fused alumina and ordinary alumina with a particle size of ≤1mm, the weight ratio of fused alumina and ordinary alumina is 40:60;

[0031] Step S20, the above-mentioned weight parts of alumina, refractory clay, kaolin, zirconium silicate, talc, vanadium pentoxide, boron nitride and magnesium oxide are put into a ball mill for ball...

Embodiment 2

[0036] A kind of ceramic roller for tempered glass furnace and its manufacturing process

[0037] The manufacturing process of ceramic roller for tempered glass furnace includes the following steps:

[0038] Step S10, prepare materials: 20kg of mullite, 20kg of alumina, 6kg of refractory clay, 8kg of kaolin, 3kg of zirconium silicate, 0.8kg of talc, 0.4kg of vanadium pentoxide, 1.2kg of boron nitride and 0.4kg of magnesium oxide; The mullite is light-fired mullite with particle size ≤10μm and fused mullite with particle size ≤1mm, and the weight ratio of light-burned mullite and fused mullite is 10:90; the above alumina is particle size ≤10μm The weight ratio of fused alumina and ordinary alumina is 30:70;

[0039] Step S20, the above-mentioned weight parts of alumina, refractory clay, kaolin, zirconium silicate, talc, vanadium pentoxide, boron nitride and magnesium oxide are put into a ball mill for ball milling for 6 hours, and the above-mentioned weight parts of mullite ar...

Embodiment 3

[0044] A kind of ceramic roller for tempered glass furnace and its manufacturing process

[0045] The manufacturing process of ceramic rollers for tempered glass furnace includes the following steps:

[0046] Step S10, prepare materials: 40kg of mullite, 45kg of alumina, 18kg of refractory clay, 20kg of kaolin, 10kg of zirconium silicate, 2.0kg of talc, 2.5kg of vanadium pentoxide, 2.8kg of boron nitride and 1.8kg of magnesium oxide; The mullite is light-fired mullite with particle size ≤ 10μm and fused mullite with particle size ≤ 1mm, and the weight ratio of light-burned mullite and fused mullite is 30:70; the above alumina is particle size ≤ 10μm The weight ratio of fused alumina and ordinary alumina is 50:50;

[0047] Step S20, put the alumina, refractory clay, kaolin, zirconium silicate, talc, vanadium pentoxide, boron nitride and magnesium oxide of the above-mentioned parts by weight into a ball mill for ball milling for 10 hours, add the mullite of the above-mentioned ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic roller for a tempered glass furnace and a manufacturing process thereof, comprising the following steps: preparing materials: mullite, alumina, refractory clay, kaolin, zirconium silicate, talc, vanadium pentoxide, boron nitride and magnesium oxide; mixing the ball mill to obtain a mixture; spray-drying the mixture, adding water to the spray powder, stirring, and extruding after muddling to obtain a green body; It is sintered in a high-temperature shuttle kiln to obtain a blank; cylindrically ground to a specified size to obtain a ceramic roller for tempered glass kiln. The ceramic roller for tempered glass furnace prepared by the invention has high density, high strength and hardness, high heat resistance, creep resistance and thermal peeling resistance, long service life, simple production method and easy operation, and high economic benefit. , suitable for industrial production.

Description

technical field [0001] The invention relates to the technical field of ceramic material processing, in particular to a ceramic roller for a tempered glass furnace and a manufacturing process thereof. Background technique [0002] Roller kilns are widely used in building sanitary ceramics, glass and other industries due to their characteristics of small firing temperature difference, short firing cycle, high yield, low energy consumption and easy control. In the glass tempered roller kiln, the roller is the most critical refractory material, which plays the role of carrying and conveying products in the kiln. The strength and high-temperature mechanical properties of the roller determine the operating temperature and loading of the roller kiln. quantity. Ceramic rollers have increasingly become the first choice for roller kiln transmission and bearing due to their high softening temperature and high temperature strength. The biggest feature of the ceramic roller is high tem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66C04B35/185C04B35/106C04B35/622C03B27/00C03B27/012
CPCC04B35/66C04B35/185C04B35/106C04B35/622C03B27/00C03B27/012C04B2235/349C04B2235/3248C04B2235/3239C04B2235/3206C04B2235/386C04B2235/96
Inventor 吴维宾刘德峰董峰
Owner 福建安溪马斯特陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com